Abstract:
:This study examined the ability of a photocatalyst mixed in a denture base resin to decompose organic substances which adhered to the denture base resin surface. The photocatalyst was mixed with denture base resin at concentrations of 0, 5, 10, and 15% (w/w). Decomposition test, bending test, and surface roughness measurement were performed at 1, 7, 30, 90, and 180 days after polymerization. Decomposition ability was evaluated based on the residual amount of methylene blue (MB) dissolved in ethanol after UV irradiation for 12 hours. As the mixing ratio increased, the amount of MB in the solution decreased. Meanwhile, no changes in the amount of MB in the immersion solution were observed in the photocatalyst-free resin specimen. Therefore, the results indicated that a denture base resin containing a photocatalyst might have a photocatalytic ability.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Cheng Y,Sakai T,Moroi R,Nakagawa M,Sakai H,Ogata T,Terada Ydoi
10.4012/dmj.27.179subject
Has Abstractpub_date
2008-03-01 00:00:00pages
179-86issue
2eissn
0287-4547issn
1881-1361journal_volume
27pub_type
杂志文章abstract::This study evaluated the effect of resin coating (COA) on dentin bond strength (BS) of five resin cements (RC). Ten groups were tested, according to RC and COA combinations. RCs were applied onto prepolymerized resin discs, which were bonded to dentin surfaces. Teeth were stored in water for 24 h, subjected to 5,000 t...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-099
更新日期:2015-01-01 00:00:00
abstract::Adhesion promoting monomers for precious metals, 2,3-epithiopropyl methacrylate (EP1MA), 4,5-epithiopentyl methacrylate (EP3MA), 9,10-epithiodecyl methacrylate (EP8MA), 10,11-epithioundecyl methacrylate (EP9MA), 9,10-epithiodecyl 4-vinylbenzoate (EP8VB), 2,3-epithiocyclohexyl methacrylate (EPCHMA), and 3,4-epithiobuty...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.29
更新日期:2007-01-01 00:00:00
abstract::The purpose of this study was to evaluate the influence of heating, cast bonding, and subsequent polishing procedures on attractive force of magnetic attachments. Two magnetic attachment systems with keepers of different chemical compositions (Hicorexslim 3013, 447J1; Magfit EX400, AUM20) were employed. Keepers examin...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.393
更新日期:2007-05-01 00:00:00
abstract::The aim of the study was to evaluate bone regeneration using a canine model with surgically created periodontal defects filled for 12 weeks using a stratified biomaterial consisting in a biphasic calcium phosphate (BCP) covered with a crosslinking hydrogel acting as polymer membrane of silated hydroxypropyl methylcell...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-238
更新日期:2018-09-30 00:00:00
abstract::The efficacy of four commercial and two experimental dentin bonding systems was examined by observing the cavity adaptation of commercial light-cured resin composites restored in the dogs scheduled to be sacrificed after a medical experiment. Before being sacrificed, a cylindrical class V cavity was prepared in each c...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.17.195
更新日期:1998-09-01 00:00:00
abstract::The effects of desensitizer, disinfectant, saliva, blood, and hydrogen peroxide on the tensile bond strength between adhesive and ceramic as well as between adhesive and dentin were examined. Sixty 7x3 mm pressed ceramic discs of IPS e.max were fabricated and randomly assigned to six groups of different dentin surface...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-074
更新日期:2010-08-01 00:00:00
abstract::The aim of this study was to evaluate temperature changes in the pulp chamber during polymerization of four different pulp-capping materials using a LED-light-curing-unit in the contact and noncontact positions. A pulpal circulation mechanism was simulated to measure increases in temperature in four pulp-capping mater...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-274
更新日期:2014-01-01 00:00:00
abstract::The purposes of this study were to examine the shock absorption capability of addition-cured silicone denture relining materials and the bonding strength of addition-cured silicone denture relining materials and a commercial mouthguard material to determine its applicability to mouthguard adjustment. Two addition-cure...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-378
更新日期:2016-01-01 00:00:00
