Abstract:
:Aim of the study was to examine if the addition of buffering sodiumhydrogenphosphate to poly(D,L)lactide(PDLLA) would stabilize the pH-value in the in vivo environment of implanted material and whether this improves its biocompatibility. The material was predegraded just to the point of viscous disintegration to test the PDLLA in the moment of its most aggressive effect on the surrounding tissue. Racemic amorphous PDLLA was injection-molded with or without the admixture of 1 mol NaP per 100 mol lactate, the degradation product of PDLLA (=1 mol%) to form 20mm x 3 mm x 2mm rods. Predegradation was performed by storing the rods at 55 degrees C for 14 days, just to the point of beginning dissolution. Predegraded PDLLA or PDLLA + NaP samples were used for in vitro incubation tests, as well as for the in vivo study, where the rods were implanted into the spinal muscles of 30 male Wistar rats. Repeatedly, measurements of the pH-value were made in the incubation solutions in vitro. The surrounding tissue of the implanted samples as well as the normal contralateral muscle tissue was checked for its pH-value in a group of 3 rats, respectively, anaesthesized at various time intervals after implantation. After these measurements the implants and their surrounding tissues were excised for histological examination. In Ringer's solution pH-values dropped immediately within the first week of incubation of both predegraded materials reaching -4 pH units after 4 weeks in the PDLLA containing medium, after 6 weeks in the PDLLA + NaP containing medium. Soerensen buffer slowed the pH decrease with significant differences between the material groups up to the 28th week. In vivo, the pH of the surrounding tissue was influenced by the implanted PDLLA material up to the 4th week, while the admixture of NaP resulted in a significant pH stabilization. A higher quantity of macrophages and giant cells were seen between the 2nd and 6th week after the implantation in the environment of pure PDLLA compared with PDLLA + NaP. Complete resorption of predegraded pure PDLLA or PDLLA + NaP from the extracellular space was reached 28 weeks postimplantation in vivo. Thus, sodiumhydrogenphosphate improves the biocompatibility of degrading PDLLA at the point of viscous disintegration by stabilizing the pH-value in the environment of the implants for several weeks and reducing adverse tissue reactions.
journal_name
Biomaterialsjournal_title
Biomaterialsauthors
Heidemann W,Jeschkeit-Schubbert S,Ruffieux K,Fischer JH,Jung H,Krueger G,Wintermantel E,Gerlach KLdoi
10.1016/s0142-9612(02)00046-7keywords:
subject
Has Abstractpub_date
2002-09-01 00:00:00pages
3567-74issue
17eissn
0142-9612issn
1878-5905pii
S0142-9612(02)00046-7journal_volume
23pub_type
杂志文章相关文献
BIOMATERIALS文献大全abstract::Acellular porcine cornea stroma (APCS) prepared using pancreatic phospholipase A(2) was proven to be promising corneal scaffold. However, its dense ultrastructure provides insufficient space that prevents the seeded cells from organizing into a functional tissue. In this report, freezing dry APCS (FD-APCS) biomaterial...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2011.05.084
更新日期:2011-10-01 00:00:00
abstract::The formation of a confluent endothelium on expanded polytetrafluoroethylene (PTFE) vascular prostheses has never been observed. This lack of endothelialization is known to be one of the main reasons leading to the development of thromboses and/or intimal hyperplasia. In this context, several efforts were put forward ...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2005.05.051
更新日期:2005-12-01 00:00:00
abstract::Nanoparticles, such as dendritic polymers, are currently investigated as excellent candidates for drug delivery vehicles. In this study, we report the preparation and characterization of mPEGylated peptide dendron-doxorubicin (dendron-DOX) conjugate based vehicle carrying 14.0 wt% (weight percent) of doxorubicin (DOX)...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2012.11.007
更新日期:2013-02-01 00:00:00
abstract::The electrospinning process was utilized successfully to fabricate the random oriented and aligned electrically conductive nanofibers of biodegradable poly-DL-lactide (PLA) in which multiwalled carbon nanotubes (MWCNTs) were embedded. The topographical features of the composite nanofibers were characterized by SEM. Th...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2011.01.051
更新日期:2011-04-01 00:00:00
abstract::Saturated neoglycopolymers, prepared via tandem ROMP-hydrogenation (ROMP=ring-opening metathesis polymerization) of carbohydrate-functionalized norbornenes, are investigated as novel collagen crosslinking agents in corneal tissue engineering. The neoglycopolymers were incorporated into recombinant human collagen type ...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2009.06.016
更新日期:2009-10-01 00:00:00
abstract::The recent introduction of microseparation of the components of ceramic-on-ceramic hip prostheses during hip simulations has produced clinically relevant wear rates, wear patterns and wear particles. This provided an opportunity to determine the response of primary human peripheral blood mononuclear cells to clinicall...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/s0142-9612(02)00510-0
更新日期:2003-03-01 00:00:00
