:The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a newly developed resin cement, ECD-89 (ECD, Tokuyama Dental, Tokyo, Japan) to dentin and to observe the interfacial micromorphology by comparing with two commercial resin cements, Multilink Automix (MA, Ivoclar Vivadent AG, Schaan, Liechtenstein) and Panavia F2.0 (PF, Kuraray Noritake Dental, Tokyo, Japan). Flat dentin surfaces of human third molars were exposed using #600 SiC. After application of primer and cement to the dentin surface, each cement was applied and cured with light (light condition) or without light (dark condition). The teeth were sectioned to obtain beams (1 mm×1 mm) after 24 h of water storage. The mean bond strengths and SDs (MPa) were: ECD: 68.6±14.9, MA: 39.2±18.9, PF: 39.4±18.5 and ECD: 54.5±22.4, MA: 36.7±15.6, PF: 13.4±4.46 when cured in light and dark condition, respectively. In both conditions, ECD-89 showed statistically higher µTBS than the others.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Kawano S,Fu J,Saikaew P,Chowdhury AA,Fukuzawa N,Kadowaki Y,Kakuda S,Hoshika S,Nakaoki Y,Ikeda T,Tanaka T,Sano Hdoi
10.4012/dmj.2014-122subject
Has Abstractpub_date
2015-01-01 00:00:00pages
61-9issue
1eissn
0287-4547issn
1881-1361journal_volume
34pub_type
杂志文章abstract::The purpose of this study was to examine the antibacterial activity of composite resin with glass-ionomer filler particles versus that of contemporary commercial composite resins. Three composite resins were used: Beautifil II (containing S-PRG filler), Clearfil AP-X, and Filtek Z250. Resin blocks were bonded to maxil...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-050
更新日期:2010-03-01 00:00:00
abstract::The purpose of this study was to investigate the effect of remaining dentin thickness (RDT) and long term water storage on dentin bond strength in-vitro. Twenty-seven third molars were randomly divided into 3 groups: Clearfil Bond SE ONE (SE1, Kuraray Noritake Dental, Okayama, Japan), G-Bond plus (GB, GC, Tokyo, Japan...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-140
更新日期:2018-07-29 00:00:00
abstract::The possibility of the segregation under solidification process using a centrifugal casting machine was investigated using an electron probe microanalyzer with elemental distribution map, line analysis and quantitative analysis. When a very small quantity of platinum was added to local molten titanium during the casti...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.15.212
更新日期:1996-12-01 00:00:00
abstract::The objective of the study was to compare 1) the mean micro-shear bond strength and 2) failure mode of cements to metals in nonenclosed and mold-enclosed specimens. Specimens were prepared in mold-enclosed and non-enclosed formats from two RMGIC's and a self-adhesive resin-cement. 3-way ANOVA analysis and Tukey post h...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-065
更新日期:2013-01-01 00:00:00
abstract::This research was conducted to investigate the bond strength between artificial teeth and a thermoplastic denture base resin for injection molding with different surface preparations for use in flexible resin removable partial dentures. Composite resin denture teeth and acrylic denture resin teeth were bonded to three...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2020-183
更新日期:2021-01-15 00:00:00
abstract::The purpose of this study was to propose a new numerical modeling of the glass fiber cloth reinforced denture base resin (GFRP). The proposed model is constructed with an isotropic shell, beam and orthotropic shell elements representing the outmost resin, interlaminar resin and glass fiber cloth, respectively. The pro...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.21.105
更新日期:2002-06-01 00:00:00
abstract::The mechanical properties of resin-modified "hybrid" glass-ionomers, for both restorative and liner/base applications, were assessed by a flexural test and compared with those of conventional acid-base glass-ionomers. Flexural strength, flexural modulus, and the modulus of resilience were determined 30 minutes after m...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.14.109
更新日期:1995-12-01 00:00:00
abstract::The aim of the present study was to measure various mechanical properties of acrylic denture base resins, including flexural modulus, flexural strength, fracture toughness, Barcol and Vickers hardness and their related properties, and to investigate correlations between different mechanical properties. Resin specimens...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-205
