Abstract:
:This study investigated the efficacies of adhesive resin cements (Clearfil SA Luting, Maxcem, G-CEM, RelyX Unicem Clicker, Vitremer Paste) for bonding to Ag-Pd-Cu-Au alloy not surface-pretreated with metal primer. For control, Panavia F 2.0 -developed for use with a proprietary metal primer, Alloy Primer- was tested with and without metal primer application. Pairs of alloy disks (10.0 and 8.0 mm in diameters, 3.0 mm thickness) were air-abraded with alumina and bonded with one of the cements. Shear bond strengths (SBSs) were measured before and after 50,000 times of thermocycling. Among Maxcem, RelyX Unicem Clicker and the control, there were no statistical differences in SBS before and after thermocycling. After thermocycling, Clearfil SA Luting exhibited the highest SBS among all the cements. Results showed that Clearfil SA Luting, Maxcem, and RelyX Unicem Clicker were efficacious for bonding to Ag-Pd-Cu-Au alloy after air abrasion surface treatment for the latter.
journal_name
Dent Mater Jjournal_title
Dental materials journalauthors
Muraguchi K,Minami H,Minesaki Y,Suzuki S,Tanaka Tdoi
10.4012/dmj.2010-093subject
Has Abstractpub_date
2011-01-01 00:00:00pages
199-205issue
2eissn
0287-4547issn
1881-1361pii
JST.JSTAGE/dmj/2010-093journal_volume
30pub_type
杂志文章abstract::This study compared differences in discoloration and dissolution in several titanium alloys with immersion in peroxide- or fluoride-containing solution. Commercially pure titanium (CP-Ti) and six titanium-based alloys were used: Ti-0.15Pd, Ti-6Al-4V, Ti-7Nb-6Al, Ti-55Ni, Ti-10Cu, and Ti-20Cr. Two test solutions were p...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.117
更新日期:2008-01-01 00:00:00
abstract::The aim was to investigate the effect of simulated low-temperature degradation (s-LTD) and hydrothermal fatigue on the degradation of three ZrO(2)-based dental materials. Lava, IPS, and NanoZr discs were randomly assigned to (1) Control-Storage in distilled water at 37°C; (2) Aging at 134°C for 5 h (s-LTD); (3) Thermo...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-216
更新日期:2012-01-01 00:00:00
abstract::The diamond burs of two dental CAD/CAM systems (GN and CD) were examined if they could be used to fabricate up to 21 ceramic full crowns without fracture. After one, 11, and 21 machining times, the surfaces of the diamond burs were observed and the number of particles captured on SEM pictures was counted. The average ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.134
更新日期:2005-03-01 00:00:00
abstract::Application of a light-cured porcelain margin is a technique which has been developed recently. In this study, we compared the porcelain margin properties of the porcelain-light-cured resin matrix system and the traditional porcelain-water system, in terms of volumetric shrinkage, density, compressive strength, surfac...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.14.1
更新日期:1995-06-01 00:00:00
abstract::Besides micro-mechanical interlocking through hybrid-layer formation, self-etch adhesives may benefit from additional chemical interaction between the functional monomer and residual hydroxyapatite. One-step adhesives are commonly associated with lower bonding effectiveness, which must be attributed in part to the dis...
