Abstract:
:The blending effect (BE) plays an important role in esthetics of the composite resin. The objective of this study was to determine the extents to which filler size and content affect the BE. Three types of fillers (0.7, 1.0, and 1.5 µm) were mixed at weight contents of 60, 70, 75, and 80%. This study simulated clinical class 3 or 4 cavities and quantitatively measured the color diffusion of the objects next to the cavities based on the CIELab color space. For each filler size, there was a trend of increasing BE as the filler content was increased. The translucency parameter (TP) exhibited the opposite trend of decreasing (p<0.05) with increases in filler content. The filler size did not affect the BE, and the different filler sizes produced statistically non-significant results in this study. Increases in filler content elevated the opacity of the composite resin and significantly influenced the BE.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Suh YR,Ahn JS,Ju SW,Kim KMdoi
10.4012/dmj.2016-083subject
Has Abstractpub_date
2017-01-31 00:00:00pages
35-40issue
1eissn
0287-4547issn
1881-1361journal_volume
36pub_type
杂志文章abstract::The physical properties of experimental visible light-activated resins containing dyestuff, which could be quickly discolored by irradiation was, evaluated by analyzing light absorbance characteristics and measuring micro Vickers hardness. The experimental resin, which was prepared by mixing equivalent weights of Bis ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.8.147
更新日期:1989-12-01 00:00:00
abstract::This study investigated the changes in hardness and Young's modulus of the transparent layer of dentin associated with aging and the carious process. Eighteen extracted human molars with or without coronal caries were used in this study. The normal teeth were divided into two groups by age, and the carious teeth were ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.648
更新日期:2005-12-01 00:00:00
abstract::The aim of this study was to evaluate the trial Teaching Robot for the development of a contact-type measuring apparatus for using directly in the oral cavity. A standard model was used to mimic the dentition by placing an arrangement of three bearing balls. The diameters of the balls were measured. A practical dentit...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.168
更新日期:2003-06-01 00:00:00
abstract::The objective of this study was to evaluate, using methylene blue (MB), the effects of various light sources on the bleaching action of hydrogen peroxide (H(2)O(2)) with two titanium dioxide (TiO(2)) photocatalysts - an ultraviolet light-activated TiO(2) photocatalyst (UVTiO(2)) versus a visible light-activated TiO(2)...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.693
更新日期:2009-11-01 00:00:00
abstract::The effects of monomer structure on the mechanical properties of visible light-cured composite resins based on the seven types of aromatic dimethacrylates were investigated. The results of this study suggested that the mechanical properties of the composite resins were dependent upon the chemical structure of the dime...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.8.40
更新日期:1989-06-01 00:00:00
abstract::Despite progress in the development of denture base resin and artificial tooth materials, dental clinics are still plagued with artificial teeth falling off the denture base--due to poor bond strength--after denture delivery. Against this background, this study sought to examine the effect and durability of an adhesiv...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.75
更新日期:2006-03-01 00:00:00
abstract::The aim of the present study was to examine whether interconnected porous hydroxyapatite ceramics (IP-CHA) could be used as bone substitute for implant treatment in reconstructive surgery. We firstly assessed if surround of the titanium surface placed into granular or block-type IP-CHA can observe new bone formation i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-169
更新日期:2013-01-01 00:00:00
abstract::The aim of this investigation was to compare the cleaning and shaping efficiency of Self-adjusting file and Protaper, and to assess the correlation between root canal curvature and working time in mandibular molars using micro-computed tomography. Twenty extracted mandibular molars instrumented with Protaper and Self-...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-255
更新日期:2017-09-26 00:00:00
abstract::This study aimed to evaluate the effect of sulfinic acid sodium salt interposition after acid and sodium hypochlorite treatment (NC treatment) on dentin bonding durability using a mild type one-step self-etching adhesive. Fifteen human third molars were randomly assigned into three experimental groups according to den...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-105
更新日期:2017-11-29 00:00:00
abstract::We examined the mold filling capacity and microhardness of two industrial 1% Fe titanium alloys: Super-TIX800 (Nippon Steel Corp.) (Fe: 0.910%, O: 0.370%, N: 0.005%) and Super-TIX800N (Nippon Steel Corp.) (Fe: 0.960%, O: 0.300%, N: 0.041%). Two wedge-shaped acrylic patterns (with 30 degrees or 15 degrees angles) were ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.211
更新日期:2004-06-01 00:00:00
abstract::The purpose of this study was to evaluate the effects of ultrasonic and manual placement techniques on the push-out bond strength of Biodentine and MTA with and without calcium chloride. One hundred and twenty mid-root slices from forty freshly extracted single-rooted human mandibular premolar teeth were instrumented ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-094
更新日期:2016-10-01 00:00:00
abstract::The aim of this study was to investigate the bond durability of heat-polymerized denture base resin to cast CP Ti and Co-Cr alloy. The alloy specimens were divided into five groups: 1) airborne-particle abraded with 50 µm alumina (SAND), 2) Rocatec tribochemical silica coating system (RO), 3) air-abraded followed by a...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2010-089
更新日期:2011-01-01 00:00:00
abstract::This study aimed to evaluate the inhibitory effect of experimental pastes containing surface pre-reacted glass ionomer (S-PRG) fillers on enamel demineralization. Bovine blocks were treated twice a day for 4 days by 7 groups; experimental pastes containing 0-30 wt% S-PRG filler (S00, S01, S05, S10, and S30), deionized...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-303
更新日期:2017-07-26 00:00:00
abstract::A new tensile fatigue test using a stainless steel screw was introduced. A transparent PMMA rod was selected as the test material. A hole was drilled and tapped into the rod; a screw was put into the rod with dental cement or without cementation. Three types of cyclic loads were applied to the test piece; the number o...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.11.141
