Influence of water storage on fatigue strength of self-etch adhesives.

Abstract:

OBJECTIVES:The purpose of this study was to determine enamel and dentin bond durability after long-term water storage using self-etch adhesives. METHODS:Two single step self-etch adhesives (SU, Scotchbond Universal and GB, G-ӕnial Bond) and a two-step self-etch adhesive (OX, OptiBond XTR) were used. The shear bond strength (SBS) and shear fatigue strength (FS) of the enamel and dentin were obtained with and without phosphoric acid pre-etching prior to application of the adhesives. The specimens were stored in distilled water at 37 °C for 24 h, 6 months, and one year. A staircase method was used to determine the FS using a frequency of 10 Hz for 50,000 cycles or until failure occurred. RESULTS:The SBS and FS of enamel bonds were significantly higher with pre-etching, when compared to no pre-etching for the same water storage period. The FS of dentin bonds with pre-etching tended to decrease relative to no pre-etching at the same storage period. For the one year storage period, SU and GB with pre-etching showed significantly lower FS values than the groups without pre-etching. CONCLUSIONS:The influence of water storage on FS of the self-etch adhesives was dependent on the adhesive material, storage period and phosphoric acid pre-etching of the bonding site. CLINICAL SIGNIFICANCE:Phosphoric acid pre-etching of enamel improves the effectiveness of self-etch adhesive systems. Inadvertent contact of phosphoric acid on dentin appears to reduce the ability of self-etch adhesives to effectively bond resin composite materials.

journal_name

J Dent

journal_title

Journal of dentistry

authors

Takamizawa T,Barkmeier WW,Tsujimoto A,Scheidel DD,Watanabe H,Erickson RL,Latta MA,Miyazaki M

doi

10.1016/j.jdent.2015.10.018

subject

Has Abstract

pub_date

2015-12-01 00:00:00

pages

1416-27

issue

12

eissn

0300-5712

issn

1879-176X

pii

S0300-5712(15)30064-6

journal_volume

43

pub_type

杂志文章
  • Clinical performance and marginal adaptation of class II direct and semidirect composite restorations over 3.5 years in vivo.

    abstract:OBJECTIVE:The study evaluated the clinical performance and marginal adaptation of direct and semi-direct class II composite restorations in a split-mouth design over 3.5 years. DESIGN:44 upper posterior teeth in 11 adults with primary carious lesions were treated with 22 direct and 22 semi-direct restorations. Convent...

    journal_title:Journal of dentistry

    pub_type: 临床试验,杂志文章,随机对照试验

    doi:10.1016/j.jdent.2004.11.009

    authors: Spreafico RC,Krejci I,Dietschi D

    更新日期:2005-07-01 00:00:00

  • Improving the quality of papers submitted to dental journals: Transcription of session for editors, associate editors, publishers and others with an interest in scientific publishing held at IADR meeting in Cape Town on Wednesday, 25 June 2014.

    abstract::This satellite symposium was the fourth in a series for editors, publishers, reviewers and all those with an interest in scientific publishing. It was held on Wednesday 25th June 2014 at the IADR International meeting in Cape Town, South Africa. The symposium attracted more than 180 attendees. This symposium placed an...

    journal_title:Journal of dentistry

    pub_type:

    doi:10.1016/j.jdent.2015.02.007

    authors: Eaton KA,Giannobile WV,Sourgen DL,Balaji SM,Honkala E,Lynch CD

    更新日期:2015-08-01 00:00:00

  • Tooth whitening evaluation of blue covarine containing toothpastes.

    abstract:OBJECTIVES:To measure the tooth whitening effects delivered immediately after brushing with silica-based toothpastes containing blue covarine in vitro and in vivo. METHODS:Salivary pellicle coated human extracted teeth were brushed with either a slurry of a toothpaste containing blue covarine (BC), a formulation conta...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2017.10.014

    authors: Tao D,Smith RN,Zhang Q,Sun JN,Philpotts CJ,Ricketts SR,Naeeni M,Joiner A