abstract::A biocompatible hydrogel of poly[N-(2-hydroxypropyl)methacrylamide] (PHPMA) which includes the cell-adhesive region of fibronectin Arg-Gly-Asp was synthesized and its structure, rheological and dielectric properties were characterized. The ability of a PHPMA-RGD hydrogel to promote tissue regeneration and support axon...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/s0142-9612(00)00354-9
更新日期:2001-05-01 00:00:00
abstract::To study the effect of ionizable functional groups on the adhesion of leucocytes to surfaces, both poly(ethyleneimine) and poly(acrylic acid) were immobilized on polyurethane films, resulting in the introduction of amine and carboxylic acid groups, respectively. This was confirmed by contact angle measurements and XPS...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/0142-9612(92)90114-4
更新日期:1992-01-01 00:00:00
abstract::Fracture healing and fracture fixation in the context of osteoporosis is extremely difficult. To inhibit osteoclast-induced bone resorption and associated implant loosening in this pathology, we describe a local delivery strategy to delivery RNA interfering technology to bone sites to target and down-regulate osteocla...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2012.07.039
更新日期:2012-11-01 00:00:00
abstract::The search for a cell-supporting scaffold with controlled topography and surface chemistry is a constant topic within tissue engineering. Here we have employed M13 phages, which are genetically modifiable biological nanofibers (∼ 880 nm long and ∼ 6.6 nm wide) non-toxic to human beings, to form films for supporting th...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2011.03.030
更新日期:2011-07-01 00:00:00
abstract::To fully understand biological behavior in vitro often dictates that oxygen be reported at either a local or a cellular level. Oxygen sensors based on the luminescent quenching of a specific form of electrospun fiber were developed for measurement of both gaseous and dissolved oxygen concentrations. Electrospinning wa...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2015.10.055
更新日期:2016-01-01 00:00:00
abstract::Thrombomodulin (TM) is a newly described endothelial cell-associated protein that functions as a potent natural anticoagulant by converting thrombin from a procoagulant protease to an anticoagulant. In this study, focussing on the application of TM for biomedical materials, recombinant human TM (hTM) was immobilized o...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/0142-9612(94)90041-8
更新日期:1994-08-01 00:00:00
abstract::Primary rat bone marrow cells were cultured for periods of 8 d on hydroxyapatite discs produced by sintering compressed powder at 1130 degrees C. The disc surfaces were roughened using silicon carbide paper to create three groups of samples (n = 10) of differing surface topography. The culture conditions permitted bot...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/0142-9612(93)90216-o
更新日期:1993-01-01 00:00:00
abstract::Lacking a blood supply and having a low cellular density, articular cartilage has a minimal ability for self-repair. Therefore, wide-ranging cartilage damage rarely resolves spontaneously. Cartilage damage is typically treated by chondrocyte transplantation, mosaicplasty or microfracture. Recent advances in tissue eng...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2012.01.056
更新日期:2012-05-01 00:00:00
abstract::The surface of polyetheretherketone (PEEK) was coated with a pure titanium (Ti) layer using an electron beam (e-beam) deposition method in order to enhance its biocompatibility and adhesion to bone tissue. The e-beam deposition method was a low-temperature coating process that formed a dense, uniform and well crystall...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2009.12.030
更新日期:2010-05-01 00:00:00
abstract::The protective role of different dentine fractions and of dentine slices in moderating the cytotoxicity of zinc oxide eugenol (ZOE) was investigated. The collagen fraction of dentine powder provided increased protection over intact powder. Slices of dentine offered greater protection probably by providing a physical b...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/0142-9612(86)90035-9
更新日期:1986-11-01 00:00:00
abstract::Microcontact printing (mCP) is employed to generate discontinuous microscale gradients of active fractalkine, a chemokine expressed by endothelial cells near sites of inflammation where it is believed to form concentration gradients descending away from the inflamed area. In vivo, fractalkine is a transmembrane molecu...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2009.06.018
更新日期:2009-10-01 00:00:00
abstract::The ligand-tethered poly(ethylene oxide-propylene oxide-ethylene oxide) (PEO-PPO-PEO) triblock copolymer was explored to engineer poly(DL-lactic acid) (PDL-LA) material to promote cell attachment and growth. The PEO-PPO-PEO was activated by methyl sulfonyl chloride and the amino acid, and peptide were attached. By ble...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2003.08.031
更新日期:2004-05-01 00:00:00
abstract::Current advances in skin tissue engineering and wound healing augur well for the development of split or full thickness skin substitutes to recapitulating the native functional skin. These engineered skin substitutes have fared successfully in recent years with exploration of various emerging technologies. As a result...
