Abstract:
:The aim of this review is to evaluate the long-term effectiveness of calcium silicate-based cement (CS) and calcium hydroxide (CH) for direct pulp capping (DPC) to human pulp-exposed permanent teeth. An electronic search and manual search were performed on 21 June 2019. Long-term clinical and radiographic evaluations of the effectiveness of CS and CH for DPC to human pulp-exposed teeth were included, and data extraction, risk-of-bias assessment and meta-analyses were performed. From 645 identified articles, 7 articles met the eligibility criteria. The meta-analyses comparing CS with CH and Biodentine with mineral trioxide aggregates (MTA) on DPC success rate were performed, and significant difference was observed between CS and CH (risk ratio=1.20; p=0.005), whereas no significant difference was observed between Biodentine and MTA. CS seems to be a more effective and predictable DPC material than CH; however, these analyses are based on the studies judged at high risk of bias.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Matsuura T,Ziauddin SM,Kawata-Matsuura VKS,Sugimoto K,Yamada S,Yoshimura Adoi
10.4012/dmj.2020-043subject
Has Abstractpub_date
2020-10-01 00:00:00eissn
0287-4547issn
1881-1361pub_type
杂志文章abstract::The blending effect (BE) plays an important role in esthetics of the composite resin. The objective of this study was to determine the extents to which filler size and content affect the BE. Three types of fillers (0.7, 1.0, and 1.5 µm) were mixed at weight contents of 60, 70, 75, and 80%. This study simulated clinica...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-083
更新日期:2017-01-31 00:00:00
abstract::The purpose of the present study was to evaluate the bond strength between a fiber-reinforced composite (FRC) and six luting agents (Panavia F 2.0, Linkmax MC, Chemiace II, Multibond, Super-Bond C&B, and Fuji I). A prosthodontic resin composite material (RC-control) and a luting agent containing no functional monomer ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.628
更新日期:2007-09-01 00:00:00
abstract::Temperature dependencies of thermal expansion coefficients for the alloys of Pd-Ag, Pd-Cu and Pd-Co binary systems were measured at temperatures up to 900 degrees C, with heating and cooling rates of 5 degrees C/min. The coefficient of thermal expansion of alloys with no transformation in the temperature range of inte...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.9.47
更新日期:1990-06-01 00:00:00
abstract::The aim of the study was to evaluate bone regeneration using a canine model with surgically created periodontal defects filled for 12 weeks using a stratified biomaterial consisting in a biphasic calcium phosphate (BCP) covered with a crosslinking hydrogel acting as polymer membrane of silated hydroxypropyl methylcell...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-238
更新日期:2018-09-30 00:00:00
abstract::Seven types of amide monomers, methacryloyl tyrosine amide (MTYA), p-methacryloxybenzamide (p-MBA), p-methacryloxybutoxybenzamide (p-MBBA), o-methacryloxybutoxybenzamide (o-MBBA), p-methacryloxybutoxy phenylpropionamide (p-MBPPA), 3,5-dimethacryloxybenzamide (3,5-DMBA), and 3,5-di (methacryloxybutoxy)benzamide (3,5-DM...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.10.165
更新日期:1991-12-01 00:00:00
abstract::This paper reviews the development of dental adhesives by collating information of related studies from original scientific papers, reviews, and patent literatures. Through our development, novel radical polymerization initiators, adhesive monomers, and microcapsules were synthesized, and their effects on adhesion wer...
journal_title:Dental materials journal
pub_type: 杂志文章,评审
doi:10.4012/dmj.2009-057
更新日期:2010-03-01 00:00:00
abstract::In tissue engineering, biodegradable polymer materials with both high biocompatibility and high strength are very important as scaffolds for long term use. Therefore, in this research, we tried to prepare the three types of poly(L-lactic acid) (PLLA)/calcium phosphate (CP) hybrid composite for a scaffold biomaterial. ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-117
更新日期:2012-01-01 00:00:00
abstract::The torsional fracture strength at the interface between a base plate and veneering material was evaluated for three kinds of veneered restoration: porcelain fused to zirconia (PFZ), porcelain fused to metal (PFM), and composite resin veneered metal (CRVM). The metal and zirconia base plate (30×4×0.4 mm) were prepared...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-432
更新日期:2018-07-29 00:00:00
abstract::The aim of this study was to investigate the relationship between the different mechanical properties with the filler fraction of various resin composites. Mechanical properties of eighteen different resin composites were investigated in this study; flexural strength (FS), flexural modulus (FM), fracture toughness (FT...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-178
更新日期:2013-01-01 00:00:00
abstract::The purpose of this study was to examine the antibacterial activity of composite resin with glass-ionomer filler particles versus that of contemporary commercial composite resins. Three composite resins were used: Beautifil II (containing S-PRG filler), Clearfil AP-X, and Filtek Z250. Resin blocks were bonded to maxil...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-050
更新日期:2010-03-01 00:00:00
abstract::Although titanium has been widely used in prosthetic appliances, such as cast removable partial denture frameworks, high quality castings are still difficult to obtain. This study proposes a new partition technique using a metal foil for improving castability of a two-chamber pressure casting unit. The metal foil was ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.19.307
更新日期:2000-09-01 00:00:00
abstract::This research was conducted to investigate the bond strength between artificial teeth and a thermoplastic denture base resin for injection molding with different surface preparations for use in flexible resin removable partial dentures. Composite resin denture teeth and acrylic denture resin teeth were bonded to three...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2020-183
更新日期:2021-01-15 00:00:00
abstract::The purpose of this study was to investigate the effect of laser irradiation on the enamel surface spectroscopically. Polished bovine enamel surface was irradiated with an Er:YAG laser apparatus and chemically analyzed using X-ray photoelectron spectroscopy (XPS). XPS detected core electron peaks such as carbon (C 1s)...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.214
更新日期:2006-06-01 00:00:00