    更新日期:2017-12-01 00:00:00

  • Effect of shading technique and thickness on color stability and translucency of new generation translucent zirconia.

    abstract:OBJECTIVE:To evaluate the effect of shading technique and thickness on the color stability and translucency of translucent zirconia after coffee thermocycling. METHODS:Specimens in different thicknesses (1; 1.5; 2 mm) (n = 4 for each thickness) were sectioned from translucent preshaded zirconia (Pre) and externally sh...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2018.03.011

    authors: Alp G,Subaşı MG,Seghi RR,Johnston WM,Yilmaz B

    更新日期:2018-06-01 00:00:00

  • Longevity of defective direct restorations treated by minimally invasive techniques or complete replacement in permanent teeth: A systematic review.

    abstract:OBJECTIVES:This systematic review aimed to verify if there is difference in the longevity of minimally invasive techniques compared to the complete replacement for the treatment of defective direct restorations in permanent teeth. DATA:The data included randomized controlled clinical trials comparing the clinical perf...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2018.09.001

    authors: Martins BMC,Silva EJNLD,Ferreira DMTP,Reis KR,Fidalgo TKDS

    更新日期:2018-11-01 00:00:00

  • Validation of swept source optical coherence tomography (SS-OCT) for the diagnosis of smooth surface caries in vitro.

    abstract:OBJECTIVE:An accurate evaluation of the extent of dental caries and possible progress of the lesion from enamel into dentin is very important in clinical dentistry. Dentists need an imaging technology that can noninvasively and reliably quantify the extent of caries. This study aimed to evaluate the effectiveness of no...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2012.10.007

    authors: Nakagawa H,Sadr A,Shimada Y,Tagami J,Sumi Y

    更新日期:2013-01-01 00:00:00

  • Effect of sandblasting, grinding, polishing and glazing on the flexural strength of two pressable all-ceramic dental materials.

    abstract:OBJECTIVES:During laboratory fabrication procedures and/or clinical adjustments, pressable materials: IPS Empress and Empress 2, may be ground, polished or sandblasted. These treatments may affect their strength by introducing microscopic flaws and defects. This study investigates the effect of these procedures on the ...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2003.08.006

    authors: Albakry M,Guazzato M,Swain MV

    更新日期:2004-02-01 00:00:00

  • Can repair increase the longevity of composite resins? Results of a 10-year clinical trial.

    abstract:OBJECTIVES:The aim of this double-blind clinical trial was to assess the longevity of repairs to localized clinical defects in composite resin restorations that were initially planned to be treated with a restoration replacement. METHODS:Twenty-eight patients aged 18-80 years old with 50 composite resin restorations (...

    journal_title:Journal of dentistry

    pub_type: 杂志文章,随机对照试验

    doi:10.1016/j.jdent.2014.05.015

    authors: Fernández E,Martín J,Vildósola P,Oliveira Junior OB,Gordan V,Mjor I,Bersezio C,Estay J,de Andrade MF,Moncada G

    更新日期:2015-02-01 00:00:00

  • Use of metal conditioners to improve bond strengths of autopolymerizing denture base resin to cast Ti-6Al-7Nb and Co-Cr.

    abstract:OBJECTIVE:The shear bond strengths of an autopolymerizing denture base resin to cast Ti-6Al-7Nb and Co-Cr alloys using three metal conditioners were investigated. METHODS:Ti-6Al-7Nb alloy and Co-Cr alloy discs were cast. The disc surfaces were air-abraded with 50 microm alumina particles and treated with three metal c...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2005.05.002

    authors: Shimizu H,Kurtz KS,Tachii Y,Takahashi Y

    更新日期:2006-02-01 00:00:00

  • Human epithelial tissue culture study on restorative materials.

