Abstract:
:This in vitro study aimed to investigate the effects of glass-ionomer and flowable composite liners on the fracture resistance of Class II amalgam and composite restorations. Group 1 cavities were restored with amalgam and Group 4 cavities with nanofill composite after the application of a dentin-bonding agent. For the remaining groups, light-cured-glass-ionomer liner was used in a gingival floor proximal box (Groups 2, 5) or flowable composite was used as a liner (Groups 3, 6), the remainder of the cavity was restored with amalgam (Groups 2, 3) or composite (Groups 5, 6). The restorations were loaded in compression to failure. The data was analyzed using Tukey's multiple comparison test. The fracture resistance was significantly higher (p<0.05) in Group 3 than in all other groups, except Group 2 (p>0.05). Flowable composite, glass-ionomer liners increased the fracture resistance of open-sandwich Class II amalgam restorations.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Güray Efes B,Yaman BC,Gümüştaş B,Tıryakı Mdoi
10.4012/dmj.2013-053subject
Has Abstractpub_date
2013-01-01 00:00:00pages
877-82issue
6eissn
0287-4547issn
1881-1361pii
DN/JST.JSTAGE/dmj/2013-053journal_volume
32pub_type
杂志文章abstract::This study investigated the durability, especially the nonwaterdegradable qualities, of experimental light-cured composite resin containing barium-borosilicate glass filler. For this purpose, Bis-GMA, a typical component of base monomer in conventional composite resin, was replaced by Bis-GMA-F which is water-repellen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.1
更新日期:1993-06-01 00:00:00
abstract::The purpose of this study was to devise and propose appropriate conditions for the photographing of thermal images in the oral cavity and to evaluate which thermography techniques can be applied to dentistry by evaluating the differences in temperature among oral tissues. Thermal images of oral cavities of 20 voluntee...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.436
更新日期:2003-12-01 00:00:00
abstract::The depths of cure and the distributions of degree of conversion (DC), polymerization conversion (PC) and percent pendant double bonds (PDB) of light-cured composite resins cured under various intensities of light were investigated. When the total amount of exposure, represented by the product of the light intensity a...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.13.198
更新日期:1994-12-01 00:00:00
abstract::The aim of this investigation was to compare the cleaning and shaping efficiency of Self-adjusting file and Protaper, and to assess the correlation between root canal curvature and working time in mandibular molars using micro-computed tomography. Twenty extracted mandibular molars instrumented with Protaper and Self-...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-255
更新日期:2017-09-26 00:00:00
abstract::This study was carried out to investigate the influences of elastic moduli of the dowel-core combination on the stress distribution in the root by the use of 2-dimensional finite element analysis. The peak stress at the dowel-cement interface was influenced strongly by a change of elastic modulus of the post (from 20,...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.19.50
更新日期:2000-03-01 00:00:00
abstract::Using a scanning electron microscope (SEM) and an electron probe surface roughness analyzer (ERA), we conducted the in vivo study of the effect of various filler components on the wear of composite resins. Experimental light-cured composite resins were prepared employing three different filler components; -(1) Silica ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.13.36
更新日期:1994-06-01 00:00:00
abstract::The purpose of the present study was to evaluate the effect of four silane coupling agents on the bond strength between two resin-modified glass ionomer cements and a machinable leucite glass ceramic. Ceramic specimens were ground with silicon carbide paper and cleaned with phosphoric acid. They were then conditioned ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.240
更新日期:2007-03-01 00:00:00
abstract::This study evaluated the effects of ceramic surface treatment agents on shear bond strengths to ceramic materials with and without thermocycling. Ceramic plates were prepared from feldspathic ceramic; AAA, lithium disilicate ceramic material; IPS e.max Press, zirconia ceramic; Lava. Ceramic surfaces were pretreated wi...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-383
更新日期:2017-11-29 00:00:00
abstract::The efficacy of four commercial and two experimental dentin bonding systems was examined by observing the cavity adaptation of commercial light-cured resin composites restored in the dogs scheduled to be sacrificed after a medical experiment. Before being sacrificed, a cylindrical class V cavity was prepared in each c...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.17.195
更新日期:1998-09-01 00:00:00
abstract::The mechanical properties of polycarboxylate cements containing 20 mass% of four kinds of aluminoborate whiskers with different fiber lengths and diameters were evaluated. Bending strength of the cements increased with increase in fiber length, whereby the strength of the cement with the longest fiber was about two ti...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.561
更新日期:2008-07-01 00:00:00
abstract::The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to e...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-012
更新日期:2018-01-30 00:00:00
abstract::The purpose of this study was to characterize the surface damages of zirconia by Nd:YAG dental laser irradiation through a systematic evaluation of the associated microstructural changes. Disk specimens of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) and ceria-stabilized zirconia/alumina nanocomposite (C...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-127
更新日期:2010-10-01 00:00:00
abstract::The purposes of this study were to examine the shock absorption capability of addition-cured silicone denture relining materials and the bonding strength of addition-cured silicone denture relining materials and a commercial mouthguard material to determine its applicability to mouthguard adjustment. Two addition-cure...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-378
更新日期:2016-01-01 00:00:00
abstract::The mechanical properties of resin-modified "hybrid" glass-ionomers, for both restorative and liner/base applications, were assessed by a flexural test and compared with those of conventional acid-base glass-ionomers. Flexural strength, flexural modulus, and the modulus of resilience were determined 30 minutes after m...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.14.109