journal_title:Biomaterials
pub_type: 杂志文章,评审
doi:10.1016/j.biomaterials.2019.119267
更新日期:2019-09-01 00:00:00
abstract::There is a great clinical need for tissue engineered blood vessels that could be used to replace or bypass damaged arteries. The success of such grafts will depend strongly on their ability to mimic the cellular and matrix organization found in native arteries, but currently available cell scaffolds such as electrospu...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2012.04.040
更新日期:2012-08-01 00:00:00
abstract::Ultrasoft biomaterials-polymers, gels, and human soft tissues with an elastic modulus less than ∼100 kPa-are increasingly used in medical devices. While bacterial interactions (adhesion and biofilm formation) have been extensively studied on stiffer materials, little is known about how bacteria colonize ultrasoft mate...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2016.04.005
更新日期:2016-07-01 00:00:00
abstract::This study is concerned with the effect of dual implantation of calcium and phosphorus upon the structure, corrosion resistance and biocompatibility of titanium. The ions were implanted in sequence, first Ca and then P, both at a dose of 10(17) ions/cm2 at a beam energy of 25 keV. Transmission electron microscopy was ...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2004.08.015
更新日期:2005-06-01 00:00:00
abstract::Carbon fiber implants were used to fill osteochondral defects created on the articular surface of the patella of 36 rabbits, for the purpose of studying the long-term histological changes of the repair process. Six months after surgery the defect was filled by fibrous tissue, where the superficial area was organized p...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/s0142-9612(00)00144-7
更新日期:2000-11-01 00:00:00
abstract::Biomaterials can potentially influence stem and progenitor cell proliferation and differentiation in both a positive and a negative way. Herein, we report on the expansion and differentiation of rat embryonic (E17) liver (RLC-18) cells on new bioactive membrane made of PEEK-WC-PU, whose surface was grafted with nitrog...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2009.08.024
更新日期:2009-11-01 00:00:00
abstract::Here we document the complete process of bioresorption and bone replacement of rods made of forged composites of unsintered hydroxyapatite particles/poly l-lactide (F-u-HA/PLLA) implanted in the femoral medullary cavities of rabbits. Bioresorption, osteoconductive bioactivity and bone replacement were compared in thre...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2005.02.016
更新日期:2005-09-01 00:00:00
abstract::Three critical aspects of searching for and understanding how to find highly resistant surfaces to protein adhesion are addressed here with specific application to synthetic membrane filtration. They include the (i) discovery of a series of previously unreported monomers from a large library of monomers with high prot...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2011.11.001
更新日期:2012-02-01 00:00:00
abstract::A facile and efficient method to immobilize bioactive proteins onto polymeric substrate was established. Testis-specific protease 50 (TSP50) was immobilized on ultrafine biodegradable polymer fibers, i.e., (1) to prepare a propargyl-containing polymer P(LA90-co-MPC10) by introducing propargyl group into a cyclic carbo...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2007.11.008
更新日期:2008-03-01 00:00:00
abstract::Three-dimensional gelatin-chondroitin 6 sulphate-hyanuronic acid (gelatin-C6S-HA) biomatrices were used as the scaffold to investigate the phenotypic and molecular expression of basement membrane (BM) and extracellular matrix (ECM) proteins in vitro. The cells were cultured in three different culture conditions: kerat...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2006.05.004
更新日期:2006-10-01 00:00:00
abstract::Small-diameter vascular grafts made of biomedical polytetrafluoroethylene (PTFE) suffer from the poor long-term patency rate originating from thrombosis and intimal hyperplasia, which can be ascribed to the insufficient endothelialization and chronic inflammation of the materials. Hence, bio-functionalization of PTFE ...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/j.biomaterials.2017.06.023
更新日期:2017-09-01 00:00:00
abstract::Peel bond strength and tensile bond strength between three polyvinylsiloxane denture soft liners and a heat-cured acrylic resin denture base were measured using two adhesive systems. The soft lining materials differed only in regard of their filler content and compliance. The values of bond strength and mode of failur...
journal_title:Biomaterials
pub_type: 杂志文章
doi:10.1016/s0142-9612(01)00253-8
更新日期:2002-03-01 00:00:00