    abstract:OBJECTIVES:Health condition of the gingival tissues contacting the surfaces of fixed prostheses is a result of multiple etiologic factors. The aim of the investigation discussed here was to evaluate the attachment and proliferation rate of cultured human epithelial cells on three commonly used restorative materials und...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2013.11.008

    authors: Forster A,Ungvári K,Györgyey Á,Kukovecz Á,Turzó K,Nagy K

    更新日期:2014-01-01 00:00:00

  • Quantification of dental plaque in the research environment.

    abstract:OBJECTIVES:To review the established and novel methods of plaque quantification employed in dental research, including a discussion of their merits and to present a new method of planimetrically measuring plaque using light induced fluorescence. METHOD:Quantitative light-fluorescence (QLF) images were acquired from th...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2004.10.017

    authors: Pretty IA,Edgar WM,Smith PW,Higham SM

    更新日期:2005-03-01 00:00:00

  • Estimated erosive potential depends on exposure time.

    abstract:OBJECTIVES:Evaluate erosive potential of beverages, using exposure times from 3 to 30 min, and to analyse the relationship between erosion and several drink parameters. METHODS:pH, calcium, phosphate and fluoride concentration, saturation, titratable-acidity to pH 5.5 and the viscosity of sixteen beverages were measur...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2012.09.004

    authors: Jager DH,Vieira AM,Ruben JL,Huysmans MC

    更新日期:2012-12-01 00:00:00

  • Outcome of direct restorations placed within the general dental services in England and Wales (Part 3): variation by dentist factors.

    abstract:AIM:It is the aim of this paper to investigate the survival of direct-placement restorations provided within the General Dental Services in England and Wales, in relation to the dentist factors which may affect this. METHODS:For this work, survival of a restoration was considered to be the time between the date of com...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2005.03.009

    authors: Lucarotti PS,Holder RL,Burke FJ

    更新日期:2005-11-01 00:00:00

  • Pre-heating of high-viscosity bulk-fill resin composites: effects on shrinkage force and monomer conversion.

    abstract:OBJECTIVES:To investigate the influence of pre-heating of high-viscosity bulk-fill composite materials on their degree of conversion and shrinkage force formation. METHODS:Four bulk-fill composite materials (Tetric EvoCeram Bulk Fill-TECBF, x-tra fil-XF, QuixFil-QF, SonicFill-SF) and one conventional nano-hybrid resin...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2015.07.014

    authors: Tauböck TT,Tarle Z,Marovic D,Attin T

    更新日期:2015-11-01 00:00:00

  • Opalescence of bleached teeth.

    abstract:OBJECTIVES:To evaluate the influence of tooth bleaching on the opalescence properties of enamel. METHODS:Color of 38 specimens was determined by colorimetric analysis before and after bleaching in the reflectance and transmittance modes. The results were described as CIELab color coordinates. The Opalescent Parameter ...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2012.01.011

    authors: Schmeling M,Maia HP,Baratieri LN

    更新日期:2012-07-01 00:00:00

  • Modulated photoactivation methods: Influence on contraction stress, degree of conversion and push-out bond strength of composite restoratives.

    abstract:OBJECTIVES:Verify the influence of curing methods on contraction stress, stress rate, and degree of conversion (DC) of a restorative composite and on bond strength of composite restoratives. METHODS:For the stress test, composite (0.84 mm thick) was applied between two 5-mm diameter glass rods, mounted in a servohydra...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2006.10.003

    authors: Cunha LG,Alonso RC,Pfeifer CS,Correr-Sobrinho L,Ferracane JL,Sinhoreti MA

    更新日期:2007-04-01 00:00:00

  • Metal chloride primers for bonding dentine with tri-n-butylborane-initiated luting agents.

    abstract:OBJECTIVES:The bonding of resin to dentine is dependent largely on surface modifications. The purpose of the present study was to test the hypothesis that a role of the metal chlorides used as primers is to initiate polymerization of resin at the resin-dentine interface, thereby affecting bond strength. METHODS:Nine p...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/s0300-5712(97)00030-4

    authors: Taira Y,Matsumura H,Yoshida K,Kamada K,Tanaka T,Atsuta M

    更新日期:1998-09-01 00:00:00

  • A laboratory investigation of the role of guide planes in the retention of cast cobalt-chromium alloy partial denture frameworks.

