Effects of attrition, prior acid-etching, and cyclic loading on the bond strength of a self-etching adhesive system to dentin.

Abstract:

:The purpose of this study was to evaluate the effects of dentin attrition, phosphoric acid etching, and cyclic loading on the microtensile bond strength (microTBS) of a self-etching adhesive system to dentin. Flat dentin surfaces of human molars were assigned to eight experimental groups based on those with or without attrition, prior acid-etching, and cyclic loading. Resin composite paste was placed and polymerized after the bonding procedure according to manufacturer's instructions. The specimens were subjected to microTBS testing at a crosshead speed of 0.5 mm/min. Results showed that the minimum mean value of microTBS was 14.9 MPa in the group without attrition and acid-etching but with loading, while the maximum mean value of microTBS was 40.0 MPa in the group without attrition and loading but with acid etching. Therefore, the value of microTBS to dentin without attrition was significantly decreased by cyclic loading but that to dentin with attrition was not affected.

journal_name

Dent Mater J

journal_title

Dental materials journal

authors

Shinkai K,Ebihara T,Shirono M,Seki H,Wakaki S,Suzuki M,Suzuki S,Katoh Y

doi

10.4012/dmj.28.197

subject

Has Abstract

pub_date

2009-03-01 00:00:00

pages

197-203

issue

2

eissn

0287-4547

issn

1881-1361

journal_volume

28

pub_type

杂志文章,随机对照试验
  • Soda-lime glass as a binder in reusable experimental investment for dental castings.

    abstract::In this study, different glasses were investigated to improve reusable investments. Borosilicate glass (BSG) powder and soda-lime glass (SLG) powder were prepared by milling broken beakers and microscope slides, respectively, and used in experimental investments (I-BSG, I-SLG) by blending glass powder (10 wt%) with cr...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2011-040

    authors: Yagi S,Zhang Z,Aida Y,Hotta Y,Tamaki Y,Miyazaki T

    更新日期:2011-01-01 00:00:00

  • Radiopacity of experimental composite resins containing radiopaque materials.

    abstract::This study aimed to investigate the relationship between the radiopacity of an experimental light-cured composite resin and the amount and type of its radiopaque material: Ti, SrCO3, ZrO2, BaSO4, or Bi2O3. Radiopacity of each material was evaluated in terms of aluminum equivalent thickness using an aluminum step wedge...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.24.315

    authors: Aoyagi Y,Takahashi H,Iwasaki N,Honda E,Kurabayashi T

    更新日期:2005-09-01 00:00:00

  • Kinetic polymerization behavior of fluorinated monomers for dental use.

    abstract::The kinetic polymerization behavior of 2,2,2-trifluoroethyl methacrylate (TFEMA), 1,1,1,3,3,3-hexafluoroisopropyl methacrylate (HFIPMA), 2,2,2-trifluoroethyl acrylate (TFEA) and 1,1,1,3,3,3-hexafluoroisopropyl acrylate (HFIPA) was determined by isothermal differential scanning calorimetry (DSC) and high-performance li...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2010-054

    authors: Kadoma Y

    更新日期:2010-10-01 00:00:00

  • Influence of the number of cycles on shear fatigue strength of resin composite bonded to enamel and dentin using dental adhesives in self-etching mode.

    abstract::The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to e...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2017-012

    authors: Tsujimoto A,Barkmeier WW,Erickson RL,Takamizawa T,Latta MA,Miyazaki M

    更新日期:2018-01-30 00:00:00

  • The effects of glass ionomer and flowable composite liners on the fracture resistance of open-sandwich class II restorations.

    abstract::This in vitro study aimed to investigate the effects of glass-ionomer and flowable composite liners on the fracture resistance of Class II amalgam and composite restorations. Group 1 cavities were restored with amalgam and Group 4 cavities with nanofill composite after the application of a dentin-bonding agent. For th...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2013-053

    authors: Güray Efes B,Yaman BC,Gümüştaş B,Tıryakı M

    更新日期:2013-01-01 00:00:00

  • Analysis of fracture surface of titanium-porcelain bonding by electron spectroscopy for chemical analysis.

