Abstract:
STATEMENT OF PROBLEM:The surface hardness and roughness of different glaze materials for denture base acrylic resins have not been well reported. PURPOSE:The purpose of the study was to measure the surfaces hardness, elastic modulus and surface roughness of 5 different light-polymerized glaze materials for poly methyl methacrylate (PMMA) denture base materials. MATERIAL AND METHODS:A total of 210 PMMA resin specimens (10 × 5 × 2 mm) were prepared (30 per group); control group was untreated, group 1 was surface treated with conventional pumice and high shine paste; group 2 to 6 specimens were glaze coated with different commercially available denture glaze materials. 20 specimens out of 30 underwent thermocycling to simulate 6 months and 12 months in vivo. Nanoindentation was performed to measure the surface hardness and elastic modulus. Surface roughness was quantitatively analysed using surface metrology software and qualitatively analysed under scanning electron microscope (SEM). Collected data was statistically analysed using SPSS version 24. RESULTS:The mean surface hardness of tested specimens ranged from 0.33 ±0.09 GPa to 0.68 ±0.10 GPa. Specimens coated with Optiglaze produced statistically higher surface hardness compared to other groups (P< 0.01). Aging of 6 months and 12 months was found to have no statistical significance for all groups' surface hardness values. For elastic modulus, specimens coated with Nanovarnish produced statistically higher values compared to other groups (P= 0.03). Thermocycling showed no influence on the elastic modulus of specimens. The mean surface roughness of all groups ranged from 0.16 ±0.01 to 0.30 ±0.02 μm with no statistical significance between groups (P= 0.67). However, under SEM analysis, surfaces showed increased roughness over time. CONCLUSIONS:Statistically significant differences in surface hardness and elastic modulus were found among the different types of surface coated denture acrylic resins. Silica-nanoparticle containing surface coatings produced the highest surface hardness and elastic modulus, however there was no statistical significance found in aging for 6 and 12 months. Contrary to expectations, the surface roughness did not have a significant increase in all groups over time, despite changes observed under SEM. CLINICAL IMPLICATIONS:This study will contribute to our understanding of surface glazed PMMA acrylic resin denture materials and how it improves the surface strength. This research can help dental clinicians and technicians select the most effective polishing and coating material for the dentures.
journal_name
J Mech Behav Biomed Materauthors
Choi JJE,Uy CE,Ramani RS,Waddell JNdoi
10.1016/j.jmbbm.2019.103601subject
Has Abstractpub_date
2020-03-01 00:00:00pages
103601eissn
1751-6161issn
1878-0180pii
S1751-6161(19)31583-8journal_volume
103pub_type
杂志文章abstract::Calcium sulfate hemihydrate (CSH) was introduced into the mineralized collagen (nHAC) to prepare an injectable and self-setting in situ bone graft substitute. The mechanical properties of materials, which are dependant on the L/S ratio, the content of nHAC and setting accelerator, were discussed based on the satisfyin...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2011.12.007
更新日期:2012-08-01 00:00:00
abstract::Dental adhesive provides effective retention of filling materials via adhesive-dentin hybridization. The use of co-monomers, such as 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP), is thought to be crucial for hybridization owing to their ionic-binding to calcium and co-polymerization in the polymerizable adhe...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2018.12.038
更新日期:2019-04-01 00:00:00
abstract::Infusion of vitamin E (α-tocopherol) in highly crosslinked ultra-high molecular weight polyethylene (UHMWPE) liners has been conceived to achieve superior oxidation stability while preserving enhanced mechanical properties as compared to post-irradiation remelted liners. However, the presence of an antioxidant in the ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2012.12.009
更新日期:2014-03-01 00:00:00
abstract::Telescopic crowns are used as support for removable dental prostheses' construction. A distinctive feature of crowns often used in their description and comparison is retention, which is understood as resistance when removing the prosthesis or a force needed to disconnect crowns. The article describes a method for the...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.01.042
更新日期:2017-05-01 00:00:00
abstract::Tissue engineering is a field which aims to regenerate damaged tissues by enhancing tissue growth through the porous architecture of the scaffolds which is desired to mimic the human cancellous bone. Mg-based scaffolds are gaining importance in the field of tissue engineering owing to its potential application as a bi...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2019.02.010
更新日期:2019-06-01 00:00:00