    abstract:OBJECTIVES:This in vitro study examined the resistance to displacement offered by guide planes and the displacement mechanics of a bilateral bounded saddle cast cobalt chrome alloy removable partial denture framework under conditions simulating an average initial fit. METHODS:A specially designed model mouth jig fitte...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/s0300-5712(01)00016-1

    authors: Ali M,Waters NE,Nairn RI,West F,Sherriff M

    更新日期:2001-05-01 00:00:00

  • 'Interleukin-4 gene polymorphism and its relation to periodontal disease in a Brazilian population of African heritage'.

    abstract:OBJECTIVES:Host modifying factors, such as genetic predisposition, may increase severity of periodontitis. Genetic polymorphisms in interleukin-4 (IL-4) genes seem to influence host response to microbial challenge. Two IL-4 polymorphisms were found in association with asthma and atopy, and later with aggressive periodo...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2003.11.004

    authors: Pontes CC,Gonzales JR,Novaes AB Jr,Taba Júnior M,Grisi MF,Michel J,Meyle J,de Souza SL

    更新日期:2004-03-01 00:00:00

  • Evaluation of laboratory scanner accuracy by a novel calibration block for complete-arch implant rehabilitation.

    abstract:OBJECTIVES:To compare the accuracies of 4 laboratory scanners using a new custom-made block for complete-arch implant rehabilitation. MATERIALS AND METHODS:A block comprised 4 cylinders, with 2 in the anterior (0° angulation) and 2 in the posterior region (45° distal angulation) (Experimental group) and a standard blo...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2020.103476

    authors: Pan Y,Tam JM,Tsoi JK,Lam WY,Huang R,Chen Z,Pow EH

    更新日期:2020-11-01 00:00:00

  • Final year dental students' views on cross-infection precautions.

    abstract::This study was undertaken to determine the influence that undergraduate training currently has on the formation of clinical management strategies for minimizing cross-infection, among final year dental students. A 10-page questionnaire was sent to final year dental students attending 15 of the UK's 16 dental schools. ...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/0300-5712(93)90155-j

    authors: Nuttall NM,Gilbert AD

    更新日期:1993-04-01 00:00:00

  • Monitoring bacterial-demineralization of human dentine by electrochemical impedance spectroscopy.

    abstract:OBJECTIVE:The purpose of this study was two-fold: (1) to monitor bacterial biofilm formation and bacteria-induced demineralization of dentine in situ by using electrochemical impedance spectrum (EIS); (2) to examine the relationship between EIS findings and changes in the chemical composition and ultrastructure of dent...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2009.09.013

    authors: Xu Z,Neoh KG,Amaechi B,Kishen A

    更新日期:2010-02-01 00:00:00

  • The effect of sandblasting on adhesion of a dual-cured resin composite to methacrylic fiber posts: microtensile bond strength and SEM evaluation.

    abstract:OBJECTIVES:To evaluate the influence of different surface treatments on the microtensile bond strength of a dual-cured resin composite to fiber posts. METHODS:Thirty-two glass methacrylate-based fiber posts (GC Corp.) were used in the study. Posts were divided into two groups, according to the surface pretreatment per...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2007.01.009

    authors: Radovic I,Monticelli F,Goracci C,Cury AH,Coniglio I,Vulicevic ZR,Garcia-Godoy F,Ferrari M

    更新日期:2007-06-01 00:00:00

  • Enamel surface roughness and dental pulp response to coaxial carbon dioxide-neodymium: YAG laser irradiation.

