Abstract:
:Fracture resistance of provisional restorations is an important clinical concern. This property is directly related to transverse strength. Strengthening of provisional fixed partial dentures may result from reinforcement with various fiber types. This study evaluated the effect of fiber type and water storage on the transverse strength of a commercially available provisional resin under two different conditions. The denture resin was reinforced with either glass or aramid fiber or no reinforcement was used. Uniform samples were made from a commercially available autopolymerizing provisional fixed partial denture resin. Sixteen bar-shaped specimens (60 x 10 x 4 mm) were reinforced with pre-treated epoxy resin-coated glass fibers, with aramid fibers, or with no fibers. Eight specimens of each group, with and without fibers, were tested after 24 h of fabrication (immediate group), and after 30-day water storage. A three-point loading test was used to measure the transverse strength, the maximal deflection, and the modulus of elasticity. The Kruskal-Wallis Analysis of Variance was used to examine differences among the three groups, and then the Mann-Whitney U Test and Wilcoxon Signed Ranks Test were applied to determine pair-wise differences. The transverse strength and the maximal deflection values in the immediate group and in the 30-day water storage group were not statistically significant. In the group tested immediately, the elasticity modulus was found to be significant (P = 0.042). In the 30-day water storage group, all the values were statistically insignificant. The highest transverse strength was displayed by the glass-reinforced resin (66.25MPa) in the immediate group. The transverse strength value was 62.04MPa for the unreinforced samples in the immediate group. All the specimens exhibited lower transverse strength with an increase in water immersion time. The transverse strength value was 61.13 MPa for the glass-reinforced resin and was 61.24 MPa for the unreinforced resin. The aramid-reinforced resin decreased from 62.29 to 58.77 MPa. The addition of fiber reinforcement enhanced the physical properties (the transverse strength, the maximal deflection, the modulus of elasticity) of the processed material over that seen with no addition of fiber. Water storage did not statistically affect the transverse strength of the provisional denture resin compared to that of the unreinforced resin. The transverse strength was lowered at water storage but it was not statistically significant. The transverse strength was enhanced by fiber addition compared to the unreinforced resin. The glass fiber was superior to the other fiber. Also the modulus of elasticity was enhanced by fiber addition compared to the unreinforced resin.
journal_name
J Biomater Appljournal_title
Journal of biomaterials applicationsauthors
Uzun G,Keyf Fdoi
10.1177/0885328203017004003subject
Has Abstractpub_date
2003-04-01 00:00:00pages
277-86issue
4eissn
0885-3282issn
1530-8022journal_volume
17pub_type
杂志文章abstract::A multifunctional targeted nanoplatform combining photothermal therapy and chemotherapy has emerged as a promising strategy for comprehensive therapies of breast cancer. In this study, we constructed human epidermal growth factor receptor 2 (Her2)-targeted gold nanoshelled poly(lactic-co-glycolic acid) hybrid nanocaps...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328220929616
更新日期:2020-09-01 00:00:00
abstract::The aim of this study was to investigate the effect of C-Graft particles on formation of new cementum and bone in periodontal bone defects in dog. Healing and tissue change were histologically determined at 2, 4, 8, and 16 weeks. Little bone or cementum formation was observed in the control group. A statistically sign...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328208094427
更新日期:2009-08-01 00:00:00
abstract:PURPOSE:To produce biodurable small diameter microporous vascular grafts with self-sealing properties for vascular access, for peripheral vascular and potentially for coronary artery bypass. The prosthesis should retain compliance and pulsatile flow in situ using a unique modus operandi permitting wall compression whic...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829501000207
更新日期:1995-10-01 00:00:00
abstract::We assess the effects of chemical processing, ethylene oxide sterilization, and threading on bone surface and mechanical properties of bovine undecalcified bone screws. In addition, we evaluate the possibility of manufacturing bone screws with predefined dimensions. Scanning electronic microscopic images show that che...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328208092110
更新日期:2009-03-01 00:00:00
abstract::In this study, a novel bilayer scaffold composed of electrospun polycaprolactone and poly(lacto-co-glycolic acid) (PCL/PLGA) membrane and glutaraldehyde (3.5% v/v) cross-linked chitosan/gelatin hydrogel was fabricated using two methods: electrospinning of the membrane onto the lyophilized hydrogel (BS-1) and membrane ...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328211416527
更新日期:2013-01-01 00:00:00