abstract::Alterations in mechanical loading can induce growth and remodeling in soft connective tissues. Numerous studies have measured changes in the collagen structure and mechanical properties of cellularized native and engineered tissues in response to cyclic mechanical loading. However, a recent experimental study demonstr...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2018.03.027
更新日期:2018-06-01 00:00:00
abstract::Dentin restoration produces weak interfaces because of the effects of bacterial microflora, biofilms, and mechanical, thermal, and shrinkage stresses. This results in secondary caries. Therefore, hydrophobic elastic polyurethane (PU) containing different concentrations of triclosan derivatives was synthesized and appl...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2019.103471
更新日期:2020-02-01 00:00:00
abstract::Recent developments showed that β-type Ti-Nb alloys are good candidates for hard tissue replacement and repair. However, their elastic moduli are still to be further reduced to match Young׳s modulus values of human bone, in order to avoid stress shielding. In the present study, the effect of indium (In) additions on t...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2014.07.010
更新日期:2014-11-01 00:00:00
abstract::Mechanical property data for brain tissue are needed to understand the biomechanics of neurological disorders and response of the brain to different mechanical and surgical forces. Most studies have characterized mechanical behavior of brain tissues over large regions or classified tissue properties for either gray or...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.08.026
更新日期:2014-01-01 00:00:00
abstract::The biomechanical behavior of human corneal stroma under uniaxial tension was investigated by the experimental analysis of cornea stromal lenticules taken out by corneal refractive surgery. Uniaxial tests were conducted to determine their stress-strain relationship and tensile strength. The Gasser-Ogden-Holzapfel (GOH...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2018.05.042
更新日期:2018-09-01 00:00:00
abstract::In the study, CoCrWCu alloys with differing Cu content (2, 3, 4 wt%) were prepared by selective laser melting using mixture powders consisting of CoCrW and Cu, aiming at investigating the effect of Cu on the microstructures, mechanical properties, corrosion behavior and cytotoxicity. The SEM observations indicated tha...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2018.02.026
更新日期:2018-05-01 00:00:00
abstract::In this study, Polylactic acid (PLA)/phosphate glass fibres (PGF) composites were prepared by compression moulding. Fibres produced from phosphate based glasses P2O5-CaO-MgO-Na2O (P45B0), P2O5-CaO-MgO-Na2O-B2O3 (P45B5), P2O5-CaO-MgO-Na2O-Fe2O3 (P45Fe3) and P2O5-CaO-MgO-Na2O-B2O3-Fe2O3 (P45B5Fe3) were used to reinforce...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2015.12.011
更新日期:2016-06-01 00:00:00
abstract:OBJECTIVE:To introduce an experimental non-carious cervical lesion (NCCL) model for studying the influence of presence and type of stress (tension or compression) on acid effects involved in NCCL formation on the enamel near the cement-enamel junction (CEJ). METHODS:108 bovine incisors were cut into 18 × 3×3 mm3 beams...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2016.11.003
更新日期:2017-02-01 00:00:00
abstract::Clinical meshes used in pelvic organ prolapse (POP) repair are predominantly manufactured from monofilament polypropylene (PP). Complications from the use of these meshes in transvaginal kits, including mesh exposure and pain, have prompted two public health notifications by the FDA. The aim of this study was to compa...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.04.002
更新日期:2013-07-01 00:00:00
abstract::Hydroxyapatite (HAP) is a natural bioceramic which is currently used in scaffolds and coatings for the regrowth of osseous tissue but offers poor load-bearing capacity compared to other biomaterials. The deformation mechanisms responsible for the mechanical behavior of HAP are not well understood, although the advent ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103894
更新日期:2020-10-01 00:00:00
abstract:OBJECTIVES:To compare the effects of four surface coating methods on resin to zirconia shear bond strength. MATERIAL AND METHODS:Eighty pre-sintered zirconia discs were prepared and randomly divided into five study groups according to the corresponding methods of surface treatments as follows: group C (control group, ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.12.011
更新日期:2014-04-01 00:00:00
abstract::A mixture of water/carbon dioxide is a "green" perspective solvent from the viewpoint of biomedical applications. Clathrate hydrates are formed this solvent under certain conditions and a very interesting question is the impact of clathrates hydrates on the structure and properties of bovine pericardium, which is used...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2016.11.015
更新日期:2017-03-01 00:00:00
abstract::Severe degeneration of the intervertebral disc has an immensely debilitating effect on quality of life that has become a serious health and economic burden throughout the world. The disc plays an integral role in biomechanical movement and support within the spine. The emergence of tissue engineering endeavours to res...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2016.10.015