journal_title:Dental materials journal
pub_type: 杂志文章,评审
doi:10.4012/dmj.24.1
更新日期:2005-03-01 00:00:00
abstract::This study evaluated a new enzyme solution (SFC-V) for dentin caries removal, and obtained results were compared with Carisolv. Both solutions were used with a prototype plastic instrument - this being a modified technique for Carisolv. Five carious deciduous teeth were sectioned, and both treatments were applied alte...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.675
更新日期:2006-12-01 00:00:00
abstract::The depths of cure and the distributions of degree of conversion (DC), polymerization conversion (PC) and percent pendant double bonds (PDB) of light-cured composite resins cured under various intensities of light were investigated. When the total amount of exposure, represented by the product of the light intensity a...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.13.198
更新日期:1994-12-01 00:00:00
abstract::The aim was to evaluate the effect of different zirconia discontinuous fiber fractions on radiopacity and other selected properties of glass discontinuous fiber-reinforced flowable composite (Exp-SFRC). Exp-SFRC was prepared by mixing 30 wt% of resin-matrix and 45 wt% of particulate-fillers to 25 wt% of various weight...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2018-102
更新日期:2019-03-31 00:00:00
abstract::This study investigated the effect of a coating material containing S-PRG fillers on the demineralization of bovine enamel and dentin, by measuring changes in the transmitted ultrasonic velocity. Bovine enamel and dentin specimens with and without coating (n=6 for each condition) were cut into blocks, immersed in 0.1 ...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2012-153
更新日期:2012-01-01 00:00:00
abstract::The aim of the study was to evaluate bone regeneration using a canine model with surgically created periodontal defects filled for 12 weeks using a stratified biomaterial consisting in a biphasic calcium phosphate (BCP) covered with a crosslinking hydrogel acting as polymer membrane of silated hydroxypropyl methylcell...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-238
更新日期:2018-09-30 00:00:00
abstract::The objective of this study was to test the hypothesis that thermal cycling weakens the flexural strength of porcelain. Specimens of Deguceram Gold and Vita Omega 900 were tested in four groups of 30 specimens each: in the original glazed condition versus being ground with 1000-grit, 600-grit, and 100-grit silicon car...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.28.433
更新日期:2009-07-01 00:00:00
abstract::This study investigated the effects of storing impressions for 3 hours after spraying them with a disinfectant solution on dimensional change and deformation of maxillary edentulous stone models. Three brands of alginate impression materials, characterized by a small degree of contraction in 100% relative humidity, we...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-083
更新日期:2010-05-01 00:00:00
abstract::Despite progress in the development of denture base resin and artificial tooth materials, dental clinics are still plagued with artificial teeth falling off the denture base--due to poor bond strength--after denture delivery. Against this background, this study sought to examine the effect and durability of an adhesiv...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.75
更新日期:2006-03-01 00:00:00
abstract::This study was evaluating how three desensitizing toothpastes used at home influence the effect associated with desensitizing agents after application in the clinic. Fifty dentine disks measure it permeability and 32 dentine disks with similar permeability levels were selected. Following Dental desensitizer treatment,...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2019-164
更新日期:2020-09-29 00:00:00
abstract::The possibility of the segregation under solidification process using a centrifugal casting machine was investigated using an electron probe microanalyzer with elemental distribution map, line analysis and quantitative analysis. When a very small quantity of platinum was added to local molten titanium during the casti...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.15.212
更新日期:1996-12-01 00:00:00
abstract::The purpose of this study was to characterize the surface damages of zirconia by Nd:YAG dental laser irradiation through a systematic evaluation of the associated microstructural changes. Disk specimens of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) and ceria-stabilized zirconia/alumina nanocomposite (C...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2009-127
更新日期:2010-10-01 00:00:00
abstract::The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to e...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-012
更新日期:2018-01-30 00:00:00
