Abstract:
:We here present the first successful report on combining nanostructured silk and poly(ε-caprolactone) (PCL) with a ceramic scaffold to produce a composite scaffold that is highly porous (porosity ∼85%, pore size ∼500 μm, ∼100% interconnectivity), strong and non-brittle with a surface that resembles extracellular matrix (ECM). The ECM-like surface was developed by self-assembly of nanofibrous structured silk (20-80 nm diameter, similar to native collagen found in ECM) over a thin PCL layer which is coated on biphasic calcium phosphate (BCP) scaffolds. The effects of different concentrations of silk solution on the mechanical and physical properties of the scaffolds were also comprehensively examined. Our results showed that using silk only (irrespective of concentration) for the modification of ceramic scaffolds could drastically reduce the compressive strength of the modified scaffolds in aqueous media, and the modification made a limited contribution to improving scaffold toughness. Using PCL/nanostructured silk the compressive strength and modulus of the modified scaffolds reached 0.42 MPa (compared with 0.07 MPa for BCP) and ∼25 MPa (compared with 5 MPa for BCP), respectively. The failure strain of the modified scaffold increased more than 6% compared with a BCP scaffold (failure strain of less than 1%), indicating a transformation from brittle to elastic behavior. The cytocompatibility of ECM-like composite scaffolds was investigated by studying the attachment, morphology, proliferation and bone-related gene expression of primary human bone-derived cells. Cells cultured on the developed scaffolds for 7 days had significant up-regulation of cell proliferation (∼1.6-fold higher, P<0.001) and osteogenic gene expression levels (collagen type I, osteocalcin and bone sialoprotein) compared with the other groups tested.
journal_name
Acta Biomaterjournal_title
Acta biomaterialiaauthors
Roohani-Esfahani SI,Lu ZF,Li JJ,Ellis-Behnke R,Kaplan DL,Zreiqat Hdoi
10.1016/j.actbio.2011.10.009subject
Has Abstractpub_date
2012-01-01 00:00:00pages
302-12issue
1eissn
1742-7061issn
1878-7568pii
S1742-7061(11)00440-5journal_volume
8pub_type
杂志文章abstract::Cardiac fibrosis, an important pathological feature of structural remodeling, contributes to ventricular stiffness, diastolic dysfunction, arrhythmia and may even lead to sudden death. Matrix stiffness, one of the many mechanical factors acting on cells, is increasingly appreciated as an important mediator of myocardi...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2014.01.031
更新日期:2014-06-01 00:00:00
abstract::Antibiotic resistance is a major challenge to the treatment of bacterial infections associated with medical devices and biomaterials. One important intrinsic mechanism of such resistance is the formation of persister cells that are phenotypic variants of microorganisms and highly tolerant to antibiotics. Recently, we ...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2016.12.053
更新日期:2017-03-01 00:00:00
abstract::To date, there has been little investigation of biodegradable tissue engineered arterial grafts (TEAG) using clinically relevant large animal models. The purpose of this study is to explore how pore size of electrospun scaffolds can be used to balance neoarterial tissue formation with graft structural integrity under ...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2020.08.011
更新日期:2020-10-01 00:00:00
abstract::Inhibition of bacterial growth with the simultaneous promotion of angiogenesis has been challenging in the repair and regeneration of infected tissues. Here, we aim to tackle this issue through the use of cobalt-doped silicate microspheres that can sustainably release dual ions (silicate and cobalt) at therapeutically...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2018.11.025
更新日期:2019-01-01 00:00:00
abstract::Antibiotic resistance of bacterial biofilms limits available treatment methods for implant-associated orthopaedic infections. This study evaluated the effects of applying cathodic voltage-controlled electrical stimulations (CVCES) of -1.5V and -1.8V (vs. Ag/AgCl) to coupons of commercially pure titanium (cpTi) incubat...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2016.11.056
更新日期:2017-01-15 00:00:00
abstract::Dentin contains 1-2μm diameter tubules extending from the pulp cavity to near the junction with enamel. Peritubular dentin (PTD) borders the tubule lumens and is surrounded by intertubular dentin (ITD). Differences in PTD and ITD composition and microstructure remain poorly understood. Here, a (∼200nm)(2), 10.1keV syn...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2014.05.027
更新日期:2014-09-01 00:00:00
abstract::Novel porous bilayered scaffolds, fully integrating a silk fibroin (SF) layer and a silk-nano calcium phosphate (silk-nanoCaP) layer for osteochondral defect (OCD) regeneration, were developed. Homogeneous porosity distribution was achieved in the scaffolds, with calcium phosphate phase only retained in the silk-nanoC...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2014.10.021
更新日期:2015-01-01 00:00:00
abstract::Modification of a biomedical-grade stainless steel 316LS surface by electrochemical cyclic potentiodynamic passivation (CPP) and the response of fibrinogen (Fg), platelets, endothelial cells (ECs) and smooth muscles cells (SMCs) to this surface was investigated. Polarization modulation infrared reflection absorption s...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2009.07.007
