Abstract:
PURPOSE:Limited information is available on the effect of Immediate Dentin Sealing (IDS) on the fracture strength of indirect partial posterior restorations. This study evaluated the effect of IDS on the fracture strength and failure types of two indirect restorative materials. MATERIALS AND METHODS:Standard MOD inlay preparations were made on sound molars (N=40, n=10 per group) and randomly divided into four groups to receive the inlay materials with and without the application of IDS: Group L-IDS-: Li2Si2O5 (Lithium disilicate, IPS e.max) without IDS; Group L-IDS+: Li2Si2O5 with IDS; Group MR-IDS-: Multiphase resin composite (MR, Lava Ultimate) without IDS; MR-IDS+: MR with IDS. Inlays made of L were etched with 5% hydrofluoric acid, and MR inlays were silica coated. After silanization, they were cemented using adhesive resin cement (Variolink Esthetic DC). The specimens were thermo-mechanically aged (1.2×106 cycles, 1.7Hz, 8000 cycles, 5-55°C) and then subjected to load to failure (1 mm/min). Failure types and locations of debondings were classified. Data were statistically analyzed using ANOVA, Mann Whitney U-test and Chi-square tests (α=0.05). Two-parameter Weibull distribution values including the Weibull modulus, scale (m) and shape (0), values were calculated. RESULTS:After aging conditions, no apparent changes were observed in marginal integrity but occlusal wear facets were more common with MR than with L (p<0.001). Material type and the application of IDS significantly affected the results (p=0.013). While group L-IDS- showed the lowest mean fracture strength (1358±506N) among all groups (p<0.05), application of IDS significantly increased the results significantly (L-IDS+: 2035±403N) (p=0.006). MR groups with and without IDS, did not show significant difference (MR-IDS-: 1861±423, MR-IDS+: 1702±596 N) (p=0.498). When materials without IDS are compared, L showed significantly lower results than that of MR (p=0.035). With the application of IDS, no significant difference was noted between L and MR materials (p=0.160). Weibull distribution presented the highest shape (0) for L-IDS+ (5.66) compared to those of other groups (3.01-4.76). Neither the material type (p=0.830), nor the application of IDS (p=0.54) affected the severity of the failure types. In 95% of the cases, the IDS layer left adhered on the tooth surface after fracture tests. In groups where no IDS was used, resin cement remained on the tooth surface in 44% of the cases (p=0.001). No significant differences were observed between the materials with respect to cement remnants or IDS after fracture (p=0.880). The incidence of repairable failure types (83%) was more common with L than with MR (75%) material (p>0.05). CONCLUSION:Immediate dentin sealing improves adhesion, and thereby the fracture strength of inlays made of lithium disilicate but not that multiphase resin composite.
journal_name
J Mech Behav Biomed Materauthors
van den Breemer CRG,Özcan M,Cune MS,van der Giezen R,Kerdijk W,Gresnigt MMMdoi
10.1016/j.jmbbm.2017.04.002subject
Has Abstractpub_date
2017-08-01 00:00:00pages
102-109eissn
1751-6161issn
1878-0180pii
S1751-6161(17)30154-6journal_volume
72pub_type
杂志文章abstract::Core decompression is a minimally invasive surgical technique used to treat patients with avascular necrosis of the femoral head. The procedure requires an entry hole in the lateral cortex of the femur which potentially leaves patients susceptible to subtrochanteric fractures. The purpose of this study was to determin...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.104263
更新日期:2021-03-01 00:00:00
abstract::Advances in adhesive technologies have increased indications for the use of inlays. Decrease in the bonded interface integrity due to wear has been cited as the main cause of its failure. However, this process of interface degradation and the influence of inlay material on damage mechanism appear to be poorly understo...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2019.103430
更新日期:2020-01-01 00:00:00
abstract::In this study, the fabrication and properties of a synthetic keratoprosthesis skirt for use in osteo-odonto-keratoprosthesis (OOKP) surgery are discussed. In the search for a new material concept, bioactive glass and polymethyl methacrylate (PMMA)-based composites were prepared. Three different bioactive glasses (i.e....