abstract::The purpose of this study was to characterize the surface damages of zirconia by Nd:YAG dental laser irradiation through a systematic evaluation of the associated microstructural changes. Disk specimens of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) and ceria-stabilized zirconia/alumina nanocomposite (C...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-127
更新日期:2010-10-01 00:00:00
abstract::Oral bacteria adhered to dental material surfaces are known to cause various oral diseases. This study aimed to develop a highsensitive and non-radioisotopic fluorescence dye method for quantification of oral bacteria (Streptococcus, Actinomyces and Veillonella) adhered to denture material surfaces. The amount of adhe...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-060
更新日期:2013-01-01 00:00:00
abstract::This study evaluated the effect of adding silane coupling agent on initial and long-term bond strengths of one-step self-etch adhesives to enamel-dentin-composite in combined situation. Cervical cavities were prepared on extracted molars and filled with Clearfil AP-X. After water-storage for one-week, the filled teeth...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-050
更新日期:2015-01-01 00:00:00
abstract::The purpose of this study was to determine the bonding durability when a Megabond self-etching primer is used with 4-META/MMA-TBB resin to bond metal orthodontic brackets to human premolar enamel. Three conditions of enamel were prepared: Megabond self-etching primer without saliva contamination, Megabond self-etching...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.251
更新日期:2004-09-01 00:00:00
abstract::The aim was to evaluate the effect of different zirconia discontinuous fiber fractions on radiopacity and other selected properties of glass discontinuous fiber-reinforced flowable composite (Exp-SFRC). Exp-SFRC was prepared by mixing 30 wt% of resin-matrix and 45 wt% of particulate-fillers to 25 wt% of various weight...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-102
更新日期:2019-03-31 00:00:00
abstract::This study was designed to examine the effects of dose of recombinant human BMP-2 (rhBMP-2) on bone formation at palatal sites in 10-week-old (10w) and 70-week-old (70w) rats, when combined with a polylactate-polyglycolate copolymer/gelatine sponge (PGS). New bone formation was observed at six weeks after implantation...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.481
更新日期:2007-07-01 00:00:00
abstract::This study investigated the efficacies of adhesive resin cements (Clearfil SA Luting, Maxcem, G-CEM, RelyX Unicem Clicker, Vitremer Paste) for bonding to Ag-Pd-Cu-Au alloy not surface-pretreated with metal primer. For control, Panavia F 2.0 -developed for use with a proprietary metal primer, Alloy Primer- was tested w...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-093
更新日期:2011-01-01 00:00:00
abstract::To recognize good mechanical properties and water-resistance of a dental resin, dimethacryloxyethyl-1,1,6,6-tetrahydro-perfluoro-hexamethylene-1,6-dicarbamate (FDMHD) was newly synthesized. FDMHD initially was a white powder with m.p. 98.5-99.5°C. The copolymers of FDMHD and methyl methacrylate (MMA), FDMHD/MMA copoly...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-126
更新日期:2011-01-01 00:00:00
abstract::The purpose of present investigation was to compare the cyto-genotoxicity induced by five dental alloys in vitro. The cyto-genotoxicity induced by five dental alloy extracts on human B lymphoblast cells was assessed with neutral red uptake (NRU) , CCK-8, comet and micronucleus (CBMN) assays in vitro, respectively. The...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-127
更新日期:2011-01-01 00:00:00
abstract::This study aimed to investigate the relationship between the radiopacity of an experimental light-cured composite resin and the amount and type of its radiopaque material: Ti, SrCO3, ZrO2, BaSO4, or Bi2O3. Radiopacity of each material was evaluated in terms of aluminum equivalent thickness using an aluminum step wedge...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.315
更新日期:2005-09-01 00:00:00
abstract::The fluorescence and physical properties of thulium-doped zirconia were investigated. A standard grade of zirconia (TZ-3Y-E) and two translucent dental zirconia materials (Zpex and Zpex Smile) were examined. The specimens were prepared by addition of 0-1.5 wt% Tm2O3 and then sintering. When exposed to UV light, the Tm...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-384
更新日期:2018-11-30 00:00:00