abstract::Ti-6Al-7Nb alloy was cast into three differently designed, removable partial denture frameworks: Palatal strap (PS), Anterior-posterior bar (AP), and Horseshoe-shaped bar (HS). The vertical displacement and local strain of Ti-6Al-7Nb alloy frameworks were investigated to compare against those of Co-Cr alloy frameworks...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.23.497
更新日期:2004-12-01 00:00:00
abstract::This study aimed to introduce a procedure for determining the bilinear elastic moduli (E1 and E2) of the periodontal ligament for a mathematical tooth model to analyse stress in the mandible. The bone and tooth morphology were scanned from a dry skull and an extracted intact tooth, respectively, and reconstructed in a...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2010-170
更新日期:2011-01-01 00:00:00
abstract::To evaluate the effect of a dentin adhesive on sclerotic dentin, contraction gap width and shear bond strength were measured. Dentin cavity wall was pretreated with an experimental dentin bonding system with and without a dentin primer, or with a commercial dentin bonding system. In the experimental dentin bonding gro...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.576
更新日期:2006-09-01 00:00:00
abstract::Enamel demineralization is one of the most undesired side effects of fixed orthodontic treatment, which will lead to white spot lesions (WSLs) on tooth surfaces. The development of WSLs is due to prolonged accumulation of bacterial plaque and associated acid production. Self-etching adhesives have been used in orthodo...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2017-286
更新日期:2018-07-29 00:00:00
abstract::The aim of this investigation was to evaluate the metal-ceramic bonding of Au-1.6 wt% Ti alloy. Therefore, the coefficient of thermal expansion, modulus of elasticity, ceramic bonding strength, and hardness of Au-1.6 wt% Ti alloy were measured. The metal-ceramic interface was observed by EPMA to investigate its bondin...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.24.268
更新日期:2005-06-01 00:00:00
abstract::The aim of this study was to investigate the effects of potassium fluoride (KF) and sodium fluoride (NaF) in different concentrations on micro-shear bond strength (µSBS) and their protective effects against acid. The enamel blocks were treated with several concentrations of KF and NaF. For µSBS, Clearfil SE Bond 2 was...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2020-019
更新日期:2020-10-27 00:00:00
abstract::The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-023
更新日期:2011-01-01 00:00:00
abstract::In this study, different glasses were investigated to improve reusable investments. Borosilicate glass (BSG) powder and soda-lime glass (SLG) powder were prepared by milling broken beakers and microscope slides, respectively, and used in experimental investments (I-BSG, I-SLG) by blending glass powder (10 wt%) with cr...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.2011-040
更新日期:2011-01-01 00:00:00
abstract::The aim of this study was to investigate the bond durability of heat-polymerized denture base resin to cast CP Ti and Co-Cr alloy. The alloy specimens were divided into five groups: 1) airborne-particle abraded with 50 µm alumina (SAND), 2) Rocatec tribochemical silica coating system (RO), 3) air-abraded followed by a...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2010-089
更新日期:2011-01-01 00:00:00
abstract::The purpose of this study was to examine the antibacterial activity of composite resin with glass-ionomer filler particles versus that of contemporary commercial composite resins. Three composite resins were used: Beautifil II (containing S-PRG filler), Clearfil AP-X, and Filtek Z250. Resin blocks were bonded to maxil...
journal_title:Dental materials journal
pub_type: 杂志文章,随机对照试验
doi:10.4012/dmj.2009-050
更新日期:2010-03-01 00:00:00
abstract::To investigate the bonding of tooth-colored indirect restorations to cervical dentin, shear bond strengths of bonded resin inlays to cervical dentin and mid-coronal dentin were investigated and compared. Indirectly fabricated composite inlays (Estenia) were cemented with a dual-cured resin cement (Panavia Fluoro Cemen...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.25.7
更新日期:2006-03-01 00:00:00
abstract::The aim of this in vitro study was to evaluate the effects of different preparation angles on the precision of fit of zirconia crown frameworks. Dies were fabricated with three different preparation angles: 4, 8, and 12 degrees total taper. Ten copings were fabricated for each angle by a laboratory and a milling-cente...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.814
更新日期:2008-11-01 00:00:00
abstract::The behavior of microencapsulated polymerization initiators in dental adhesives is unknown. This study investigated the effects of new microencapsulated initiators in novel, multi-purpose, PMMA-type adhesive resin on the bonding performance and polymerization reactivity. Microencapsulated BPO and 1,3,5-trimethylbarbit...
journal_title:Dental materials journal
pub_type: 杂志文章
doi:10.4012/dmj.27.35
更新日期:2008-01-01 00:00:00