更新日期:2017-01-01 00:00:00
abstract::The purpose of this study was to investigate how water aging of the resin cement influences the stress distribution in all-ceramic crowns and if there is an increase in the propensity for crown failure. The failure of all-ceramic crowns attributed to cement degradation was explored using a combination of experimental ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2012.08.003
更新日期:2013-01-01 00:00:00
abstract::As a supplement to our investigation into R-curves in a short-fiber reinforced dental resin composite, we investigate the effects of 2-months water storage. Water is known to degrade the siloxane bonds linking matrix and fillers, which has been suggested to decrease the fracture toughness in conventional resin composi...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103674
更新日期:2020-04-01 00:00:00
abstract::Success of tissue engineering relies on the architecture and properties of porous scaffolds. Electrospun nonwoven scaffolds in the form of mats are unique materials due to large surface area to volume ratio, high porosity, versatility in surface functionalities and excellent mechanical properties. Maneuvering the mech...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.04.013
更新日期:2017-08-01 00:00:00
abstract::In the present study, inflation tests with free axial extension of 15 human vena saphena magna were conducted ex vivo to obtain data suitable for multi-axial constitutive modeling at overloading conditions (pressures up to approximately 15kPa). Subsequently the data were fitted with a hyperelastic, nonlinear and aniso...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2015.01.023
更新日期:2015-05-01 00:00:00
abstract::Bite forces are studied in order to understand a wide range of factors pertaining to the mastication system. Various strain gauge transducers have been employed to measure bite forces, with several descriptions of these available in the literature; unfortunately, many reports provide insufficient detail to enable accu...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103846
更新日期:2020-09-01 00:00:00
abstract:AIM:For the proper function of small diameter vascular grafts their mechanical properties are essential. A variety of testing methods and protocols exists to measure tensile strength, compliance and viscoelastic material behavior. In this study the impact of the measurement protocol in hoop tensile tests on the measure...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103652
更新日期:2020-04-01 00:00:00
abstract::A severe shortage of good quality donor cornea is now an international crisis in public health. Alternatives for donor tissue need to be urgently developed to meet the increasing demand for corneal transplantation. Hydrogels have been widely used as scaffolds for corneal tissue regeneration due to their large water co...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.03.001
更新日期:2013-05-01 00:00:00
abstract::Orthopedic interfaces such as the tendon-bone junction (TBJ) present unique challenges for biomaterials development. Here we describe a multi-compartment collagen-GAG scaffold fabricated via lyophilization that contains discrete mineralized (CGCaP) and non-mineralized (CG) regions joined by a continuous interface. Mod...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.07.016
更新日期:2013-12-01 00:00:00
abstract::A limitation in the use of hydrophilic polymers as implantable devices is their inherently poor mechanical strength. Using interpenetrating polymer networks (IPNs) consisting of both hydrophilic and hydrophobic networks is an effective method of strengthening these polymers. In this work, a series of poly(dimethyl sil...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2009.01.002
更新日期:2009-10-01 00:00:00
abstract::Muscle fiber direction strain provides invaluable information for characterizing muscle function. However, methods to study this for human muscles in vivo are lacking. Using magnetic resonance (MR) imaging based deformation analyses and diffusion tensor (DT) imaging based tractography combined, we aimed to assess musc...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2016.06.031
更新日期:2016-10-01 00:00:00
abstract::Cortical bone provides the main form of support in humans and other vertebrates against various forces. Thus, capturing its mechanical properties is important. In this study, the mechanical properties of cortical bone were investigated by using automated ball indentation and graphics processing at both the macroscopic...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.11.039
更新日期:2018-02-01 00:00:00
abstract::A laser based surface nitriding process was adopted to further enhance the osseo-integration, corrosion resistance, and tribological properties of the commonly used bioimplant alloy, Ti-6Al-4V. Earlier preliminary osteoblast, electrochemical, and corrosive wear studies of laser nitrided titanium in simulated body flui...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2014.05.017
更新日期:2014-09-01 00:00:00