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2011.05.025
更新日期:2011-11-01 00:00:00
abstract::Biodegradable magnesium-calcium (MgCa) alloy is a very attractive orthopedic biomaterial compared to permanent metallic alloys. However, the critical issue is that MgCa alloy corrodes too fast in the human organism. Compared to dry cutting, the synergistic dry cutting-finish burnishing can significantly improve corros...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.11.026
更新日期:2018-02-01 00:00:00
abstract:OBJECTIVE:This study examined the effect of phytic acid (IP6) in stabilizing the morphology of dentine collagen network and resin-dentine bonding. METHODS:Dentine beams were fully demineralized with 10% phosphoric acid (PA) or 1% IP6 (pH 1.2). PA-demineralized beams were divided into three groups: (a) no further treat...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2015.03.027
更新日期:2015-08-01 00:00:00
abstract::In the present work, the releasing heat, scaffold apatite formation, and magnetic behavior of a novel diopside-magnetite nanocomposite with various contents of magnetite (Fe3O4) were evaluated. The N´eel and Brown relaxations did not have a significant effect on the specific absorption rate (SAR) of the composite samp...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.10.015
更新日期:2018-01-01 00:00:00
abstract::Crosslinked Ultra High Molecular Weight Polyethylene (UHMWPE), which is used as a bearing material in total joint replacement components, is subjected to static and cyclic loads in vivo. Resistance to crack initiation from a notch as a function of static and cyclic loads is not well understood for crosslinked UHMWPE. ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2018.12.032
更新日期:2019-03-01 00:00:00
abstract::Enamel possesses a complex hierarchical structure, which bestows this tissue with unique mechanical properties. In this study, the mechanical behavior of single enamel rods was investigated under uniaxial compression. Numerical simulations were also performed using micromechanics models for individual enamel rods to i...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2014.10.014
更新日期:2015-02-01 00:00:00
abstract::Use of hydroxyapatite (HAP) for biomaterials is widely established, often in a combination with titanium alloy substrates in orthopaedic and other implants. Porous HAP-based coatings undergo sintering and heat treatment processes to achieve proper level of density yet avoiding undesirable reactions and phase changes. ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.11.017
更新日期:2014-02-01 00:00:00
abstract::The adhesion of bovine chondrocytes and human osteoblasts to three titania-based coatings, formed by plasma electrolytic oxidation (PEO), was compared to that on uncoated Ti-6Al-4V substrates, and some comparisons were also made with plasma sprayed hydroxyapatite (HA) coatings. This was done using a centrifuge, with a...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2011.07.009
更新日期:2011-11-01 00:00:00
abstract::Using a 50-station pin-on-disc (SuperCTPOD) machine, the influence of lubricant viscosity on the wear of vitamin E blended crosslinked polyethylene was investigated. Five different test lubricants were prepared by mixing different concentrations of carboxymethyl cellulose powder with deionised water. The viscosity ran...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.104067
更新日期:2020-12-01 00:00:00
abstract::Infection incidence for total hip and knee arthroplasty (THA and TKA, respectively) is between 0.2% and 5% and results in approximately 100,000 device failures per year in the United States. Treatment requires prolonged systemic antibiotic therapy with additional surgical revisions. As a prophylactic measure against i...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2018.06.033
更新日期:2018-11-01 00:00:00
abstract::Pressure ulcers (PUs) are common in patients who chronically depend on a wheelchair for mobility, such as those with a spinal cord injury (SCI). In attempt to prevent the formation of PUs, pressure relieving maneuvers, such as push-ups, are commonly recommended for individuals with SCI. However, very little is known a...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.04.015
更新日期:2013-12-01 00:00:00
abstract::Nickel and carbides free Co-28Cr-6Mo alloy was fabricated by combination of mechanical alloying and warm pressing. The microstructure, mechanical properties, pin-on-disk dry sliding wear and corrosion behavior in simulated physiological solution were investigated. The produced Co-28Cr-6Mo alloy has elongated ultra-fin...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2015.12.039
更新日期:2016-07-01 00:00:00
abstract::Patent ductus arteriosus (PDA) is a congenital cardiovascular defect in which a fetal connection between the aorta and pulmonary artery does not spontaneously close shortly after birth. If left uncorrected serious complications and even death can occur. Surgical ligation is the traditional treatment method; however, i...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.07.033
更新日期:2017-11-01 00:00:00
abstract::Patient-specific finite element models have been used to predict femur strength and fracture risk in individuals. Validation of the adopted finite element modelling procedure against mechanical testing data is a crucial step when aiming for clinical applications. The majority of the works available in literature used ...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.02.006
更新日期:2013-05-01 00:00:00
abstract::During an underbody blast (UBB) event, mounted occupants are exposed to high rate loading of the spine via the pelvis. The objective of this study was to simulate UBB loading conditions and examine mechanisms of injury in the thoracic, lumbar and sacral spine. Fourteen instrumented, whole-body, postmortem human subjec...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.104271