更新日期:2012-02-03 00:00:00
abstract::The cream type of denture adhesives after use cannot be easily removed from oral mucosa and have the potential risk to change the oral flora. The effects of the temperature-responsive hydrogel Pluronic F-127 (PF) on the complex viscosity of denture adhesives were evaluated. Carboxy methylcellulose (CMC) mass fractions...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-191
更新日期:2016-01-01 00:00:00
abstract::To elucidate the mechanism of dimensional changes in alginate impression in solutions, the relationship between the ion concentrations in three types of solutions (nonelectrolyte and monovalent and divalent metallic salts) and change in gel volume was examined. The gel in the monovalent metallic salt solution expanded...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.19.396
更新日期:2000-12-01 00:00:00
abstract::To investigate the bonding of tooth-colored indirect restorations to cervical dentin, shear bond strengths of bonded resin inlays to cervical dentin and mid-coronal dentin were investigated and compared. Indirectly fabricated composite inlays (Estenia) were cemented with a dual-cured resin cement (Panavia Fluoro Cemen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.7
更新日期:2006-03-01 00:00:00
abstract::The purpose of this study was to characterize the surface damages of zirconia by Nd:YAG dental laser irradiation through a systematic evaluation of the associated microstructural changes. Disk specimens of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) and ceria-stabilized zirconia/alumina nanocomposite (C...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-127
更新日期:2010-10-01 00:00:00
abstract::Comparative studies on two-body sliding wear resistance were performed between a hybrid composite resin and conventional light-curing composite veneering materials. This study investigated the wear resistance of hybrid composite resins compared with three composite resin veneering materials for 12%Au-Ag-Pd alloy, the ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.21.225
更新日期:2002-09-01 00:00:00
abstract::The purpose of this review is to summarise recent advances in the design and composition of bioactive surface layers of implantabile biomaterials, and thus the genetic potential of osteoprogenitor cells to recognize and respond to these diverse implanted biomaterials. Changes applied to a biomaterial's surface, in gen...
journal_title:Dental materials journal
pub_type: 杂志文章,评审
doi:10.4012/dmj.19.99
更新日期:2000-06-01 00:00:00
abstract::This study investigated the changes in hardness and Young's modulus of the transparent layer of dentin associated with aging and the carious process. Eighteen extracted human molars with or without coronal caries were used in this study. The normal teeth were divided into two groups by age, and the carious teeth were ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.648
更新日期:2005-12-01 00:00:00
abstract::The purpose of this study was to determine the optimal condition for fabricating accurate crowns efficiently using an internet-based CAD/CAM system. The influences of three different CAD/CAM restorative materials (titanium, porcelain, and composite resin) and three different step-over scanning distances (0.01 mm, 0.11...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.549
更新日期:2007-07-01 00:00:00
abstract::The present study investigated the influences of a denture strengthener on the deformation of a maxillary complete denture. Three groups of maxillary complete dentures were fabricated (Group 1 without a strengthener; Group 2 with a Co-Cr alloy wire strengthener; Group 3 with an experimental fiberglass strengthener). T...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.507
更新日期:2009-07-01 00:00:00
abstract::The aim of this study was to compare the shear bond strengths (SBS), failure modes (adhesive, cohesive, or mixed), and marginal microleakage occurrence of conventional resin (CR)-based, glass ionomer (GI)-based, and self-adhesive resin (SAR)-based fissure sealants with or without prior phosphoric acid (PA) etching. Fi...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-227
更新日期:2014-01-01 00:00:00
abstract::The behavior of microencapsulated polymerization initiators in dental adhesives is unknown. This study investigated the effects of new microencapsulated initiators in novel, multi-purpose, PMMA-type adhesive resin on the bonding performance and polymerization reactivity. Microencapsulated BPO and 1,3,5-trimethylbarbit...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.35