    abstract::Three commercially available porcelains bonded to titanium were evaluated to determine the weakest zone of the titanium-porcelain bonding structures. Tensile bond tests were performed for these specimens (NO, DU, and VI) and for Ni-Cr alloy-porcelain bonding samples that served as controls. The maximum bond strengths ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2013-263

    authors: Kannari Y,Endo K,Ida Y,Ochi M,Ohno H

    更新日期:2014-01-01 00:00:00

  • A simplified numerical simulation method of bending properties for glass fiber cloth reinforced denture base resin.

    abstract::The purpose of this study was to propose a new numerical modeling of the glass fiber cloth reinforced denture base resin (GFRP). The proposed model is constructed with an isotropic shell, beam and orthotropic shell elements representing the outmost resin, interlaminar resin and glass fiber cloth, respectively. The pro...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.21.105

    authors: Tanimoto Y,Nishiwaki T,Nishiyama N,Nemoto K,Maekawa Z

    更新日期:2002-06-01 00:00:00

  • Effects of different luting cements and light curing units on the sealing ability and bond strength of fiber posts.

    abstract::This study evaluated the sealing ability and push-out bond strength of two luting cements cured with two different types of light curing units (LCU): light-emitting diode (LED) versus quartz tungsten halogen (QTH). Forty teeth were divided into four groups(n=10/group). Quartz fiber posts (D. T. Light-Post) were luted ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2011-209

    authors: Beriat NC,Ertan AA,Yilmaz Z,Gulay G,Sahin C

    更新日期:2012-01-01 00:00:00

  • The effect of five kinds of surface treatment agents on the bond strength to various ceramics with thermocycle aging.

    abstract::This study evaluated the effects of ceramic surface treatment agents on shear bond strengths to ceramic materials with and without thermocycling. Ceramic plates were prepared from feldspathic ceramic; AAA, lithium disilicate ceramic material; IPS e.max Press, zirconia ceramic; Lava. Ceramic surfaces were pretreated wi...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2016-383

    authors: Noda Y,Nakajima M,Takahashi M,Mamanee T,Hosaka K,Takagaki T,Ikeda M,Foxton RM,Tagami J

    更新日期:2017-11-29 00:00:00

  • A novel glass ionomer cement containing MgCO(3 )apatite induced the increased proliferation and differentiation of human pulp cells in vitro.

    abstract::This study aimed to investigate the in vitro biological response of human dental pulp cells to glass ionomer cement (GIC, Fuji IX GP(®)) containing 2.5% magnesium carbonate apatite (MgCO(3)Ap). MgCO(3)Ap was synthesized by wet method and characterized using FT-IR, XPS, and SEM. Fuji IX GP(®) served as a control. Test ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2012-096

    authors: Laiteerapong A,Lochaiwatana Y,Hirata I,Okazaki M,Mori K,Murakami S,Poolthong S

    更新日期:2012-01-01 00:00:00

  • Discoloration and dissolution of titanium and titanium alloys with immersion in peroxide- or fluoride-containing solutions.

    abstract::This study compared differences in discoloration and dissolution in several titanium alloys with immersion in peroxide- or fluoride-containing solution. Commercially pure titanium (CP-Ti) and six titanium-based alloys were used: Ti-0.15Pd, Ti-6Al-4V, Ti-7Nb-6Al, Ti-55Ni, Ti-10Cu, and Ti-20Cr. Two test solutions were p...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.27.117

    authors: Noguchi T,Takemoto S,Hattori M,Yoshinari M,Kawada E,Oda Y

    更新日期:2008-01-01 00:00:00

  • Bioactive-glass in periodontal surgery and implant dentistry.

    abstract::Bioactive-glass (B-G) is a material known for its favorable biological response when in contact with surrounding fibro-osseous tissues, due not only to an osteoconductive property, but also to an osteostimulatory capacity, and superior biocompatibility for use in human body. The objectives of this paper are to review ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2014-233

    authors: Profeta AC,Prucher GM

    更新日期:2015-01-01 00:00:00

  • Novel, multi-purpose, PMMA-type adhesive resin with newly synthesized microcapsule of radical polymerization initiators.