abstract::Silicate-based cements have been developed as a class of bioactive and biodegradable bone cements owing to their good in vitro bioactivity and ability to dissolve in a simulated body fluid. Until recently, however, the in vivo evidence of their ability to support bone regeneration is still scarce. In the present study...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328217715428
更新日期:2017-08-01 00:00:00
abstract::Polysulfone (PSU) composite films filled with Beta-dicalcium silicate (Beta-Ca(2)SiO(4)) particles are prepared by the solvent casting-evaporation method. The surface morphologies and mechanical properties of the films are determined. The bioactivity of the composite films is evaluated by soaking them in simulated bod...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328206054712
更新日期:2006-04-01 00:00:00
abstract::Biodegradable sponges, as a promising hemostatic biomaterial, has been clinically required over the past decades. Current hemostatic sponges are generally prepared by crosslinking and freeze-drying, but the quality control or biocompatibility is often unsatisfactory due to the freezing-caused morphological non-uniform...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328216687663
更新日期:2017-03-01 00:00:00
abstract::Excessive demineralization in osteoporotic bones impairs its self-regeneration potential following a defect/fracture and is of great concern among the aged population. In this context, implants with inherent osteogenic ability loaded with therapeutic ions like Strontium (Sr2+) may bring forth promising outcomes. Micro...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328216647197
更新日期:2016-10-01 00:00:00
abstract::Dicalcium phosphate dihydrate particles functionalized with triethyleneglycol dimethacrylate were synthesized and added to a photocurable mixture of bisphenol-A glycidyl dimethacrylate and triethyleneglycol dimethacrylate with the purpose of developing a resin composite capable of releasing calcium and phosphate ions ...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328216680116
更新日期:2017-01-01 00:00:00
abstract::A range of crystalline and nano-sized carbonate- and silicate-substituted hydroxyapatite has been successfully produced by using continuous hydrothermal flow synthesis technology. Ion-substituted calcium phosphates are better candidates for bone replacement applications (due to improved bioactivity) as compared to pha...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328212460289
更新日期:2013-09-01 00:00:00
abstract::The aim of this work was to study the cytotoxicity of different fractions of gold nanoparticles prepared by ultrasonic spray pyrolysis from gold scrap. The target cells were rat thymocytes, as a type of nonproliferating cells, and L929 mouse fibroblasts, as a type of continuous proliferating cells. Fractions 1 and 2, ...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328210377536
更新日期:2012-01-01 00:00:00
abstract::Osteo-odonto-keratoprostheses, incorporating dental laminate material as an anchoring skirt around a central poly(methyl methacrylate) (PMMA) optic, have been used to replace the cornea for many years. However, there are many intricacies associated with the use of autologous dental laminate material, surgical complexi...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328220972219
更新日期:2020-11-11 00:00:00
abstract::A rapid and continuous hydrothermal route for the synthesis of nano-sized hydroxyapatite rods co-precipitated with calcium-doped zirconia nanoparticles using a superheated water flow at 450°C and 24.1 MPa as a crystallizing medium is described. Hydroxyapatite and calcium-doped zirconia phases in the powder mixtures co...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328212444483
更新日期:2012-07-01 00:00:00
abstract::Bone tissue engineering, which relies on the interactions between stem cells and suitable scaffold materials, represents a highly desirable alternative to currently used allograft or autograft strategies for the treatment of bone defects caused by injury or disease, with one of the major challenges being to generate s...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328213515734
更新日期:2014-07-01 00:00:00
abstract::Adhesions commonly occur after internal disease or surgery. The natural healing response leads to the formation of vascular and avascular adhesions after inflammatory diseases and surgical interventions. A barrier film could be incorporated during surgery between layers of tissues that must not adhere to one another. ...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829601100203
更新日期:1996-10-01 00:00:00
abstract::The purpose of this research was to develop novel nanoparticles (NPs) of star-like copolymer mannitol-functionalized poly(lactide)-vitamin E TPGS (M-PLA-TPGS) for paclitaxel delivery for prostate cancer treatment, and evaluate their therapeutic effects in prostate cancer cell line and animal model in comparison with t...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328214527486
更新日期:2014-09-01 00:00:00
abstract::In this study, the effects of sodium carbonate (Na(2)CO(3) ) solution with different concentrations (10, 15, 20, and 25 wt%) as liquid phase on the setting time and compressive strength of tricalcium silicate bone cements are investigated. The in vitro bioactivity and degradability of the resultant Ca(3)SiO(5)-Na(2)CO...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328208088714