    abstract::The purpose of this study was to evaluate the effect of a coaxial carbon dioxide/neodymium:yttrium aluminium garnet laser beam on enamel surface roughness and the dental pulps of mongrel dogs. In four dogs, four maxillary left posterior teeth were irradiated at 16 cm source-tooth distances. Two teeth were irradiated w...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/0300-5712(91)90095-g

    authors: Arcoria CJ,Steele RE,Wagner MJ,Judy MM,Matthews JL,Hults DF

    更新日期:1991-04-01 00:00:00

  • Muted dental voices on interprofessional healthcare teams.

    abstract::This paper addresses three main themes: (1) oral health and frailty; (2) interprofessional healthcare teams; and (3) dental professionals on healthcare teams. Oral diseases exacerbate frailty, are rampant in most long-term care (LTC) facilities, and typically are not managed effectively by the medical and nursing staf...

    journal_title:Journal of dentistry

    pub_type: 杂志文章,评审

    doi:10.1016/j.jdent.2011.10.017

    authors: MacEntee MI

    更新日期:2011-12-01 00:00:00

  • Effect of surface treatments on the tensile bond strength of repaired water-aged anterior restorative micro-fine hybrid resin composite.

    abstract:OBJECTIVES:The purpose of this study was to characterize changes in surface topography associated with different surface treatments and their effect on tensile bond strength (TBS) of repaired water-aged anterior restorative micro-fine hybrid resin composite. METHODS:The TBS of repaired resin-based composite slabs eith...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2008.07.014

    authors: Fawzy AS,El-Askary FS,Amer MA

    更新日期:2008-12-01 00:00:00

  • Array analysis for T-cell associated cytokines in gingival crevicular fluid: Identifying altered profiles associated with periodontal disease status.

    abstract:OBJECTIVE:Cytokine networks regulate innate and adaptive immune responses, which in turn are recognised to direct the progression or arrest of periodontal disease. This study aimed to compare the profile of seven cytokines, implicated in regulating T-cell networks, in gingival crevicular fluid (GCF) samples with differ...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/j.jdent.2019.04.009

    authors: Koshy B,Rees JS,Farnell DDJJ,Wei XQ,Waddington RJ

    更新日期:2019-06-01 00:00:00

  • Dentifrice pH but not consistency may affect fluoride uptake in plaque.

    abstract:OBJECTIVE:Test the ability of acidic fluoridated solutions to enhance fluoride (F) bound on bacteria (1) and the effect of dentifrice consistency on plaque fluid F uptake (2). METHODS:(1) Streptococcus mutans isolates were grown in BHI medium (37°C/18h). Bacteria were washed either with EDTA or CaCl2 both at 1mM to re...

    journal_title:Journal of dentistry

    pub_type: 杂志文章,随机对照试验

    doi:10.1016/j.jdent.2014.12.003

    authors: Cardoso CA,Levy FM,Peres-Buzalaf C,Buzalaf MA

    更新日期:2015-02-01 00:00:00

  • Relationship between dentine hydraulic conductance and the cytotoxicity of four dentine bonding resins in vitro.

    abstract:OBJECTIVES:Dentine modifies pulpward diffusion of monomers leaching from restorative materials. Thus, remaining dentine thickness must be taken into account during in vitro cytotoxicity tests. This in vitro study was designed to determine the influence of dentine permeability on the outcome of a cytotoxicity test. MET...

    journal_title:Journal of dentistry

    pub_type: 杂志文章

    doi:10.1016/s0300-5712(98)00019-0

    authors: Abou Hashieh I,Franquin JC,Cosset A,Dejou J,Camps J

    更新日期:1998-07-01 00:00:00

  • Biocompatibility of glass-ionomer bone cements.

    abstract::Glass-ionomer cements (GIC) have been extensively used in dentistry for over 30 years. Due to their excellent biocompatibility in dental applications GIC have been formulated for medical applications. The past decade has seen some impressive advances in the development of medical GICs, however these advances have been...

    journal_title:Journal of dentistry

    pub_type: 杂志文章,评审

    doi:10.1016/j.jdent.2004.10.027

    authors: Hatton PV,Hurrell-Gillingham K,Brook IM

    更新日期:2006-09-01 00:00:00