Effect of light intensity on polymerization of light-cured composite resins.

abstract：:The biaxial flexural strength and cyclic fatigue biaxial flexural strength of CAD/CAM ceramics polished with #220, 400, 600 and 1000 diamond pads were measured in an effort to determine the effect of surface roughness on fatigue behavior of dental ceramics. The surface roughness was improved after polishing with a sma...

journal_title：Dental materials journal

authors： Nakazato T,Takahashi H,Yamamoto M,Nishimura F,Kurosaki N

更新日期：1999-12-01 00:00:00

abstract：:This study investigated the contrast ratio and grain size depending on sintering parameters of twelve different zirconia materials and compared with glass-ceramic (N=156, n=12 per group). Contrast ratio of all ceramics was measured using a spectrophotometer according to ISO 2471: 2008. Grain sizes of zirconia were det...

journal_title：Dental materials journal

authors： Stawarczyk B,Emslander A,Roos M,Sener B,Noack F,Keul C

更新日期：2014-01-01 00:00:00

abstract：:Despite progress in the development of denture base resin and artificial tooth materials, dental clinics are still plagued with artificial teeth falling off the denture base--due to poor bond strength--after denture delivery. Against this background, this study sought to examine the effect and durability of an adhesiv...

journal_title：Dental materials journal

authors： Nishigawa G,Maruo Y,Okamoto M,Oki K,Kinuta Y,Minagi S,Irie M,Suzuki K

更新日期：2006-03-01 00:00:00

abstract：:The aim of this study was to evaluate the effect of resin infiltration on root caries induced by Streptococcus mutans biofilms. Human premolar specimens were divided to 5 groups: negative control (NC), Clearfil SE Bond (SEB), Icon-etch120s+Icon-infiltrant (HA120), Icon-etch10s+Icon-infiltrant (HA10) and K-etchant10s+I...

journal_title：Dental materials journal

authors： Zhou Y,Matin K,Shimada Y,Sumi Y,Tagami J

更新日期：2017-03-31 00:00:00

abstract：:The effects of monomer structure on the mechanical properties of visible light-cured composite resins based on the seven types of aromatic dimethacrylates were investigated. The results of this study suggested that the mechanical properties of the composite resins were dependent upon the chemical structure of the dime...

journal_title：Dental materials journal

authors： Kawaguchi M,Fukushima T,Horibe T

更新日期：1989-06-01 00:00:00

abstract：:This study aimed to introduce a procedure for determining the bilinear elastic moduli (E1 and E2) of the periodontal ligament for a mathematical tooth model to analyse stress in the mandible. The bone and tooth morphology were scanned from a dry skull and an extracted intact tooth, respectively, and reconstructed in a...

journal_title：Dental materials journal

authors： Borák L,Florian Z,Bartáková S,Prachár P,Murakami N,Ona M,Igarashi Y,Wakabayashi N

更新日期：2011-01-01 00:00:00

abstract：:The physical properties of experimental visible light-activated resins containing dyestuff, which could be quickly discolored by irradiation was, evaluated by analyzing light absorbance characteristics and measuring micro Vickers hardness. The experimental resin, which was prepared by mixing equivalent weights of Bis ...

journal_title：Dental materials journal

authors： Nakazato J,Itoh K,Wakumoto S

更新日期：1989-12-01 00:00:00

abstract：:This study was designed to evaluate the cytotoxicity of four dentin bonding agents and the effects of an antioxidant addition. Group A: G-aenial Bond, Group B: Optibond All in One, Group C: Gluma Self Etch and Group D: Clearfil S(3) Bond were added to the medium using extract method. The cells were cultured with or wi...

journal_title：Dental materials journal

authors： Atalayin C,Armagan G,Konyalioglu S,Kemaloglu H,Tezel H,Ergucu Z,Keser A,Dagci T,Onal B

更新日期：2015-01-01 00:00:00

abstract：:Ag-Pd-Cu-Au alloy was subjected to a Thermo-Mechanical Analyzer to investigate high temperature properties up to its liquidus temperature. Microstructural examination and elemental analysis with EPMA were also conducted in the solid/liquid mixture region. The following conclusions were obtained. (1) The solidus temper...

journal_title：Dental materials journal

authors： Nagasawa S,Yoshida T,Mizoguchi T,Terashima N,Ito M,Platt JA,Oshida Y

更新日期：2003-09-01 00:00:00

abstract：:A zirconia-binding peptide motif was identified using a peptide phage display system. Yttria stabilized zirconia beads and discs were used as the target. Quartz crystal microbalance was used to monitor the binding of phages to zirconia. Starting from a library of phages displaying random sequences of 12-mer peptides, ...