    abstract::The behavior of microencapsulated polymerization initiators in dental adhesives is unknown. This study investigated the effects of new microencapsulated initiators in novel, multi-purpose, PMMA-type adhesive resin on the bonding performance and polymerization reactivity. Microencapsulated BPO and 1,3,5-trimethylbarbit...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.27.35

    authors: Fuchigami K,Ikemura K,Ichizawa K

    更新日期:2008-01-01 00:00:00

  • Effect of different remaining dentin thickness and long term water storage on dentin bond strength.

    abstract::The purpose of this study was to investigate the effect of remaining dentin thickness (RDT) and long term water storage on dentin bond strength in-vitro. Twenty-seven third molars were randomly divided into 3 groups: Clearfil Bond SE ONE (SE1, Kuraray Noritake Dental, Okayama, Japan), G-Bond plus (GB, GC, Tokyo, Japan...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2017-140

    authors: Ting S,Chowdhury AFMA,Sun J,Kakuda S,Sidhu SK,Yoshida Y,Selimovic D,Sano H

    更新日期:2018-07-29 00:00:00

  • Evaluation of an articulated measuring apparatus for use in the oral cavity.

    abstract::The aim of this study was to evaluate the trial Teaching Robot for the development of a contact-type measuring apparatus for using directly in the oral cavity. A standard model was used to mimic the dentition by placing an arrangement of three bearing balls. The diameters of the balls were measured. A practical dentit...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.22.168

    authors: Maikuma Y,Usui K,Araki K,Mataki S,Kurosaki N,Furuya N

    更新日期:2003-06-01 00:00:00

  • Effect of three metal priming agents on the bond strength of adhesive resin cement to Ag-Zn-Sn-In alloy and component metals.

    abstract::The aim of this study was to investigate the effect of three metal priming agents on the bond strength of adhesive resin cement to Silver-Zinc-Tin-Indium (Ag-Zn-Sn-In) alloy and pure Ag, Zn, Sn, and In. The specimens were air-abraded with alumina and then primed with one of three metal priming agents: V-Primer, Esteni...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2017-139

    authors: Imamura N,Kawaguchi T,Shimizu H,Takahashi Y

    更新日期:2018-03-30 00:00:00

  • Influence of different elastic moduli of dowel and core on stress distribution in root.

    abstract::This study was carried out to investigate the influences of elastic moduli of the dowel-core combination on the stress distribution in the root by the use of 2-dimensional finite element analysis. The peak stress at the dowel-cement interface was influenced strongly by a change of elastic modulus of the post (from 20,...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.19.50

    authors: Ukon S,Moroi H,Okimoto K,Fujita M,Ishikawa M,Terada Y,Satoh H

    更新日期:2000-03-01 00:00:00

  • Evaluation of a hydrogel membrane on bone regeneration in furcation periodontal defects in dogs.

    abstract::The aim of the study was to evaluate bone regeneration using a canine model with surgically created periodontal defects filled for 12 weeks using a stratified biomaterial consisting in a biphasic calcium phosphate (BCP) covered with a crosslinking hydrogel acting as polymer membrane of silated hydroxypropyl methylcell...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2017-238

    authors: Struillou X,Fruchet A,Rakic M,Badran Z,Rethore G,Sourice S,Fellah BH,LE Guehennec L,Gauthier O,Weiss P,Soueidan A

    更新日期:2018-09-30 00:00:00

  • Shear bond strength of veneering porcelain to porous zirconia.

    abstract::In this study, two types of porous zirconia and dense zirconia were used. The flexural strength of non-layered zirconia specimens and those of the layered zirconia specimens with veneering porcelain were examined. Furthermore, the shear bond strength of veneering porcelain to zirconia was examined. The flexural streng...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2013-191

    authors: Nakamura T,Sugano T,Usami H,Wakabayashi K,Ohnishi H,Sekino T,Yatani H

    更新日期:2014-01-01 00:00:00

  • Fracture force for veneered materials on restorations measured by torsion testing.