更新日期:2008-01-01 00:00:00
abstract::This study aimed to evaluate the effect of sulfinic acid sodium salt interposition after acid and sodium hypochlorite treatment (NC treatment) on dentin bonding durability using a mild type one-step self-etching adhesive. Fifteen human third molars were randomly assigned into three experimental groups according to den...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-105
更新日期:2017-11-29 00:00:00
abstract::The influence of a thin carbonate-containing hydroxyapatite (CA) coating to tetragonal zirconia polycrystal (TZP) on osteoblastlike cell response was investigated. TZP disks were subjected to blasting and acid etching. Thin CA coatings were deposited by the molecular precursor method (TZP-CA). Initial cell adhesion of...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-122
更新日期:2014-01-01 00:00:00
abstract::The aim of this study was to evaluate temperature changes in the pulp chamber during polymerization of four different pulp-capping materials using a LED-light-curing-unit in the contact and noncontact positions. A pulpal circulation mechanism was simulated to measure increases in temperature in four pulp-capping mater...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-274
更新日期:2014-01-01 00:00:00
abstract::Despite progress in the development of denture base resin and artificial tooth materials, dental clinics are still plagued with artificial teeth falling off the denture base--due to poor bond strength--after denture delivery. Against this background, this study sought to examine the effect and durability of an adhesiv...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.75
更新日期:2006-03-01 00:00:00
abstract::The objective of this study was to test the hypothesis that thermal cycling weakens the flexural strength of porcelain. Specimens of Deguceram Gold and Vita Omega 900 were tested in four groups of 30 specimens each: in the original glazed condition versus being ground with 1000-grit, 600-grit, and 100-grit silicon car...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.433
更新日期:2009-07-01 00:00:00
abstract::This study investigated the anti-demineralization effects of surface pre-reacted glass-ionomer (S-PRG) filler-containing varnishes. Thirty-five bovine root specimens were divided into five treatment groups, with seven specimens each coated with 1) MI varnish (MIV), 2) F varnish (FV), 3) PRG varnish I (PV), 4) PRG varn...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-396
更新日期:2020-11-11 00:00:00
abstract::The aim of our study was twofold: to immobilize an organosilicon quaternary ammonium salt (3-(trimethoxysilyl)-propyldimethyl-octadecyl ammonium chloride, Si-QAC) on the surface of pure titanium and to investigate the antimicrobial activity of Si-QAC-immobilized titanium against microbial adherence and biofilm formati...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.570
更新日期:2005-12-01 00:00:00
abstract::The aim of this review is to evaluate the long-term effectiveness of calcium silicate-based cement (CS) and calcium hydroxide (CH) for direct pulp capping (DPC) to human pulp-exposed permanent teeth. An electronic search and manual search were performed on 21 June 2019. Long-term clinical and radiographic evaluations ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2020-043
更新日期:2020-10-01 00:00:00
abstract::With a view to understanding the structure-property relation of a silicone-based soft lining denture material after polymerization, its chemical composition and viscoelastic properties were investigated. Chemical compositions of the cured and uncured polymers of a commercial silicone permanent soft liner were determin...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:
更新日期:2007-05-01 00:00:00
abstract::The blending effect (BE) plays an important role in esthetics of the composite resin. The objective of this study was to determine the extents to which filler size and content affect the BE. Three types of fillers (0.7, 1.0, and 1.5 µm) were mixed at weight contents of 60, 70, 75, and 80%. This study simulated clinica...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-083
更新日期:2017-01-31 00:00:00
abstract::This study evaluated the influence of heat treatment (HT) of the silane on the microtensile bond strength of resin cement to a feldspathic ceramic. Ceramic (VITA VM7) and composite blocks (N=32) were divided into four groups (n=6 for bond test, n=2 for SEM) at random and subject to following sequence of conditioning: ...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:
更新日期:2011-01-01 00:00:00