当前位置： SCI文献检索 > INTERNATIONAL JOURNAL OF BIOLOGICAL MACROMOLECULES期刊下所有文献 > Material properties and cell compatibility of poly(γ-glutamic acid)-keratin hydrogels.

Material properties and cell compatibility of poly(γ-glutamic acid)-keratin hydrogels.

Abstract：

:Given the great demand for biopolymer and protein-based products from renewable resources, synthesis of a keratin-based hydrogel is presented herein. In this work, a novel hydrogel of poly(γ-glutamic acid) (γ-PGA) and keratin was synthesized through facile EDC·HCl/HOBt chemistry. Since keratin main chain is rich in amino side groups, carboxyl groups in γ-PGA were crosslinked with multi terminated amine groups in keratin. In the following, the hydrogel characteristics, including swelling ratio (2010% at molar ratio of HOBt/EDC = 0.105), in vitro degradation and mass loss (about 20% at day 21 for the aforementioned sample), chemical decomposition and the rheological properties were investigated. The chemical activator agents, enhanced the elastic modulus of swollen hydrogel from around 1000 to 4000 Pa by increasing the crosslinking degree. Despite good biocompatibility for cell growth, some kind of self-assembled keratin hydrogels are not suitable for microscopic observation while the γ-PGA-Keratin hydrogel in our study is transparent. The γ-PGA-Keratin hydrogels possess significant features of rapid hydrogel formation in seconds, maximum swelling ratio of about 2500% maximum elastic modulus (stiffness) of about 4.5 kPa (for the swollen sample) with controllable matrix pore size. For further application, the biocompatibility of the γ-PGA-Keratin hydrogel was assessed by live/dead assay. Recent studies have demonstrated the effect of hydrogel porosity, water absorbing and stiffness on cell spreading, proliferation and differentiation of mesenchymal stem cells. Bone marrow mesenchymal stem cells could be differentiated into various cell fates depending on the elastic modulus of materials they are cultured on. We carried out a statistical study (to skip the cell work labor) to predetermine the proper working span in which we can gain a hydrogel to cover all features needed to be applied for some application like cartilage repair.

journal_name

Int J Biol Macromol

journal_title

International journal of biological macromolecules

authors

Bajestani MI,Kader S,Monavarian M,Mousavi SM,Jabbari E,Jafari A

doi

10.1016/j.ijbiomac.2019.10.020

subject

Has Abstract

pub_date

2020-01-01 00:00:00

pages

790-802

eissn

0141-8130

issn

1879-0003

pii

S0141-8130(19)35146-3

journal_volume

142

pub_type

杂志文章

在线工具

Material properties and cell compatibility of poly(γ-glutamic acid)-keratin hydrogels.