Abstract:
:This study evaluated the polymerization shrinkage, flexural and compressive properties of low-shrinkage resin composites. For the study, four methacrylate-based and one silorane-based resin composites were light cured using three different light-curing units (LCUs) and their polymerization shrinkage, flexural (strength (FS) and modulus (FM)) and compressive (strength (CS) and modulus (CM)) properties were evaluated. Data were statistically analyzed using ANOVA and a post-hoc Tukey test. The polymerization shrinkage ranged approximately 7.6-14.2 μm for 2-mm thick specimens depending on the resin product and LCU. Filtek LS showed the least shrinkage while the rest shrank approximately 13.2-14.2 μm. However, Filtek LS showed the greatest shrinkage difference for the used LCUs. FS and CS of the tested specimens ranged 96.2-152.1 MPa and 239.2-288.4 MPa, respectively, depending on the resin product and LCU. The highest and lowest FS and FM were recorded for the methacrylate-based resin composites. Among the specimens, Filtek LS showed the lowest CS and CM.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Park JK,Lee GH,Kim JH,Park MG,Ko CC,Kim HI,Kwon YHdoi
10.4012/dmj.2013-126subject
Has Abstractpub_date
2014-01-01 00:00:00pages
104-10issue
1eissn
0287-4547issn
1881-1361pii
DN/JST.JSTAGE/dmj/2013-126journal_volume
33pub_type
杂志文章abstract::Gold alloys with Cu contents of 10 mass%, 20%, and 30% were used for morphological observation of porous surface structures after heating at 800 degrees C in air followed by pickling with acid solution. With increasing Cu content in the gold alloy, the internal oxidation zone became well-developed in the alloy matrix....
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.503
更新日期:2005-12-01 00:00:00
abstract::The purpose of this study was to examine the effect of an electro-ionizing toothbrush with stannous fluoride in the treatment of dentin hypersensitivity following periodontal surgery. Thirty-two volunteers with dentin hypersensitivity were divided in two equal groups each using different methods: (Group I) stannous fl...
journal_title:Dental materials journal
pub_type: 临床试验,杂志文章,随机对照试验
doi:10.4012/dmj.20.164
更新日期:2001-06-01 00:00:00
abstract::This study investigated transformations of nickel-titanium wires using differential scanning calorimetry (DSC) and thermomechanical analysis (TMA) under tensile load (100 gf or 500 gf). Two nickel-titanium wires, 35°C Copper Ni-Ti and Nitinol SE, were selected. DSC analyses were performed between -90° and 100°C. Speci...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-196
更新日期:2011-01-01 00:00:00
abstract::Two types of patterns were tested for castability: 1) polyester mesh pattern (20mm x 22mm with 100 open squares) and 2) 20mm x 20mm wax plates 1.0 and 1.5 mm in thickness. These materials were invested using a pre-arranged commercial phosphate-bonded investment for titanium. Three different types of casting machines w...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.245
更新日期:1993-12-01 00:00:00
abstract::The purpose of this study was to evaluate the effects of dentin attrition, phosphoric acid etching, and cyclic loading on the microtensile bond strength (microTBS) of a self-etching adhesive system to dentin. Flat dentin surfaces of human molars were assigned to eight experimental groups based on those with or without...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.28.197
更新日期:2009-03-01 00:00:00
abstract::This study investigated the changes in hardness and Young's modulus of the transparent layer of dentin associated with aging and the carious process. Eighteen extracted human molars with or without coronal caries were used in this study. The normal teeth were divided into two groups by age, and the carious teeth were ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.648
更新日期:2005-12-01 00:00:00
abstract::The aim of this study was to evaluate the effect of resin infiltration on root caries induced by Streptococcus mutans biofilms. Human premolar specimens were divided to 5 groups: negative control (NC), Clearfil SE Bond (SEB), Icon-etch120s+Icon-infiltrant (HA120), Icon-etch10s+Icon-infiltrant (HA10) and K-etchant10s+I...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-229
更新日期:2017-03-31 00:00:00
abstract::This study examined the antimicrobial/antifungal ability of a tissue conditioner containing a photocatalyst for Escherichia coli, Streptococcus mutans, Staphylococcus aureus and Candida albicans. The photocatalyst was mixed with tissue conditioners powders at concentrations of 0, 10, 15, and 20 wt%. Tissue conditioner...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-203
