Abstract:
:The aim of this study was to investigate the diffusion of red-stained experimental GM primer and blue-stained dentin bonding agent into EDTA-conditioned dentin and the effect of GM priming on contraction gap formation. After GM priming at 0, 35, 70, or 100 vol%, marginal adaptation was evaluated by measuring the wall-to-wall contraction gap width of a light-activated resin composite (Palfique Estelite, Tokuyama Dental, Japan) mediated with a commercial dentin bonding agent (Clearfil Photo Bond, Kuraray Medical, Japan). Contraction gap formation was completely prevented when treated with 35 vol% GM primer. Moreover, after treatment with 35 vol% GM, the red and blue dyes of stained GM primer and dentin bonding agent diffused up to a depth of 40 µm into the dentin surface. The diffusion of primer and bonding agent into EDTA-conditioned dentin was essential for bonding efficacy although SEM observation revealed an absence of hybrid layer formation.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Nasu Y,Itoh K,Tani C,Hisamitsu Hdoi
10.4012/dmj.2009-084subject
Has Abstractpub_date
2010-10-01 00:00:00pages
609-14issue
5eissn
0287-4547issn
1881-1361pii
JST.JSTAGE/dmj/2009-084journal_volume
29pub_type
杂志文章abstract::The purpose of this study was to devise and propose appropriate conditions for the photographing of thermal images in the oral cavity and to evaluate which thermography techniques can be applied to dentistry by evaluating the differences in temperature among oral tissues. Thermal images of oral cavities of 20 voluntee...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.22.436
更新日期:2003-12-01 00:00:00
abstract::In this study, wedge-shaped CP titanium castings and Ti-6Al-7Nb alloy castings were produced by three types of investment. The effects of the castings' thickness on surface reaction layer were investigated by measuring Vickers hardness, observing the microstructure, and analyzing the oxygen concentration. It was found...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.387
更新日期:2004-09-01 00:00:00
abstract::The effects of desensitizer, disinfectant, saliva, blood, and hydrogen peroxide on the tensile bond strength between adhesive and ceramic as well as between adhesive and dentin were examined. Sixty 7x3 mm pressed ceramic discs of IPS e.max were fabricated and randomly assigned to six groups of different dentin surface...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-074
更新日期:2010-08-01 00:00:00
abstract::The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-023
更新日期:2011-01-01 00:00:00
abstract::Finite element analysis was performed to evaluate stress distribution in maxillary central incisors treated endodontically and restored with a post and an all-ceramic crown. Tensile stress at tooth root was analyzed using two-dimensional finite element models with different post diameters and lengths. One post length ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.145
更新日期:2006-03-01 00:00:00
abstract::This study sought to evaluate the effects of different staining solutions on the colour stability of nanocomposites compared with microhybrid resin and to evaluate the degree of conversion of these two materials. Two different shades of two different composites were cured in polytetraflouroethylene disk rings. Coffee,...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-267
更新日期:2013-01-01 00:00:00
abstract::The purpose of this study was to investigate the effect of modifying aluminum oxide slips with magnesium oxide (MgO) to create a jointing material for In-Ceram Alumina. Jointed In-Ceram Alumina bars with In-Ceram Alumina slips containing 0-1.0 mass% MgO were examined by a three-point bending test. Joint-free bars were...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.251
更新日期:2008-03-01 00:00:00
abstract::The aim of this study was to examine the lifespan or number of cycles to failure of tapered rotary nickel-titanium (Ni-Ti) endodontic instruments. Simulated root canals with different curvatures were used to determine a relation between canal curvature and instrument lifespan. Using a novel mathematical model for the ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-254
更新日期:2012-01-01 00:00:00
abstract::The objective of this study was to clarify the effect of surface topography on osteoblast-like cell behavior on yttria stabilized tetragonal zirconia polycrystals (TZP). Mirror-polished; blasted with 50- or 150-µm alumina (SB50 and SB150); and SB150 acid-etched with hydrofluoric acid (SB150E) were prepared on TZP. Ini...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-208
更新日期:2013-01-01 00:00:00
abstract::This study tested whether exhaled humid conditions would affect the adhesion of etch-and-rinse, two-step and one-step self-etch adhesive resins to enamel. Enamel surfaces of human maxillary anterior teeth (N=240, n=20) were exposed to four humid conditions (H1: 63-68%, H2: 73-78%, H3: 93-98%, H4: 36-45% RH) during bon...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-200
更新日期:2013-01-01 00:00:00
abstract::Quaternary ammonium compounds (QACs) have been used widely in medicine, owing to their antimicrobial properties. They also have strong permeability, stable performance, low skin irritation, low toxicity, low corrosion, lasting biological effects and so on, comparing with other antimicrobial agents. At the end of last ...