更新日期:1995-12-01 00:00:00
abstract::This study evaluated the sealing ability and push-out bond strength of two luting cements cured with two different types of light curing units (LCU): light-emitting diode (LED) versus quartz tungsten halogen (QTH). Forty teeth were divided into four groups(n=10/group). Quartz fiber posts (D. T. Light-Post) were luted ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-209
更新日期:2012-01-01 00:00:00
abstract::Mechanical responses of the test specimen under bidirectional and unidirectional loading were investigated using a newly developed masticatory simulator. The simulator adopted a four-bar linkage mechanism to create both loading patterns. Scratch/occlusal contact characteristics, contact force profiles and the fracture...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2016-198
更新日期:2016-01-01 00:00:00
abstract::This study assessed the impact of surface treatments and repair resin reinforcement with zirconium oxide nano-particles (nano-ZrO2) on flexural strength (FS) of repaired denture base. A total of 320 heat-polymerized acrylic resin specimens were prepared and sectioned creating 2-mm gap. According to repair surface trea...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-436
更新日期:2020-06-05 00:00:00
abstract::Enamel and dentin particles were added to an experimental 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based one-step adhesive to react for 30 s. After enamel and dentin reactants were analyzed using X-ray diffraction (XRD) and phosphorus-31 nuclear magnetic resonance ((31)P NMR) techniques, curve-fitting analys...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-260
更新日期:2015-01-01 00:00:00
abstract::The purpose of this study was to evaluate the influence of heating, cast bonding, and subsequent polishing procedures on attractive force of magnetic attachments. Two magnetic attachment systems with keepers of different chemical compositions (Hicorexslim 3013, 447J1; Magfit EX400, AUM20) were employed. Keepers examin...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.393
更新日期:2007-05-01 00:00:00
abstract::This study examined the surface microhardness of four kinds of resin composites with different fillers and resin matrices. Ten specimens of 2 mm thickness and 4 mm diameter of each resin composite were polymerized using a halogen light, a blue light-emitted diode, and a plasma arc unit. Microhardness evaluation was pe...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:
更新日期:2007-11-01 00:00:00
abstract::This study sought to evaluate the effects of different staining solutions on the colour stability of nanocomposites compared with microhybrid resin and to evaluate the degree of conversion of these two materials. Two different shades of two different composites were cured in polytetraflouroethylene disk rings. Coffee,...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-267
更新日期:2013-01-01 00:00:00
abstract::The aim of this study was to compare the shear bond strengths (SBS), failure modes (adhesive, cohesive, or mixed), and marginal microleakage occurrence of conventional resin (CR)-based, glass ionomer (GI)-based, and self-adhesive resin (SAR)-based fissure sealants with or without prior phosphoric acid (PA) etching. Fi...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-227
更新日期:2014-01-01 00:00:00
abstract::Bioactive-glass (B-G) is a material known for its favorable biological response when in contact with surrounding fibro-osseous tissues, due not only to an osteoconductive property, but also to an osteostimulatory capacity, and superior biocompatibility for use in human body. The objectives of this paper are to review ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-233
更新日期:2015-01-01 00:00:00
abstract::The aim of this study was to investigate in how far the way the specimen is fixed to the testing device influences the micro-tensile bond strength of adhesives to dentin. Compared to a flat jig, a notched jig enables the specimen to be aligned easier and more accurately perpendicular to the interface, thereby concentr...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.26.694
更新日期:2007-09-01 00:00:00
abstract::The purpose of this study was to determine the bonding durability when a Megabond self-etching primer is used with 4-META/MMA-TBB resin to bond metal orthodontic brackets to human premolar enamel. Three conditions of enamel were prepared: Megabond self-etching primer without saliva contamination, Megabond self-etching...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.251
更新日期:2004-09-01 00:00:00
abstract::The extent of polymerization of light-cured composite resins cured in relatively large class II cavities was estimated by measuring Knoop hardness on sectioned surfaces of resin restorations. The influences of the incremental placement technique, exposure time, and post-curing of resin inlay on the extent of polymeriz...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.159
更新日期:1993-12-01 00:00:00
abstract::Adhesion promoting monomers for dental metals, 5-(4-vinylbenzyl)-2-thiobarbituric acid (5VS), 6- (4-vinylbenzyl-n-propyl) amino-1,3,5-triazine-2,4-dithione (VBATDT) and 9,10-epithiodecyl methacrylate (EP8MA), were synthesized and surface treatment agents were prepared by dissolving each monomer in ethanol or acetone. ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.343
更新日期:2003-09-01 00:00:00
abstract::Supercritical water was used as a modification method of electrochemically deposited apatite on pure titanium. The apatites were coated on a commercially pure titanium plate using a hydrothermal-electrochemical method. A constant direct current at 12.5 mA/cm2 was loaded for 1 hr at 25, 60, 100, 150 and 200 degrees C i...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.20.247
更新日期:2001-12-01 00:00:00
abstract::This study investigated the effect of a coating material containing S-PRG fillers on the demineralization of bovine enamel and dentin, by measuring changes in the transmitted ultrasonic velocity. Bovine enamel and dentin specimens with and without coating (n=6 for each condition) were cut into blocks, immersed in 0.1 ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-153
更新日期:2012-01-01 00:00:00
abstract::The study evaluated changes in total enzymatic activity and degradation of demineralized dentin following the application of universal or self-etch adhesives. The universal adhesives -Scotchbond Universal (SU) and All-Bond Universal (ABU) and self-etch adhesives -Adper Easy Bond (EB) and G-aenial Bond (GB) were used f...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-304
更新日期:2020-12-03 00:00:00