更新日期:1992-12-01 00:00:00
abstract::The extent of polymerization of light-cured composite resins cured in relatively large class II cavities was estimated by measuring Knoop hardness on sectioned surfaces of resin restorations. The influences of the incremental placement technique, exposure time, and post-curing of resin inlay on the extent of polymeriz...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.159
更新日期:1993-12-01 00:00:00
abstract::The purpose of this study was to evaluate the effect of various incremental filling techniques on adhesion between composite and cavity floor using light-cured resin composite. Black ABS resin and hybrid resin composite were used as mold materials--instead of dentin--for the preparation of cavities, and standardized t...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.503
更新日期:2006-09-01 00:00:00
abstract::Though zirconia has been used in dental implant fixtures, the biocompatibility of the zirconia surface is not optimal for the surrounding tissue, and many surface modifications have been attempted. We have developed a novel method for improving the biocompatibility of zirconia by incorporating Ca ions. Elemental analy...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-199
更新日期:2015-01-01 00:00:00
abstract::In tissue engineering, biodegradable polymer materials with both high biocompatibility and high strength are very important as scaffolds for long term use. Therefore, in this research, we tried to prepare the three types of poly(L-lactic acid) (PLLA)/calcium phosphate (CP) hybrid composite for a scaffold biomaterial. ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-117
更新日期:2012-01-01 00:00:00
abstract::The aim of our study was twofold: to immobilize an organosilicon quaternary ammonium salt (3-(trimethoxysilyl)-propyldimethyl-octadecyl ammonium chloride, Si-QAC) on the surface of pure titanium and to investigate the antimicrobial activity of Si-QAC-immobilized titanium against microbial adherence and biofilm formati...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.570
更新日期:2005-12-01 00:00:00
abstract::To elucidate the cause of brittleness of porcelain fused to pure titanium (PFPT) which leads to chipping and cracking similar to that of conventional porcelain in clinical use, fracture toughness KIc, hardness (Hv and Hk) and fracture energy gamma reflecting the bonding energy of atoms were evaluated. In KIc there wer...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.532
更新日期:2003-12-01 00:00:00
abstract::The use of a single metal for all restorations would be necessary because it protects against metal corrosion caused by the contact of different metals. For this "one-metal rehabilitation" concept, non-alloyed commercially pure (CP) titanium should be used for all restorations. Titanium frameworks have been cast and u...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-137
更新日期:2017-09-26 00:00:00
abstract::The behavior of microencapsulated polymerization initiators in dental adhesives is unknown. This study investigated the effects of new microencapsulated initiators in novel, multi-purpose, PMMA-type adhesive resin on the bonding performance and polymerization reactivity. Microencapsulated BPO and 1,3,5-trimethylbarbit...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.35
更新日期:2008-01-01 00:00:00
abstract::The bactericidal efficacy of 1.00-4.50% glycine-type amphoteric surfactant (Gly) was evaluated by measuring its microorganism removal rate in denture plaque. Physical and mechanical properties such as surface roughness, color difference, and bending strength of two different denture base resins were determined before ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.307
更新日期:2009-05-01 00:00:00
abstract::The effect of acidic fluoride solution on NiTi arch wires was examined by testing crystal structure, tensile strength, morphology after fracture, and element release from wire under four different test solutions after 1 or 3 d immersion. Three-day immersion in a 0.2%/pH 4 solution did not form any new crystal structur...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.557
更新日期:2004-12-01 00:00:00
abstract::Bioactive-glass (B-G) is a material known for its favorable biological response when in contact with surrounding fibro-osseous tissues, due not only to an osteoconductive property, but also to an osteostimulatory capacity, and superior biocompatibility for use in human body. The objectives of this paper are to review ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-233
更新日期:2015-01-01 00:00:00
abstract::The aim of this study was to investigate in how far the way the specimen is fixed to the testing device influences the micro-tensile bond strength of adhesives to dentin. Compared to a flat jig, a notched jig enables the specimen to be aligned easier and more accurately perpendicular to the interface, thereby concentr...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.694
更新日期:2007-09-01 00:00:00
abstract::To clarify the mechanical properties of fiber-reinforced hybrid resin bridges, this study evaluated the influence of various bonding agents ((Modeling Liquid (ML), DE Resin (DE), Bell Bond (BE), Mega Bond (MG), Durafil Bond (DU), Fluoro Bond (FB), Mac-Bond (MC), EG Bond (EG), Unifill Bond (UN), Single Bond (SN)) impre...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.723
更新日期:2008-09-01 00:00:00
abstract::The objective of this study was to test the hypothesis that thermal cycling weakens the flexural strength of porcelain. Specimens of Deguceram Gold and Vita Omega 900 were tested in four groups of 30 specimens each: in the original glazed condition versus being ground with 1000-grit, 600-grit, and 100-grit silicon car...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.433
更新日期:2009-07-01 00:00:00
abstract::This study evaluated the irrigation extrusion and smear layer (SL) removal of continuous ultrasonic irrigation (CUI). Forty root canals were shaped, embedded in warm sterile saline agar colored with 1% acid red, and distributed into four groups; three groups had the final irrigation sequence of sodium hypochlorite and...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-411
更新日期:2018-01-30 00:00:00
abstract::We investigated the adsorption of lipoteichoic acid (LTA) on titanium surfaces by using the quartz crystal microbalance (QCM) method, and confirmed the influence of mucin (MUC) pre-adsorption on LTA adsorption. Two injection methods were evaluated. Namely, Method A: single-step injection of LTA solution to the Ti sens...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-209
更新日期:2020-12-03 00:00:00