abstract::Comparative studies on two-body sliding wear resistance were performed between a hybrid composite resin and conventional light-curing composite veneering materials. This study investigated the wear resistance of hybrid composite resins compared with three composite resin veneering materials for 12%Au-Ag-Pd alloy, the ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.21.225
更新日期:2002-09-01 00:00:00
abstract::This study evaluated the influence of heat treatment (HT) of the silane on the microtensile bond strength of resin cement to a feldspathic ceramic. Ceramic (VITA VM7) and composite blocks (N=32) were divided into four groups (n=6 for bond test, n=2 for SEM) at random and subject to following sequence of conditioning: ...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:
更新日期:2011-01-01 00:00:00
abstract::The purpose of this study was to determine the optimal condition for fabricating accurate crowns efficiently using an internet-based CAD/CAM system. The influences of three different CAD/CAM restorative materials (titanium, porcelain, and composite resin) and three different step-over scanning distances (0.01 mm, 0.11...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.549
更新日期:2007-07-01 00:00:00
abstract::This study investigated hydrogen peroxide (H2O2) concentration of two home bleaching gels, in their dispensing syringes and their degradation in vivo in intraoral bleaching trays. Two bleaching gels were studied, 7.5% hydrogen peroxide (HP) and 20% carbamide peroxide (CP). The concentration of H2O2 was determined in d...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-317
更新日期:2013-01-01 00:00:00
abstract::This study aimed to evaluate the inhibitory effect of experimental pastes containing surface pre-reacted glass ionomer (S-PRG) fillers on enamel demineralization. Bovine blocks were treated twice a day for 4 days by 7 groups; experimental pastes containing 0-30 wt% S-PRG filler (S00, S01, S05, S10, and S30), deionized...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-303
更新日期:2017-07-26 00:00:00
abstract::In this study, different glasses were investigated to improve reusable investments. Borosilicate glass (BSG) powder and soda-lime glass (SLG) powder were prepared by milling broken beakers and microscope slides, respectively, and used in experimental investments (I-BSG, I-SLG) by blending glass powder (10 wt%) with cr...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-040
更新日期:2011-01-01 00:00:00
abstract::The purpose of this study was to evaluate the effects of acid-etched titanium on the biological responses of osteoblast-like MC3T3-E1 cells. Four types of treatments (polishing, sandblasting, concentrated H2SO4 etching, and concentrated H2SO4 etching with vacuum firing) were carried out on the surfaces of commercially...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.415
更新日期:2008-05-01 00:00:00
abstract::The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-023
更新日期:2011-01-01 00:00:00
abstract::This study was designed to examine the effects of dose of recombinant human BMP-2 (rhBMP-2) on bone formation at palatal sites in 10-week-old (10w) and 70-week-old (70w) rats, when combined with a polylactate-polyglycolate copolymer/gelatine sponge (PGS). New bone formation was observed at six weeks after implantation...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.481
更新日期:2007-07-01 00:00:00
abstract::This study evaluated and compared the influence of different supporting abutment models on the fracture loads of three-unit fixed dental prostheses (FDPs) fabricated from the following materials (n=24/material): (i) IPS e.max CAD-on, (ii) IPS e.max ZirCAD, and (iii) Telio CAD. Twelve FDPs of each group were adhesively...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-344
更新日期:2014-01-01 00:00:00
abstract::The objective of this study was to clarify the effect of surface topography on osteoblast-like cell behavior on yttria stabilized tetragonal zirconia polycrystals (TZP). Mirror-polished; blasted with 50- or 150-µm alumina (SB50 and SB150); and SB150 acid-etched with hydrofluoric acid (SB150E) were prepared on TZP. Ini...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-208
更新日期:2013-01-01 00:00:00
abstract::This study investigated the effects of storing impressions for 3 hours after spraying them with a disinfectant solution on dimensional change and deformation of maxillary edentulous stone models. Three brands of alginate impression materials, characterized by a small degree of contraction in 100% relative humidity, we...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-083
更新日期:2010-05-01 00:00:00
abstract::Atmospheric-pressure cold plasma was applied to process the surface of heat-polymerized acrylic resin. Changes to the physical properties and early adherence of Candida albicans were investigated. Alternating current cold plasma with Ar/O2 as working gas was used. Scanning electron microscopy (SEM) and X-ray photoelec...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-035
更新日期:2015-01-01 00:00:00
abstract::The depths of calcium-ion incorporation into a commercially pure titanium and an experimental beta-type titanium alloy were determined using Auger electron spectroscopy. After the electrochemical deposition of apatite, new compositional gradients appeared in the profiles in which the Ca and P concentrations gradually ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.21.306
更新日期:2002-12-01 00:00:00
abstract::To evaluate the effect of a dentin adhesive on sclerotic dentin, contraction gap width and shear bond strength were measured. Dentin cavity wall was pretreated with an experimental dentin bonding system with and without a dentin primer, or with a commercial dentin bonding system. In the experimental dentin bonding gro...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.576
更新日期:2006-09-01 00:00:00
abstract::The effectiveness of a barbituric acid/copper (II) chloride initiator system in dentin was examined in terms of the effects of barbituric acid structures and dentin conditioners on bond strength. Curing times and tensile bond strengths to bovine dentin were measured for PMMA/MMA resins in conjunction with initiators c...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.14.221
更新日期:1995-12-01 00:00:00
abstract::A zirconia-binding peptide motif was identified using a peptide phage display system. Yttria stabilized zirconia beads and discs were used as the target. Quartz crystal microbalance was used to monitor the binding of phages to zirconia. Starting from a library of phages displaying random sequences of 12-mer peptides, ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-161