更新日期:2020-12-24 00:00:00
abstract::With the aim to prepare antibacterial acrylic bone cements, a series of imidazolium-containg mono-methacrylates with N-alkyl chain length varied from 10 to 18 (MEIM-x) were synthesized as polymerizable antibacterial agents through a two-step reaction. The structures of the monomers were confirmed by 1H NMR. Methyl met...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2017.06.003
更新日期:2017-10-01 00:00:00
abstract::Vascular calcification is a complex molecular process that exhibits a number of relatively characteristic morphology patterns in atherosclerotic plaques. Treatment of arterial stenosis by endovascular intervention, involving forceful circumferential expansion of the plaque, can be unpredictable in calcified lesions. T...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2015.11.001
更新日期:2016-03-01 00:00:00
abstract::This study assessed the fatigue performance (biaxial flexure fatigue strength), surface characteristics (topography and roughness) and structural stability (t-m phase transformation) of a Y-TZP ceramic subjected to air-abrasion using new powders (7% and 20% silica-coated aluminum oxide particles) in comparison to comm...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2019.05.032
更新日期:2019-10-01 00:00:00
abstract::The goal of this study was to investigate the effect of resveratrol treatment on the osteogenic potential of human and rat adipose derived stem cells in a 3-D culture environment. Adipose derived stem cells (ADSCs) have been widely studied and have shown promise as a potential source of osteogenic progenitor cells. Pr...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2011.08.014
更新日期:2012-07-01 00:00:00
abstract::Previous studies on knee biomechanics have mainly focused on the joint structure itself, largely neglecting the material properties of the muscles and connective tissues around the knee joint. Therefore, this study was purposed to conduct a systematic in vivo examination of the material properties of muscles, tendons,...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103829
更新日期:2020-09-01 00:00:00
abstract::Bones are composed of hierarchical bio-composite materials characterized by complex multiscale structural geometry and behavior. The architecture and the mechanical properties of bone tissue differ at each level of hierarchy. Thus, a multiscale approach for mechanical analysis of bone is imperative. This paper propose...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2011.03.003
更新日期:2011-08-01 00:00:00
abstract::After fractures, bone can experience different potential outcomes: successful bone consolidation, non-union and bone failure. Although, there are a lot of factors that influence fracture healing, experimental studies have shown that the interfragmentary movement (IFM) is one of the main regulators for the course of bo...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2013.09.023
更新日期:2014-01-01 00:00:00
abstract::Bioink plays a major role in 3D printing of tissues and organs. Alginate is a widely used component for bioinks but its cellular responses are limited, which limits its clinical translation. In this study, we demonstrate the printability and cellular compatibility of composite bioink consists of sodium alginate (NaAlg...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103642
更新日期:2020-04-01 00:00:00
abstract::The aim of this work was to assess the influence of reduction of the apparent mechanical properties of fully load-bearing porous titanium implants used in mandibular bone defects. Segmental 18mm long bone defects were created bilaterally in the lower jaws of adult ewes. One group of 6 ewes (group A) was treated with l...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2016.02.036
更新日期:2016-06-01 00:00:00
abstract::The AFM combined nanoindentation was performed to observe the ultrastructure of enamel rod from various section plans and positions while probing their mechanical and tribological properties of the area. The nanohardness and the elastic modulus of the head region of the enamel rods are significantly higher than that o...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2010.12.002
更新日期:2011-05-01 00:00:00
abstract::In this paper, a physics-based mathematical model is developed to describe the transient behavior of the brachial artery during the Flow Mediated Dilation (FMD) test. The change of the artery's diameter was collected for 7 cases via in vivo, non-invasive ultrasound imaging. A theoretical model was developed to capture...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2020.103756
更新日期:2020-07-01 00:00:00
abstract::With increasing interest in treating osteoarthritis at its earliest stages, it has become important to understand the mechanisms by which the disease progresses across a joint. Here, second harmonic generation (SHG) microscopy, coupled with a two-dimensional spring-mass network model, was used to image and investigate...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2011.08.004
更新日期:2012-01-01 00:00:00
abstract::Understanding tendon mechanobiology is important for gaining insight into the development of tendon pathology and subsequent repair processes. The aim of this study was to investigate how experimentally observed mechanobiological adaptation of rat Achilles tendons translate to changes in constitutive mechanical proper...
journal_title:Journal of the mechanical behavior of biomedical materials
pub_type: 杂志文章
doi:10.1016/j.jmbbm.2019.04.041
更新日期:2019-08-01 00:00:00