Abstract:
:This study aimed to evaluate the effect of an acidic-adjusted pH of solvent in silanization on the amount of fluoride released and mechanical properties of heat-cured acrylic resin containing a silanized fluoride-releasing filler. The experimental groups were divided into 4 groups; non-silanized, acidic-adjusted pH, non-adjusted pH, and no filler as control. For fluoride measurement, each specimen was placed in deionized water which was changed every day for 7 days, every week for 7 weeks and measured. The flexural strength and flexural modulus were evaluated after aging for 48 h, 1, and 2 months. Two-way ANOVA indicated significant differences among groups, storage times, and its interaction in fluoride measurement and flexural modulus. For flexural strength, there was significant difference only among groups. Acidic-adjusted pH of solvent in silanization enhanced the amount of fluoride released from acrylic resin, while non-adjusted pH of solvent exhibited better flexural strength of acrylic resin.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Nakornchai N,Arksornnukit M,Kamonkhantikul K,Takahashi Hdoi
10.4012/dmj.2015-403subject
Has Abstractpub_date
2016-01-01 00:00:00pages
440-6issue
3eissn
0287-4547issn
1881-1361journal_volume
35pub_type
杂志文章abstract::The aim of the present study was to measure various mechanical properties of acrylic denture base resins, including flexural modulus, flexural strength, fracture toughness, Barcol and Vickers hardness and their related properties, and to investigate correlations between different mechanical properties. Resin specimens...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-205
更新日期:2012-02-03 00:00:00
abstract::The purpose of the present study was to evaluate the bond strength between a fiber-reinforced composite (FRC) and six luting agents (Panavia F 2.0, Linkmax MC, Chemiace II, Multibond, Super-Bond C&B, and Fuji I). A prosthodontic resin composite material (RC-control) and a luting agent containing no functional monomer ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.628
更新日期:2007-09-01 00:00:00
abstract::We aimed to establish an experimental animal model to evaluate materials for endodontic therapy. We focused on the biocompatibility of new paste-type zinc oxide-eugenol (ZOE) sealer. The results of this sealer were compared with those of conventional powder/liquid ZOE and eugenol-free sealers. The molars of Wistar rat...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-095
更新日期:2011-01-01 00:00:00
abstract::This study investigated the effects of storing impressions for 3 hours after spraying them with a disinfectant solution on dimensional change and deformation of maxillary edentulous stone models. Three brands of alginate impression materials, characterized by a small degree of contraction in 100% relative humidity, we...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-083
更新日期:2010-05-01 00:00:00
abstract::High-power light-curing units have emerged that reduce the time of procedures in dental clinical work. However, patients sometimes complain of pain during the polymerization of composite resin. In this experiment, we investigated how differences in light-curing mode affect the temperature rise during composite resin p...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-158
更新日期:2019-07-31 00:00:00
abstract::Sixteen alloys and five pure metals were used and the open circuit potentials (OCP) and the coupled potentials with titanium were measured in five kinds of solutions. All alloys and metals showed the maximum OCP in 1.3% lactic acid solution, and the minimum in 0.01% sodium sulfide solution. The coupled potential depen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.20.75
更新日期:2001-03-01 00:00:00
abstract::To investigate the bonding of tooth-colored indirect restorations to cervical dentin, shear bond strengths of bonded resin inlays to cervical dentin and mid-coronal dentin were investigated and compared. Indirectly fabricated composite inlays (Estenia) were cemented with a dual-cured resin cement (Panavia Fluoro Cemen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.7
更新日期:2006-03-01 00:00:00
abstract::The objective of this work was to determine the antimicrobial and antibiofilm properties of mineral trioxide aggregate (MTA) supplemented with bismuth lipophilic nanoparticles (BisBAL NPs). The antimicrobial activity of the composite MTA-BisBAL NPs was determined by the disk diffusion assay, while antibiofilm activity...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-259