更新日期:2011-01-01 00:00:00
abstract::The torsional fracture strength at the interface between a base plate and veneering material was evaluated for three kinds of veneered restoration: porcelain fused to zirconia (PFZ), porcelain fused to metal (PFM), and composite resin veneered metal (CRVM). The metal and zirconia base plate (30×4×0.4 mm) were prepared...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-432
更新日期:2018-07-29 00:00:00
abstract::The effectiveness of a barbituric acid/copper (II) chloride initiator system in dentin was examined in terms of the effects of barbituric acid structures and dentin conditioners on bond strength. Curing times and tensile bond strengths to bovine dentin were measured for PMMA/MMA resins in conjunction with initiators c...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.14.221
更新日期:1995-12-01 00:00:00
abstract::This study evaluated a new enzyme solution (SFC-V) for dentin caries removal, and obtained results were compared with Carisolv. Both solutions were used with a prototype plastic instrument - this being a modified technique for Carisolv. Five carious deciduous teeth were sectioned, and both treatments were applied alte...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.675
更新日期:2006-12-01 00:00:00
abstract::Finite element analysis was performed to evaluate stress distribution in maxillary central incisors treated endodontically and restored with a post and an all-ceramic crown. Tensile stress at tooth root was analyzed using two-dimensional finite element models with different post diameters and lengths. One post length ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.145
更新日期:2006-03-01 00:00:00
abstract::The purpose of this study was to determine the bonding durability when a Megabond self-etching primer is used with 4-META/MMA-TBB resin to bond metal orthodontic brackets to human premolar enamel. Three conditions of enamel were prepared: Megabond self-etching primer without saliva contamination, Megabond self-etching...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.251
更新日期:2004-09-01 00:00:00
abstract::The purpose of this study was to devise and propose appropriate conditions for the photographing of thermal images in the oral cavity and to evaluate which thermography techniques can be applied to dentistry by evaluating the differences in temperature among oral tissues. Thermal images of oral cavities of 20 voluntee...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.436
更新日期:2003-12-01 00:00:00
abstract::This study compared bovine serum albumin (BSA) adsorption onto octacalcium phosphate (OCP) materials prepared from two wet preparations in the absence (w-OCP) and presence (c-OCP) of gelatin. Raman spectroscopy was used to analyze the BSA adsorption onto OCPs in a 150 mM Tris-HCl buffer containing 0.5 mM calcium and i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-250
更新日期:2020-09-29 00:00:00
abstract::The objective of this study was to clarify the effect of surface topography on osteoblast-like cell behavior on yttria stabilized tetragonal zirconia polycrystals (TZP). Mirror-polished; blasted with 50- or 150-µm alumina (SB50 and SB150); and SB150 acid-etched with hydrofluoric acid (SB150E) were prepared on TZP. Ini...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-208
更新日期:2013-01-01 00:00:00
abstract::This study examined the effect of air abrasion and thermocycling on the adaptation and shear bond strength, of composite resin bonded to dentin using etch-and-rinse and self-etch resin adhesives. Confocal microscopy showed both adhesives closely adapted to dentin and a significantly (p<0.001) greater number of resin t...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-146
更新日期:2012-01-01 00:00:00
abstract::Enamel and dentin particles were added to an experimental 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based one-step adhesive to react for 30 s. After enamel and dentin reactants were analyzed using X-ray diffraction (XRD) and phosphorus-31 nuclear magnetic resonance ((31)P NMR) techniques, curve-fitting analys...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-260
更新日期:2015-01-01 00:00:00
abstract::The objective of this work was to determine the antimicrobial and antibiofilm properties of mineral trioxide aggregate (MTA) supplemented with bismuth lipophilic nanoparticles (BisBAL NPs). The antimicrobial activity of the composite MTA-BisBAL NPs was determined by the disk diffusion assay, while antibiofilm activity...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-259