更新日期:2010-02-01 00:00:00
abstract::The surface of an implant device can be modified by immobilizing biological molecules on it to improve its integration into the host tissue. We have previously demonstrated that enzymatically tailored plant pectins are promising nanocoatings for biomaterials. This study investigates whether a coating of modified hairy...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2009.03.031
更新日期:2009-09-01 00:00:00
abstract::The effects of a biphasic mineralized collagen scaffold (BCS) containing intrafibrillar silica and apatite on osteogenesis of mouse mesenchymal stem cells (mMSCs) and inhibition of receptor activator of nuclear factor κB ligand (RANKL)-mediated osteoclastogenesis were investigated in the present study. mMSCs were cult...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2015.03.012
更新日期:2015-06-01 00:00:00
abstract::End-functional 2-methacryloyloxyethyl phosphorylcholine (MPC) co-polymers containing two different monomer units, 2-hydroxyethyl methacrylate (HEMA) and n-butyl methacrylate (BMA), with varying hydrophilicities were synthesized to investigate the effect of the conjugated hydrophilic polymer on the heat-induced conform...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2010.11.027
更新日期:2011-04-01 00:00:00
abstract::Wound infections are a significant clinical problem affecting millions of people worldwide. Topically applied antibacterial formulations with longer residence time and controlled antimicrobial release would offer significant benefits for improved prevention and treatment of infected wounds. In this study, we developed...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2019.12.014
更新日期:2020-02-01 00:00:00
abstract:UNLABELLED:Rapid vascularization of bone graft substitutes upon implantation is one of the most important challenges to overcome in order to achieve successful regeneration of large, critical-size bone defects. One strategy for stimulating vascularization during the regeneration process is to create a hypoxic microenvi...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2016.03.031
更新日期:2016-05-01 00:00:00
abstract::Cell-instructive hydrogels are attractive for skin repair and regeneration, serving as interactive matrices to promote cell adhesion, cell-driven remodeling and de novo deposition of extracellular matrix components. This paper describes the synthesis and photocrosslinking of cell-instructive pectin hydrogels using cel...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2017.11.016
更新日期:2018-01-15 00:00:00
abstract::The degradation of zirconia-based ceramic components for total hip arthroplasty (head and cup) has been the topic of many works. However, the correlation between what is measured in vivo and what is expected from in vitro simulations on hip simulators may be sometimes feeble, especially where zirconia component are co...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2013.03.030
更新日期:2013-07-01 00:00:00
abstract::A novel application of thermally induced phase separation (TIPS) is described enabling the rapid formation of monodisperse porous microspheres. By taking advantage of TIPS processing parameters, the porosity, the pore morphology (bimodal/channel-like/radial towards the centre) and the presence of an open-pore or dense...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2007.09.011
更新日期:2008-03-01 00:00:00
abstract::In this study the friction, wear and surface mechanical behavior of medical-grade ultra-high molecular weight polyethylene (UHMWPE) (GUR 1050 resin) were evaluated as a function of polymer crystallinity. Crystallinity was controlled by heating UHMWPE to a temperature above its melting point and varying the hold time a...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2008.02.022
更新日期:2008-09-01 00:00:00
abstract::Lanreotide (LT), a synthetic analog of somatostatin, has been demonstrated to specifically bind to somatostatin receptors (SSTRs), which are widely overexpressed in several types of cancer cells. In this study, we incorporated a chemotherapeutic agent, methotrexate (MTX), and a photosensitizer material, polyaniline (P...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2017.12.033
更新日期:2018-03-01 00:00:00
abstract:UNLABELLED:Epithelial cellular heterogeneity has been observed in pathological tissues with abnormal matrix stiffness and cells cultured on rigid substrates. However, it remains unclear how matrix stiffness influences cellular heterogeneity formation in multi-cellular population. Here, we demonstrated that cellular het...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2016.05.025
更新日期:2016-09-01 00:00:00
abstract::A new series of beta Ti-Nb-Zr (TNZ) alloys with considerable plastic deformation ability during compression test, high elastic admissible strain, and excellent cytocompatibility have been developed for removable bone tissue implant applications. TNZ alloys with nominal compositions of Ti-34Nb-25Zr, Ti-30Nb-32Zr, Ti-28...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2015.03.023
更新日期:2015-07-01 00:00:00
abstract::With the increasing demand for novel bone repair solutions that overcome the drawbacks of current grafting techniques, the design of artificial bone scaffolds is a central focus in bone regeneration research. Calcium phosphate scaffolds are interesting given their compositional similarity with bone mineral. The majori...
