Abstract:
:The possibility of the segregation under solidification process using a centrifugal casting machine was investigated using an electron probe microanalyzer with elemental distribution map, line analysis and quantitative analysis. When a very small quantity of platinum was added to local molten titanium during the casting process, macroscopic segregation was observed under conditions of density difference of 0.1 g/cm3 at the most, confirming that the centrifugal force of the casting machine is extremely strong. When a Ti-6Al-4V alloy was cast, however, no macroscopic segregation was observed. The centrifugal force of the casting machine examined in the present study hardly results in the body-force segregation in this titanium alloy.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Watanabe K,Okawa S,Kanatani M,Nakano S,Miyakawa O,Kobayashi Mdoi
10.4012/dmj.15.212subject
Has Abstractpub_date
1996-12-01 00:00:00pages
212-9issue
2eissn
0287-4547issn
1881-1361journal_volume
15pub_type
杂志文章abstract::The aim of this study was to determine the effect of autoclave polymerization on the transverse strength of denture base polymers. To this end, 30 rectangular test specimens were fabricated of two heat-polymerized denture base polymers. The test groups were: (I) control, i.e., conventional water bath to polymerize res...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:
更新日期:2008-07-01 00:00:00
abstract::The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a newly developed resin cement, ECD-89 (ECD, Tokuyama Dental, Tokyo, Japan) to dentin and to observe the interfacial micromorphology by comparing with two commercial resin cements, Multilink Automix (MA, Ivoclar Vivadent AG, Schaan, Lie...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-122
更新日期:2015-01-01 00:00:00
abstract::Gold alloys with Cu contents of 10 mass%, 20%, and 30% were used for morphological observation of porous surface structures after heating at 800 degrees C in air followed by pickling with acid solution. With increasing Cu content in the gold alloy, the internal oxidation zone became well-developed in the alloy matrix....
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.503
更新日期:2005-12-01 00:00:00
abstract::This study tested whether exhaled humid conditions would affect the adhesion of etch-and-rinse, two-step and one-step self-etch adhesive resins to enamel. Enamel surfaces of human maxillary anterior teeth (N=240, n=20) were exposed to four humid conditions (H1: 63-68%, H2: 73-78%, H3: 93-98%, H4: 36-45% RH) during bon...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-200
更新日期:2013-01-01 00:00:00
abstract::The purpose of the present study was to evaluate the effect of four silane coupling agents on the bond strength between two resin-modified glass ionomer cements and a machinable leucite glass ceramic. Ceramic specimens were ground with silicon carbide paper and cleaned with phosphoric acid. They were then conditioned ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.240
更新日期:2007-03-01 00:00:00
abstract::Despite progress in the development of denture base resin and artificial tooth materials, dental clinics are still plagued with artificial teeth falling off the denture base--due to poor bond strength--after denture delivery. Against this background, this study sought to examine the effect and durability of an adhesiv...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.75
更新日期:2006-03-01 00:00:00
abstract::The aim was to evaluate the effect of different zirconia discontinuous fiber fractions on radiopacity and other selected properties of glass discontinuous fiber-reinforced flowable composite (Exp-SFRC). Exp-SFRC was prepared by mixing 30 wt% of resin-matrix and 45 wt% of particulate-fillers to 25 wt% of various weight...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-102
更新日期:2019-03-31 00:00:00
abstract::The purpose of this study was to evaluate the influence of heating, cast bonding, and subsequent polishing procedures on attractive force of magnetic attachments. Two magnetic attachment systems with keepers of different chemical compositions (Hicorexslim 3013, 447J1; Magfit EX400, AUM20) were employed. Keepers examin...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.393
更新日期:2007-05-01 00:00:00
abstract::The objective of the study was to compare 1) the mean micro-shear bond strength and 2) failure mode of cements to metals in nonenclosed and mold-enclosed specimens. Specimens were prepared in mold-enclosed and non-enclosed formats from two RMGIC's and a self-adhesive resin-cement. 3-way ANOVA analysis and Tukey post h...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-065
更新日期:2013-01-01 00:00:00
abstract::This study aimed to determine the influence of sodium hypochlorite (NaOCl) contamination on the microhardness of build-up composites. Fifty-two samples, from each of three build-up materials (LuxaCore Dual, MultiCore flow and Rebilda DC) were prepared. Half of the samples from each material were stored in physiologic ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-007
更新日期:2010-08-01 00:00:00
abstract::This study examined the ability of a photocatalyst mixed in a denture base resin to decompose organic substances which adhered to the denture base resin surface. The photocatalyst was mixed with denture base resin at concentrations of 0, 5, 10, and 15% (w/w). Decomposition test, bending test, and surface roughness mea...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.179
更新日期:2008-03-01 00:00:00
abstract::Removable partial dentures (RPDs) with resin-clasp retentive parts, which are known as non-metal-clasp dentures (NMCDs), have been used as alternatives for conventional RPDs with metal clasp, in case of aesthetic prosthodontic treatments. In this study, a profilometer and dynamic micro-indentation tests were used to i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-012
更新日期:2018-11-30 00:00:00
abstract::To elucidate the cause of brittleness of porcelain fused to pure titanium (PFPT) which leads to chipping and cracking similar to that of conventional porcelain in clinical use, fracture toughness KIc, hardness (Hv and Hk) and fracture energy gamma reflecting the bonding energy of atoms were evaluated. In KIc there wer...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.532
更新日期:2003-12-01 00:00:00