更新日期:2008-11-01 00:00:00
abstract::In this work, we report brushite-based calcium phosphate cement (CPC) system to enhance the in vivo biodegradation and tissue in-growth by incorporation of micro-channeled hydroxyapatite (HAp) granule and silicon and sodium addition in calcium phosphate precursor powder. Sodium- and silicon-rich calcium phosphate powd...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328215601938
更新日期:2016-01-01 00:00:00
abstract::NiTi alloy is used as a biomaterial due to its pseudoelastic behaviour. It exhibits a great potential in dental and orthopedic applications where constant correcting loads are required. In order to use such materials, it is necessary to investigate the effect of the cyclic straining upon the transformation stresses an...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829801200304
更新日期:1998-01-01 00:00:00
abstract::A new diol, bis[2-(2-hydroxyethyldimethylammonio)ethyl] butylenediphosphate, that contains two phosphatidylcholine analogous moieties in one diol molecule, was synthesized and characterized. The diol together with 1,4-butanediol as chain extender was further incorporated into the propolymer of poly(ethylene oxide) (Mn...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829701200205
更新日期:1997-10-01 00:00:00
abstract::A biosensor for the analysis of D-amino acids is described. Carbon paste (graphite/paraffin oil) was chemically modified with immobilized D-amino acid oxidase and either horse-radish peroxidase or fungal peroxidase from Arthromyces ramosus. The two enzymes dissolved in buffer, together with an amine containing oligome...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829300800204
更新日期:1993-10-01 00:00:00
abstract::Calcium polyphosphate is a biodegradable bone substitute. It remains a challenge to prepare porous calcium polyphosphate with desired gradient porous structures. In this study, a modified one-step gravity sintering method was used to prepare calcium polyphosphate scaffolds with desired-gradient-pore-size distribution....
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328215608335
更新日期:2016-02-01 00:00:00
abstract::An experimental and computational investigation of the self-tapping ability of carbon fibre reinforced polyetheretherketone (CFR-PEEK) has been conducted. Six CFR-PEEK suture anchor designs were investigated using PEEK-OPTIMA® Reinforced, a medical grade of CFR-PEEK. Experimental tests were conducted to investigate th...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328214535274
更新日期:2014-10-01 00:00:00
abstract::A series biodegradable poly (γ-glutamic acid)/beta-tricalcium phosphate (γ-PGA/TCP) nanocomposites were prepared which were composed of poly-γ-glutamic acid polymerized in situ with β-tricalcium phosphate and physiochemically characterized as bone graft substitutes. The particle size via dynamic light scattering, the ...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328216632444
更新日期:2016-07-01 00:00:00
abstract::Tendon tears are a relevant concern for today's national health systems because of their social impact and high recurrence rate. The current gold standard for fixing tendon tears is surgical repair; however, this strategy is not able to fully re-establish tendon integrity and functionality. Tissue engineering approach...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328218779846
更新日期:2018-07-01 00:00:00
abstract::Compounds of a silicone elastomer suitable for preparing maxillofacial prostheses, reinforced with various amounts of silica powder, have been studied for their mechanical response and wetting properties in terms of contact angle. Tensile strength and elongation at break showed an increase with increasing silica volum...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829801300104
更新日期:1998-07-01 00:00:00
abstract::The adhesion of platelets, red blood cells, and lymphocytes onto various polymer substrates, hydrophobic to hydrophilic in nature, has been studied. Cell adhesion is found to be higher on hydrophilic substrates. The stability of these adhered cells has also been studied under a flow rate of 20 ml/min. Further the effe...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/088532829100600105
更新日期:1991-07-01 00:00:00
abstract::Medical sheets are useful in surgically repair vascular disease. To avoid long-term side effects, they are to be replaced with regenerated tissue after implantation. Silk fibroin is a fibrous protein secreted by silkworm. The advantage of silk fibroin is its biocompatibility and has been used as regenerative artificia...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328220928660
更新日期:2020-06-02 00:00:00
abstract::Sustained intestinal delivery of thiamine hydrochloride (Vitamin B(1); VB(1)) and pyridoxine hydrochloride (Vitamin B(6); VB(6)) seems to be a feasible alternative to existing therapy. The vitamins (VB(1)/VB(6)) intercalated in montmorillonite (MMT) and intercalated VB(1)/VB(6)-MMT hybrid is further used for synthesis...
journal_title:Journal of biomaterials applications
pub_type: 杂志文章
doi:10.1177/0885328209344003
更新日期:2010-08-01 00:00:00