更新日期:2017-07-26 00:00:00
abstract::Oral bacteria adhered to dental material surfaces are known to cause various oral diseases. This study aimed to develop a highsensitive and non-radioisotopic fluorescence dye method for quantification of oral bacteria (Streptococcus, Actinomyces and Veillonella) adhered to denture material surfaces. The amount of adhe...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-060
更新日期:2013-01-01 00:00:00
abstract::This study evaluated the influence of heat treatment (HT) of the silane on the microtensile bond strength of resin cement to a feldspathic ceramic. Ceramic (VITA VM7) and composite blocks (N=32) were divided into four groups (n=6 for bond test, n=2 for SEM) at random and subject to following sequence of conditioning: ...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:
更新日期:2011-01-01 00:00:00
abstract::The influence of a thin carbonate-containing hydroxyapatite (CA) coating to tetragonal zirconia polycrystal (TZP) on osteoblastlike cell response was investigated. TZP disks were subjected to blasting and acid etching. Thin CA coatings were deposited by the molecular precursor method (TZP-CA). Initial cell adhesion of...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-122
更新日期:2014-01-01 00:00:00
abstract::The clinical feasibility of a novel device called a Cariotester was investigated by measuring the Knoop hardness (KHN) of white spot lesions diagnosed as ICDAS code 1, 2 or 3. To obtain an equation for converting the Cariotester indentation depth into the KHN, a regression analysis was performed between the depth and ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-282
更新日期:2015-01-01 00:00:00
abstract::Glass-ceramic powders with the oxide batch formulation 50wt%SiO2, 20wt%P2O5 and 30wt%CaO were prepared by the sol-gel process using tetraethoxysilane, calcium nitrate and phosphoric acid as raw materials. The obtained gels and powders were characterized by TG-DTA thermal analysis, FTIR analyses and XRD measurements. T...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.16.117
更新日期:1997-12-01 00:00:00
abstract::The bonding efficacy of sclerotic dentin was determined by measuring the polymerization contraction gap width of a commercial light-activated resin composite in a cervical defect and by measuring the micro-Vicker's hardness at the dentin adhesive surface; morphological characteristics were observed using a scanning el...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.20.359
更新日期:2001-12-01 00:00:00
abstract::To evaluate the effect of a dentin adhesive on sclerotic dentin, contraction gap width and shear bond strength were measured. Dentin cavity wall was pretreated with an experimental dentin bonding system with and without a dentin primer, or with a commercial dentin bonding system. In the experimental dentin bonding gro...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.576
更新日期:2006-09-01 00:00:00
abstract::The purpose of this study was to analyze the ultrastructures and chemical compositions of precipitates formed on mineral trioxide aggregate (MTA; White ProRoot MTA) immersed in distilled water (DW) or phosphate buffered saline (PBS), based on the attribution that MTA's bioactivity and sealing ability are influenced by...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-133
更新日期:2010-10-01 00:00:00
abstract::This study evaluated the effects of combining enamel microabrasion and dental bleaching on the physical properties of enamel, using in vitro and in situ conditions and evaluating surface roughness, enamel microhardness and scanning electron microscopy images. One hundred sound bovine teeth were sectioned and cut into ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-334
更新日期:2016-01-01 00:00:00
abstract::This study compared differences in discoloration and dissolution in several titanium alloys with immersion in peroxide- or fluoride-containing solution. Commercially pure titanium (CP-Ti) and six titanium-based alloys were used: Ti-0.15Pd, Ti-6Al-4V, Ti-7Nb-6Al, Ti-55Ni, Ti-10Cu, and Ti-20Cr. Two test solutions were p...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.117
更新日期:2008-01-01 00:00:00
abstract::The blending effect (BE) plays an important role in esthetics of the composite resin. The objective of this study was to determine the extents to which filler size and content affect the BE. Three types of fillers (0.7, 1.0, and 1.5 µm) were mixed at weight contents of 60, 70, 75, and 80%. This study simulated clinica...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-083
更新日期:2017-01-31 00:00:00