abstract::Cyclic torsional loading tests were carried out in the laboratory using various implant systems, in order to clarify differences between the systems in loosening of abutment screws. Six samples from six commercially available abutment systems were used, giving a total of 36 samples. Four of the systems used internal c...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-023
更新日期:2015-01-01 00:00:00
abstract::This study determined the discoloration of five CAD/CAM resins, four manually polymerized resins, and glass-ceramic as control group. Specimens were divided into three groups (N=300, n=30) to be stored in coffee, black tea and red wine (n=10). The discoloration was measured using a spectrophotometer after 1, 7, 29, 90...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-238
更新日期:2012-01-01 00:00:00
abstract::The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a newly developed resin cement, ECD-89 (ECD, Tokuyama Dental, Tokyo, Japan) to dentin and to observe the interfacial micromorphology by comparing with two commercial resin cements, Multilink Automix (MA, Ivoclar Vivadent AG, Schaan, Lie...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-122
更新日期:2015-01-01 00:00:00
abstract::The effectiveness of a barbituric acid/copper (II) chloride initiator system in dentin was examined in terms of the effects of barbituric acid structures and dentin conditioners on bond strength. Curing times and tensile bond strengths to bovine dentin were measured for PMMA/MMA resins in conjunction with initiators c...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.14.221
更新日期:1995-12-01 00:00:00
abstract::The human antimicrobial peptide beta-defensin-2 (hBD2) shows broad antibacterial activity and infrequent bacterial resistance. Here mesoporous bioactive glass (MBG) was loaded with hBD2, forming hBD2-loaded MBG (BD-MBG). The antibacterial and osteogenic effects of BD-MBG were investigated in comparison with MBG and th...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2020-105
更新日期:2020-12-24 00:00:00
abstract::The purpose of the present study was to evaluate the effect of four silane coupling agents on the bond strength between two resin-modified glass ionomer cements and a machinable leucite glass ceramic. Ceramic specimens were ground with silicon carbide paper and cleaned with phosphoric acid. They were then conditioned ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.240
更新日期:2007-03-01 00:00:00
abstract::This in vitro study aimed to investigate the effects of glass-ionomer and flowable composite liners on the fracture resistance of Class II amalgam and composite restorations. Group 1 cavities were restored with amalgam and Group 4 cavities with nanofill composite after the application of a dentin-bonding agent. For th...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-053
更新日期:2013-01-01 00:00:00
abstract::The extent of polymerization of light-cured composite resins cured in relatively large class II cavities was estimated by measuring Knoop hardness on sectioned surfaces of resin restorations. The influences of the incremental placement technique, exposure time, and post-curing of resin inlay on the extent of polymeriz...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.159
更新日期:1993-12-01 00:00:00
abstract::The objective of this work was to analyze the antimicrobial and antibiofilm activities of bismuth lipophilic nanoparticles (BisBAL NPs) incorporated into chitosan-based membranes. Chitosan-based membranes were homogeneously embedded with BisBAL NPs, confirming the bismuth presence by scanning electron microscopy. The ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-173
更新日期:2019-07-31 00:00:00
abstract::The aim of this study was to evaluate the trial Teaching Robot for the development of a contact-type measuring apparatus for using directly in the oral cavity. A standard model was used to mimic the dentition by placing an arrangement of three bearing balls. The diameters of the balls were measured. A practical dentit...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.168
更新日期:2003-06-01 00:00:00
abstract::This study investigated transformations of nickel-titanium wires using differential scanning calorimetry (DSC) and thermomechanical analysis (TMA) under tensile load (100 gf or 500 gf). Two nickel-titanium wires, 35°C Copper Ni-Ti and Nitinol SE, were selected. DSC analyses were performed between -90° and 100°C. Speci...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-196
更新日期:2011-01-01 00:00:00