journal_title：Dental materials journal

authors： Hashimoto K,Yoshinari M,Matsuzaka K,Shiba K,Inoue T

更新日期：2011-01-01 00:00:00

abstract：:To determine the effect of titanium (Ti) surface modification by ultraviolet irradiation (UVI) on the bond strength between Ti and porcelain. Grade 2 Ti plates were allotted to five groups: sandblasted (SA), 15 min UVI (UV), SA+5 min UVI (SA+UV5), SA+10 min UVI (SA+UV10), and SA+15 min UVI (SA+UV15). After surface tre...

journal_title：Dental materials journal

authors： Kumasaka T,Ohno A,Hori N,Hoshi N,Maruo K,Kuwabara A,Seimiya K,Toyoda M,Kimoto K

更新日期：2018-06-08 00:00:00

abstract：:This study assessed the impact of surface treatments and repair resin reinforcement with zirconium oxide nano-particles (nano-ZrO2) on flexural strength (FS) of repaired denture base. A total of 320 heat-polymerized acrylic resin specimens were prepared and sectioned creating 2-mm gap. According to repair surface trea...

journal_title：Dental materials journal

authors： Gad MM,Rahoma A,Abualsaud R,Al-Thobity AM,Akhtar S,Helal MA,Al-Harbi FA

更新日期：2020-06-05 00:00:00

abstract：:Although titanium has been widely used in prosthetic appliances, such as cast removable partial denture frameworks, high quality castings are still difficult to obtain. This study proposes a new partition technique using a metal foil for improving castability of a two-chamber pressure casting unit. The metal foil was ...

journal_title：Dental materials journal

authors： Watanabe K,Okawa S,Kanatani M,Nakano S,Miyakawa O,Kobayashi M

更新日期：2000-09-01 00:00:00

abstract：:This study evaluated the polymerization shrinkage, flexural and compressive properties of low-shrinkage resin composites. For the study, four methacrylate-based and one silorane-based resin composites were light cured using three different light-curing units (LCUs) and their polymerization shrinkage, flexural (strengt...

journal_title：Dental materials journal

authors： Park JK,Lee GH,Kim JH,Park MG,Ko CC,Kim HI,Kwon YH

更新日期：2014-01-01 00:00:00

abstract：:This study examined the ability of a photocatalyst mixed in a denture base resin to decompose organic substances which adhered to the denture base resin surface. The photocatalyst was mixed with denture base resin at concentrations of 0, 5, 10, and 15% (w/w). Decomposition test, bending test, and surface roughness mea...

journal_title：Dental materials journal

authors： Cheng Y,Sakai T,Moroi R,Nakagawa M,Sakai H,Ogata T,Terada Y

更新日期：2008-03-01 00:00:00

abstract：:The purpose of this study was to evaluate the effects of acid-etched titanium on the biological responses of osteoblast-like MC3T3-E1 cells. Four types of treatments (polishing, sandblasting, concentrated H2SO4 etching, and concentrated H2SO4 etching with vacuum firing) were carried out on the surfaces of commercially...

journal_title：Dental materials journal

authors： Iwaya Y,Machigashira M,Kanbara K,Miyamoto M,Noguchi K,Izumi Y,Ban S

更新日期：2008-05-01 00:00:00

abstract：:This study assessed the effect of the resin-coating technique on the bond strength and internal adaptation of computer-aided design/computer-aided manufacturing (CAD/CAM)-fabricated inlays. Seventy-two mesio-occlusal-distal (MOD) cavities were prepared and distributed into 3 groups according to the resin-coating techn...

journal_title：Dental materials journal

authors： Rozan S,Takahashi R,Nikaido T,Tichy A,Tagami J

更新日期：2020-12-03 00:00:00

abstract：:The depths of calcium-ion incorporation into a commercially pure titanium and an experimental beta-type titanium alloy were determined using Auger electron spectroscopy. After the electrochemical deposition of apatite, new compositional gradients appeared in the profiles in which the Ca and P concentrations gradually ...

journal_title：Dental materials journal

authors： Ban S,Kamiya A,Sonoda T

更新日期：2002-12-01 00:00:00

abstract：:This study determined the discoloration of five CAD/CAM resins, four manually polymerized resins, and glass-ceramic as control group. Specimens were divided into three groups (N=300, n=30) to be stored in coffee, black tea and red wine (n=10). The discoloration was measured using a spectrophotometer after 1, 7, 29, 90...

journal_title：Dental materials journal

authors： Stawarczyk B,Sener B,Trottmann A,Roos M,Ozcan M,Hämmerle CH

更新日期：2012-01-01 00:00:00

abstract：:The possibility of the segregation under solidification process using a centrifugal casting machine was investigated using an electron probe microanalyzer with elemental distribution map, line analysis and quantitative analysis. When a very small quantity of platinum was added to local molten titanium during the casti...