更新日期:2017-07-26 00:00:00
abstract::The effects of desensitizer, disinfectant, saliva, blood, and hydrogen peroxide on the tensile bond strength between adhesive and ceramic as well as between adhesive and dentin were examined. Sixty 7x3 mm pressed ceramic discs of IPS e.max were fabricated and randomly assigned to six groups of different dentin surface...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-074
更新日期:2010-08-01 00:00:00
abstract::Glass-ceramic powders with the oxide batch formulation 50wt%SiO2, 20wt%P2O5 and 30wt%CaO were prepared by the sol-gel process using tetraethoxysilane, calcium nitrate and phosphoric acid as raw materials. The obtained gels and powders were characterized by TG-DTA thermal analysis, FTIR analyses and XRD measurements. T...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.16.117
更新日期:1997-12-01 00:00:00
abstract::This study was carried out to investigate the influences of elastic moduli of the dowel-core combination on the stress distribution in the root by the use of 2-dimensional finite element analysis. The peak stress at the dowel-cement interface was influenced strongly by a change of elastic modulus of the post (from 20,...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.19.50
更新日期:2000-03-01 00:00:00
abstract::'Tooth-coloured' ProRoot MTA is an endodontic cement comprising an 80:20 wt% mixture of white Portland cement (WPC) and bismuth oxide. The setting reactions within this cement system are not currently well understood. Accordingly, this research monitors the early hydration chemistry of ProRoot MTA by X-ray diffraction...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-309
更新日期:2015-01-01 00:00:00
abstract::The purpose of this study was to evaluate the effect of different polymerization cycles on the flexural strengths and microhardness of two denture base materials (Meliodent and Paladent). Heat-polymerized acrylic resin specimens (65.0 mm long×10.0 mm wide×2.5 mm in height) were prepared using different short and long ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-023
更新日期:2017-03-31 00:00:00
abstract::We evaluated the effect of different curing strategies for universal adhesives on micro-tensile bond strength (μTBS) between resin cement and dentin and/or between resin cement and indirect resin composite. Flat coronal dentin surfaces and composite resin disks were pretreated with silane-containing universal adhesive...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-240
更新日期:2018-06-08 00:00:00
abstract::Improved osseointegration of dental implants is imperative in clinic. Effect of doxycycline on promoting bone formation after implant placement was expected due to its inhibitory properties on inflammation and osteoclastogenesis. To evaluate new bone formation on the hydroxyapatite (HA)-coated implant surface, which w...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-007
更新日期:2018-01-30 00:00:00
abstract::Seven types of amide monomers, methacryloyl tyrosine amide (MTYA), p-methacryloxybenzamide (p-MBA), p-methacryloxybutoxybenzamide (p-MBBA), o-methacryloxybutoxybenzamide (o-MBBA), p-methacryloxybutoxy phenylpropionamide (p-MBPPA), 3,5-dimethacryloxybenzamide (3,5-DMBA), and 3,5-di (methacryloxybutoxy)benzamide (3,5-DM...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.10.165
更新日期:1991-12-01 00:00:00
abstract::The purposes of this study were to examine the shock absorption capability of addition-cured silicone denture relining materials and the bonding strength of addition-cured silicone denture relining materials and a commercial mouthguard material to determine its applicability to mouthguard adjustment. Two addition-cure...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-378
更新日期:2016-01-01 00:00:00
abstract::This study evaluated the irrigation extrusion and smear layer (SL) removal of continuous ultrasonic irrigation (CUI). Forty root canals were shaped, embedded in warm sterile saline agar colored with 1% acid red, and distributed into four groups; three groups had the final irrigation sequence of sodium hypochlorite and...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-411
更新日期:2018-01-30 00:00:00
abstract::This study investigated the durability, especially the nonwaterdegradable qualities, of experimental light-cured composite resin containing barium-borosilicate glass filler. For this purpose, Bis-GMA, a typical component of base monomer in conventional composite resin, was replaced by Bis-GMA-F which is water-repellen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.1
更新日期:1993-06-01 00:00:00