journal_title:Dental materials journal
pub_type: 杂志文章,评审
doi:10.4012/dmj.2017-096
更新日期:2018-03-30 00:00:00
abstract::The aim was to investigate the effect of simulated low-temperature degradation (s-LTD) and hydrothermal fatigue on the degradation of three ZrO(2)-based dental materials. Lava, IPS, and NanoZr discs were randomly assigned to (1) Control-Storage in distilled water at 37°C; (2) Aging at 134°C for 5 h (s-LTD); (3) Thermo...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-216
更新日期:2012-01-01 00:00:00
abstract::This study evaluated the effect of adding silane coupling agent on initial and long-term bond strengths of one-step self-etch adhesives to enamel-dentin-composite in combined situation. Cervical cavities were prepared on extracted molars and filled with Clearfil AP-X. After water-storage for one-week, the filled teeth...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-050
更新日期:2015-01-01 00:00:00
abstract::We investigated the adsorption of lipoteichoic acid (LTA) on titanium surfaces by using the quartz crystal microbalance (QCM) method, and confirmed the influence of mucin (MUC) pre-adsorption on LTA adsorption. Two injection methods were evaluated. Namely, Method A: single-step injection of LTA solution to the Ti sens...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-209
更新日期:2020-12-03 00:00:00
abstract::This study aimed to evaluate the effect of an acidic-adjusted pH of solvent in silanization on the amount of fluoride released and mechanical properties of heat-cured acrylic resin containing a silanized fluoride-releasing filler. The experimental groups were divided into 4 groups; non-silanized, acidic-adjusted pH, n...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2015-403
更新日期:2016-01-01 00:00:00
abstract::The objective of this study was to examine the effects of storage conditions on the flexural strengths of resin composite materials for CAD/CAM restorations. Seven commercially available resin composite CAD/CAM blanks were examined. Rectangular specimens (4.0×1.2×4.0 mm) of each material were trimmed from the blanks a...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-202
更新日期:2020-09-29 00:00:00
abstract::This study investigated the durability, especially the nonwaterdegradable qualities, of experimental light-cured composite resin containing barium-borosilicate glass filler. For this purpose, Bis-GMA, a typical component of base monomer in conventional composite resin, was replaced by Bis-GMA-F which is water-repellen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.12.1
更新日期:1993-06-01 00:00:00
abstract::This study determined the discoloration of five CAD/CAM resins, four manually polymerized resins, and glass-ceramic as control group. Specimens were divided into three groups (N=300, n=30) to be stored in coffee, black tea and red wine (n=10). The discoloration was measured using a spectrophotometer after 1, 7, 29, 90...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-238
更新日期:2012-01-01 00:00:00
abstract::The bactericidal efficacy of 1.00-4.50% glycine-type amphoteric surfactant (Gly) was evaluated by measuring its microorganism removal rate in denture plaque. Physical and mechanical properties such as surface roughness, color difference, and bending strength of two different denture base resins were determined before ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.307
更新日期:2009-05-01 00:00:00
abstract::This study investigated the effect of a coating material containing S-PRG fillers on the demineralization of bovine enamel and dentin, by measuring changes in the transmitted ultrasonic velocity. Bovine enamel and dentin specimens with and without coating (n=6 for each condition) were cut into blocks, immersed in 0.1 ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-153
更新日期:2012-01-01 00:00:00
abstract::This study evaluated a new enzyme solution (SFC-V) for dentin caries removal, and obtained results were compared with Carisolv. Both solutions were used with a prototype plastic instrument - this being a modified technique for Carisolv. Five carious deciduous teeth were sectioned, and both treatments were applied alte...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.675
更新日期:2006-12-01 00:00:00
abstract::The aim of this study was to investigate the effect of three metal priming agents on the bond strength of adhesive resin cement to Silver-Zinc-Tin-Indium (Ag-Zn-Sn-In) alloy and pure Ag, Zn, Sn, and In. The specimens were air-abraded with alumina and then primed with one of three metal priming agents: V-Primer, Esteni...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-139
更新日期:2018-03-30 00:00:00
abstract::The influence of a thin carbonate-containing hydroxyapatite (CA) coating to tetragonal zirconia polycrystal (TZP) on osteoblastlike cell response was investigated. TZP disks were subjected to blasting and acid etching. Thin CA coatings were deposited by the molecular precursor method (TZP-CA). Initial cell adhesion of...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2013-122
更新日期:2014-01-01 00:00:00
abstract::The purpose of this study was to analyze the ultrastructures and chemical compositions of precipitates formed on mineral trioxide aggregate (MTA; White ProRoot MTA) immersed in distilled water (DW) or phosphate buffered saline (PBS), based on the attribution that MTA's bioactivity and sealing ability are influenced by...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-133
更新日期:2010-10-01 00:00:00
abstract::The depths of cure and the distributions of degree of conversion (DC), polymerization conversion (PC) and percent pendant double bonds (PDB) of light-cured composite resins cured under various intensities of light were investigated. When the total amount of exposure, represented by the product of the light intensity a...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.13.198
更新日期:1994-12-01 00:00:00
abstract::The aim of the present study was to measure various mechanical properties of acrylic denture base resins, including flexural modulus, flexural strength, fracture toughness, Barcol and Vickers hardness and their related properties, and to investigate correlations between different mechanical properties. Resin specimens...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-205
更新日期:2012-02-03 00:00:00
abstract::Bioactive-glass (B-G) is a material known for its favorable biological response when in contact with surrounding fibro-osseous tissues, due not only to an osteoconductive property, but also to an osteostimulatory capacity, and superior biocompatibility for use in human body. The objectives of this paper are to review ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-233
更新日期:2015-01-01 00:00:00
abstract::This study investigated the contrast ratio and grain size depending on sintering parameters of twelve different zirconia materials and compared with glass-ceramic (N=156, n=12 per group). Contrast ratio of all ceramics was measured using a spectrophotometer according to ISO 2471: 2008. Grain sizes of zirconia were det...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2014-056
更新日期:2014-01-01 00:00:00
abstract::The purpose of this study was to investigate the effect of remaining dentin thickness (RDT) and long term water storage on dentin bond strength in-vitro. Twenty-seven third molars were randomly divided into 3 groups: Clearfil Bond SE ONE (SE1, Kuraray Noritake Dental, Okayama, Japan), G-Bond plus (GB, GC, Tokyo, Japan...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-140
更新日期:2018-07-29 00:00:00
abstract::The purpose of this study was to investigate the retention force of complete palate coverage and palate-less dentures made with three polymerization systems (DS system, SR-Ivocap system, microwave polymerization system) in vitro. The retention force between each denture and a polyurethane model by intervening artifici...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.19
更新日期:2004-03-01 00:00:00