abstract::The aim of this in vitro study was to evaluate the effects of desensitizer pre-treatment on in-office bleaching using an artificial discoloration tooth model. The stained specimens were divided into four groups (n=10); without application (Control group), Shield Force plus (SF group), UltraEz (UE group) and Teeth Mate...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-129
更新日期:2019-10-02 00:00:00
abstract::This study investigated the anti-demineralization effects of surface pre-reacted glass-ionomer (S-PRG) filler-containing varnishes. Thirty-five bovine root specimens were divided into five treatment groups, with seven specimens each coated with 1) MI varnish (MIV), 2) F varnish (FV), 3) PRG varnish I (PV), 4) PRG varn...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-396
更新日期:2020-11-11 00:00:00
abstract::The use of a single metal for all restorations would be necessary because it protects against metal corrosion caused by the contact of different metals. For this "one-metal rehabilitation" concept, non-alloyed commercially pure (CP) titanium should be used for all restorations. Titanium frameworks have been cast and u...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-137
更新日期:2017-09-26 00:00:00
abstract::This study evaluated the irrigation extrusion and smear layer (SL) removal of continuous ultrasonic irrigation (CUI). Forty root canals were shaped, embedded in warm sterile saline agar colored with 1% acid red, and distributed into four groups; three groups had the final irrigation sequence of sodium hypochlorite and...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-411
更新日期:2018-01-30 00:00:00
abstract::The purpose of this review is to summarise recent advances in the design and composition of bioactive surface layers of implantabile biomaterials, and thus the genetic potential of osteoprogenitor cells to recognize and respond to these diverse implanted biomaterials. Changes applied to a biomaterial's surface, in gen...
journal_title:Dental materials journal
pub_type: 杂志文章,评审
doi:10.4012/dmj.19.99
更新日期:2000-06-01 00:00:00
abstract::The aim of this study was to investigate in how far the way the specimen is fixed to the testing device influences the micro-tensile bond strength of adhesives to dentin. Compared to a flat jig, a notched jig enables the specimen to be aligned easier and more accurately perpendicular to the interface, thereby concentr...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.694
更新日期:2007-09-01 00:00:00
abstract::Supercritical water was used as a modification method of electrochemically deposited apatite on pure titanium. The apatites were coated on a commercially pure titanium plate using a hydrothermal-electrochemical method. A constant direct current at 12.5 mA/cm2 was loaded for 1 hr at 25, 60, 100, 150 and 200 degrees C i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.20.247
更新日期:2001-12-01 00:00:00
abstract::This study compared bovine serum albumin (BSA) adsorption onto octacalcium phosphate (OCP) materials prepared from two wet preparations in the absence (w-OCP) and presence (c-OCP) of gelatin. Raman spectroscopy was used to analyze the BSA adsorption onto OCPs in a 150 mM Tris-HCl buffer containing 0.5 mM calcium and i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-250
更新日期:2020-09-29 00:00:00
abstract::The aim of this study was to evaluate temperature changes in the pulp chamber during polymerization of four different pulp-capping materials using a LED-light-curing-unit in the contact and noncontact positions. A pulpal circulation mechanism was simulated to measure increases in temperature in four pulp-capping mater...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-274
更新日期:2014-01-01 00:00:00
abstract::The purpose of this study was to establish a method using FTIR to evaluate the polymerization characteristics of UDMA-based resins. Three kinds of experimental UDMA-based resins were prepared with various molar fractions. IR spectra of the cured film specimens were measured with FTIR before and after extracting residu...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.18.176
更新日期:1999-06-01 00:00:00
abstract::Adhesion promoting monomers for dental metals, 5-(4-vinylbenzyl)-2-thiobarbituric acid (5VS), 6- (4-vinylbenzyl-n-propyl) amino-1,3,5-triazine-2,4-dithione (VBATDT) and 9,10-epithiodecyl methacrylate (EP8MA), were synthesized and surface treatment agents were prepared by dissolving each monomer in ethanol or acetone. ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.343
更新日期:2003-09-01 00:00:00