journal_title：Dental materials journal

authors： Watanabe K,Okawa S,Kanatani M,Nakano S,Miyakawa O,Kobayashi M

更新日期：1996-12-01 00:00:00

abstract：:The aim of our study was twofold: to immobilize an organosilicon quaternary ammonium salt (3-(trimethoxysilyl)-propyldimethyl-octadecyl ammonium chloride, Si-QAC) on the surface of pure titanium and to investigate the antimicrobial activity of Si-QAC-immobilized titanium against microbial adherence and biofilm formati...

journal_title：Dental materials journal

authors： Nikawa H,Ishida K,Hamada T,Satoda T,Murayama T,Takemoto T,Tamamoto M,Tajima H,Shimoe S,Fujimoto H,Makihira S

更新日期：2005-12-01 00:00:00

abstract：:Temperature dependencies of thermal expansion coefficients for the alloys of Pd-Ag, Pd-Cu and Pd-Co binary systems were measured at temperatures up to 900 degrees C, with heating and cooling rates of 5 degrees C/min. The coefficient of thermal expansion of alloys with no transformation in the temperature range of inte...

journal_title：Dental materials journal

authors： Asaoka K,Kuwayama N

更新日期：1990-06-01 00:00:00

abstract：:This study aimed to evaluate the inhibitory effect of experimental pastes containing surface pre-reacted glass ionomer (S-PRG) fillers on enamel demineralization. Bovine blocks were treated twice a day for 4 days by 7 groups; experimental pastes containing 0-30 wt% S-PRG filler (S00, S01, S05, S10, and S30), deionized...

journal_title：Dental materials journal

authors： Nakamura K,Hamba H,Nakashima S,Sadr A,Nikaido T,Oikawa M,Uo M,Tagami J

更新日期：2017-07-26 00:00:00

abstract：:The purpose of this study was to establish a method using FTIR to evaluate the polymerization characteristics of UDMA-based resins. Three kinds of experimental UDMA-based resins were prepared with various molar fractions. IR spectra of the cured film specimens were measured with FTIR before and after extracting residu...

journal_title：Dental materials journal

authors： Nomoto R,Hirasawa T

更新日期：1999-06-01 00:00:00

abstract：:Improved osseointegration of dental implants is imperative in clinic. Effect of doxycycline on promoting bone formation after implant placement was expected due to its inhibitory properties on inflammation and osteoclastogenesis. To evaluate new bone formation on the hydroxyapatite (HA)-coated implant surface, which w...

journal_title：Dental materials journal

authors： Ding L,Zhang P,Wang X,Hao J,Aoki K,Kuroda S,Kasugai S

更新日期：2018-01-30 00:00:00

abstract：:The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...

journal_title：Dental materials journal

authors： Zavala-Alonso V,Aguilera-Flores R,Patiño-Marin N,Martinez-Castañon GA,Anusavice KJ,Loyola-Rodriguez JP

更新日期：2011-01-01 00:00:00

abstract：:The blending effect (BE) plays an important role in esthetics of the composite resin. The objective of this study was to determine the extents to which filler size and content affect the BE. Three types of fillers (0.7, 1.0, and 1.5 µm) were mixed at weight contents of 60, 70, 75, and 80%. This study simulated clinica...

journal_title：Dental materials journal

authors： Suh YR,Ahn JS,Ju SW,Kim KM

更新日期：2017-01-31 00:00:00

abstract：:The human antimicrobial peptide beta-defensin-2 (hBD2) shows broad antibacterial activity and infrequent bacterial resistance. Here mesoporous bioactive glass (MBG) was loaded with hBD2, forming hBD2-loaded MBG (BD-MBG). The antibacterial and osteogenic effects of BD-MBG were investigated in comparison with MBG and th...

journal_title：Dental materials journal

authors： Ren L,Zhang Z,Deng C,Zhang N,Li D

更新日期：2020-12-24 00:00:00

abstract：:In tissue engineering, biodegradable polymer materials with both high biocompatibility and high strength are very important as scaffolds for long term use. Therefore, in this research, we tried to prepare the three types of poly(L-lactic acid) (PLLA)/calcium phosphate (CP) hybrid composite for a scaffold biomaterial. ...

journal_title：Dental materials journal

authors： Hamada Y,Fujitani W,Kawaguchi N,Daito K,Niido T,Uchinaka A,Mori S,Kojima Y,Manabe M,Nishida K,Arita K,Nakano T,Matsuura N

更新日期：2012-01-01 00:00:00

abstract：:A new type of self-etching agent, the single-step adhesive, was developed. The purpose of this study was to investigate the difference in the ultrastructural features of enamel and dentin surfaces following application of the prototype single-step adhesive (EXM618, 3M, MN, USA). Extracted caries-free human premolars w...

journal_title：Dental materials journal

authors： Han L,Cruz E,Fukushima M,Okamoto A,Okiji T