abstract::Comparative studies on two-body sliding wear resistance were performed between a hybrid composite resin and conventional light-curing composite veneering materials. This study investigated the wear resistance of hybrid composite resins compared with three composite resin veneering materials for 12%Au-Ag-Pd alloy, the ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.21.225
更新日期:2002-09-01 00:00:00
abstract::The aim of the present study was to examine whether interconnected porous hydroxyapatite ceramics (IP-CHA) could be used as bone substitute for implant treatment in reconstructive surgery. We firstly assessed if surround of the titanium surface placed into granular or block-type IP-CHA can observe new bone formation i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-169
更新日期:2013-01-01 00:00:00
abstract::The aim of this study was to evaluate temperature changes in the pulp chamber during polymerization of four different pulp-capping materials using a LED-light-curing-unit in the contact and noncontact positions. A pulpal circulation mechanism was simulated to measure increases in temperature in four pulp-capping mater...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-274
更新日期:2014-01-01 00:00:00
abstract::The aim of this study was to investigate the relationship between the different mechanical properties with the filler fraction of various resin composites. Mechanical properties of eighteen different resin composites were investigated in this study; flexural strength (FS), flexural modulus (FM), fracture toughness (FT...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-178
更新日期:2013-01-01 00:00:00
abstract::This study evaluated the influence of an aqueous propolis-based solution (PROP) on gap formation and bond strength of posts bonded to root canal dentin using resin cements. Endodontically-treated bovine incisors received different irrigation protocols: 1) 2.5% sodium hypochlorite (NaOCl)/17% EDTA/NaOCl; 2) saline solu...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-111
更新日期:2020-06-05 00:00:00
abstract::The purpose of this review is to summarise recent advances in the design and composition of bioactive surface layers of implantabile biomaterials, and thus the genetic potential of osteoprogenitor cells to recognize and respond to these diverse implanted biomaterials. Changes applied to a biomaterial's surface, in gen...
journal_title:Dental materials journal
pub_type: 杂志文章,评审
doi:10.4012/dmj.19.99
更新日期:2000-06-01 00:00:00
abstract::An experimental primer was developed as a single-step bonding system for resin-modified glass ionomer cements (GIC). Efficacy of this primer on adhesion of resin-modified GICs and resin composite to enamel and dentin was evaluated by shear bond test and SEM observation. Good bond strengths to enamel were obtained (> 1...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.16.40
更新日期:1997-06-01 00:00:00
abstract::The aim of this study was to evaluate the effect of resin infiltration on root caries induced by Streptococcus mutans biofilms. Human premolar specimens were divided to 5 groups: negative control (NC), Clearfil SE Bond (SEB), Icon-etch120s+Icon-infiltrant (HA120), Icon-etch10s+Icon-infiltrant (HA10) and K-etchant10s+I...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-229
更新日期:2017-03-31 00:00:00
abstract::The purpose of this study was to characterize the surface damages of zirconia by Nd:YAG dental laser irradiation through a systematic evaluation of the associated microstructural changes. Disk specimens of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) and ceria-stabilized zirconia/alumina nanocomposite (C...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-127
更新日期:2010-10-01 00:00:00
abstract::The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-023
更新日期:2011-01-01 00:00:00
abstract::To improve the bioactivity of titanium surfaces, glow discharge was used to facilitate collagen grafting on titanium disks. Titanium test specimens were pre-treated by glow discharge fed with a mixture of argon and allylamine (AA) gases. Treated titanium disks were then grafted with type I collagen using glutaraldehyd...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.340
更新日期:2008-05-01 00:00:00
abstract::This study evaluated the polymerization shrinkage, flexural and compressive properties of low-shrinkage resin composites. For the study, four methacrylate-based and one silorane-based resin composites were light cured using three different light-curing units (LCUs) and their polymerization shrinkage, flexural (strengt...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-126
更新日期:2014-01-01 00:00:00
abstract::The aim of this investigation was to evaluate the metal-ceramic bonding of Au-1.6 wt% Ti alloy. Therefore, the coefficient of thermal expansion, modulus of elasticity, ceramic bonding strength, and hardness of Au-1.6 wt% Ti alloy were measured. The metal-ceramic interface was observed by EPMA to investigate its bondin...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.268
更新日期:2005-06-01 00:00:00
abstract::This study compared bovine serum albumin (BSA) adsorption onto octacalcium phosphate (OCP) materials prepared from two wet preparations in the absence (w-OCP) and presence (c-OCP) of gelatin. Raman spectroscopy was used to analyze the BSA adsorption onto OCPs in a 150 mM Tris-HCl buffer containing 0.5 mM calcium and i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-250
更新日期:2020-09-29 00:00:00
abstract::To investigate the bonding of tooth-colored indirect restorations to cervical dentin, shear bond strengths of bonded resin inlays to cervical dentin and mid-coronal dentin were investigated and compared. Indirectly fabricated composite inlays (Estenia) were cemented with a dual-cured resin cement (Panavia Fluoro Cemen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.7
更新日期:2006-03-01 00:00:00
abstract::The bonding efficacy of sclerotic dentin was determined by measuring the polymerization contraction gap width of a commercial light-activated resin composite in a cervical defect and by measuring the micro-Vicker's hardness at the dentin adhesive surface; morphological characteristics were observed using a scanning el...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.20.359
更新日期:2001-12-01 00:00:00
abstract::This study evaluated the influence of filling technique and curing mode on the microtensile bond strengths (MTBS) of composite cores to pulpal floor dentin. Access cavities of human molars with pulpal floor dentin were restored with a two-step self-etch adhesive system, Clearfil Liner Bond 2V and a composite core, Cle...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-104
更新日期:2010-10-01 00:00:00