journal_title:Acta biomaterialia
pub_type: 杂志文章,评审
doi:10.1016/j.actbio.2018.11.003
更新日期:2019-01-01 00:00:00
abstract::New bone cements made of Sr-substituted brushite-forming alpha-tricalcium phosphate (alpha-TCP) were prepared and characterized in the present work. The quantitative phase analysis and structural refinement of the starting powders and of hardened cements were performed by X-ray powder diffraction and the Rietveld refi...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2009.09.001
更新日期:2010-03-01 00:00:00
abstract::Durophagous fish consume a diet based primarily on hard-shelled animals, mainly mollusks. In order to successfully perform this task, they are equipped with an extra set of jaws located in their throat called pharyngeal jaws. Here we present the results of a study of the structure of the bony material of the exception...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2020.01.001
更新日期:2020-03-01 00:00:00
abstract:UNLABELLED:In order to create tissue-engineered heart valves with long-term functionality, it is essential to fully understand collagen remodeling during neo-tissue formation. Collagen remodeling is thought to maintain mechanical tissue homeostasis. Yet, the driving factor of collagen remodeling remains unidentified. I...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2015.10.044
更新日期:2016-01-01 00:00:00
abstract::The aim of the present study was to evaluate the biological properties of a collagen-phospholipid polymer hybrid gel (MiC30 gel) designed for use as a tissue membrane. The following four types of collagen gels were synthesized and tested in vitro and in vivo: physically cross-linked collagen gel (Uc gel), N-(3-dimethy...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2009.06.022
更新日期:2010-02-01 00:00:00
abstract::Surface functionalization has become of paramount importance and is considered a fundamental tool for the development and design of countless devices and engineered systems for key technological areas in biomedical, biotechnological and environmental applications. In this review, surface functionalization strategies f...
journal_title:Acta biomaterialia
pub_type: 杂志文章,评审
doi:10.1016/j.actbio.2013.03.036
更新日期:2013-07-01 00:00:00
abstract::Seeking strategies to enhance the overall combinations of mechanical properties is of great significance for engineering materials, but still remains a key challenge because many of these properties are often mutually exclusive. Here we reveal from the perspective of materials science and mechanics that adaptive struc...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2019.01.010
更新日期:2019-03-01 00:00:00
abstract::Thin film nitinol has unique mechanical properties (e.g., superelasticity), excellent biocompatibility, and ultra-smooth surface, as well as shape memory behavior. All these features along with its low-profile physical dimension (i.e., a few micrometers thick) make this material an ideal candidate in developing low-pr...
journal_title:Acta biomaterialia
pub_type: 杂志文章,评审
doi:10.1016/j.actbio.2015.03.025
更新日期:2015-07-01 00:00:00
abstract::In this paper, the 3D-morphology of the porosity in dentin is investigated within the first 350μm from the dentin-enamel junction (DEJ) by fluorescence confocal laser scanning microscopy (CLSM). We found that the porous microstructure exhibits a much more complex geometry than classically described, which may impact o...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2017.01.052
更新日期:2017-03-15 00:00:00
abstract::This study demonstrated that the surface crystallinity of carbon nanostructures is an additional independent factor that should be considered for the inhibition of cancer proliferation without activating reactive oxygen species (ROS). In addition, cytotoxic evaluation of both proliferating cancer cells and fully diffe...
journal_title:Acta biomaterialia
pub_type: 杂志文章
doi:10.1016/j.actbio.2012.05.013
更新日期:2012-09-01 00:00:00