    abstract::The torsional fracture strength at the interface between a base plate and veneering material was evaluated for three kinds of veneered restoration: porcelain fused to zirconia (PFZ), porcelain fused to metal (PFM), and composite resin veneered metal (CRVM). The metal and zirconia base plate (30×4×0.4 mm) were prepared...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2016-432

    authors: Watanabe F,Seto M,Ueda K,Ozawa M

    更新日期:2018-07-29 00:00:00

  • Effects of fluoride and dissolved oxygen concentrations on the corrosion behavior of pure titanium and titanium alloys.

    abstract::The effects of dissolved-oxygen concentration and fluoride concentration on the corrosion behaviors of commercial pure titanium, Ti-6Al-4V and Ti-6Al-7Nb alloys and experimentally produced Ti-0.2Pd and Ti-0.5Pt alloys were examined using the corrosion potential measurements. The amount of dissolved Ti was analyzed by ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.21.83

    authors: Nakagawa M,Matsuya S,Udoh K

    更新日期:2002-06-01 00:00:00

  • Self-cleaning ability of a photocatalyst-containing denture base material.

    abstract::This study examined the ability of a photocatalyst mixed in a denture base resin to decompose organic substances which adhered to the denture base resin surface. The photocatalyst was mixed with denture base resin at concentrations of 0, 5, 10, and 15% (w/w). Decomposition test, bending test, and surface roughness mea...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.27.179

    authors: Cheng Y,Sakai T,Moroi R,Nakagawa M,Sakai H,Ogata T,Terada Y

    更新日期:2008-03-01 00:00:00

  • Analysis of abutment tooth movement utilizing mandibular kinesiography (MKG). Part 2. Effects of clasp design in unilateral free-end denture.

    abstract::The three-dimensional dynamic movement of the abutment tooth was successfully analyzed on a simulation model utilizing the mandibular kinesiography. When the unilateral free-end denture retained by the RPA, RPI or Aker's clasp was subjected to various directions of loads, the abutment tooth was inclined mainly by the ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.8.56

    authors: Morikawa M,Masumi S,Kido H,Toyoda S,Kozono Y

    更新日期:1989-06-01 00:00:00

  • SEM observation of collagen fibrils secreted from the body surface of osteoblasts on a CO3apatite-collagen sponge.

    abstract::The secretion of collagen by osteoblasts was observed by scanning electron microscopy (SEM). Osteoblast-like cells were cultured on a CO3apatite-collagen sponge reinforced with a porous HAp frame. After three days' incubation, a number of newly created matrix fibrils, forming a network structure, were observed at the ...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.24.460

    authors: Hirata I,Nomura Y,Tabata H,Miake Y,Yanagisawa T,Okazaki M

    更新日期:2005-09-01 00:00:00

  • Effects of degree of dissociation of acid used on hydrolytic durability of ceramic primer.

    abstract::In this study, effects of the degree of dissociation of acids on the hydrolysis rate of methoxy group in γ-methacryloxypropyltrimethoxysilane (γ-MPS) and the adsorption characteristics of γ-MPS on ceramic surfaces were studied using acetic, phosphoric, and hydrochloric acids. Hydrolytic stability of γ-MPS adsorption l...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2013-319

    authors: Aoki N,Kimoto S,Tanimura H,Nishiyama N,Aida M

    更新日期:2014-01-01 00:00:00

  • In vivo analyses of the effects of polyamidoamine dendrimer on dentin biomineralization and dentinal tubules occlusion.

    abstract::This study evaluated the biomineralization and dentinal tubules occlusion abilities of the carboxyl-terminated polyamidoamine dendrimer (PAMAM-COOH) on human demineralized dentin in vivo at different time points. Demineralization dentin model with and without treated with PAMAM-COOH were sutured to the interior side o...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2015-209

    authors: Xie F,Wei X,Li Q,Zhou T

    更新日期:2016-01-01 00:00:00

  • Abutment screw loosening of endosseous dental implant body/abutment joint by cyclic torsional loading test at the initial stage.

    abstract::Cyclic torsional loading tests were carried out in the laboratory using various implant systems, in order to clarify differences between the systems in loosening of abutment screws. Six samples from six commercially available abutment systems were used, giving a total of 36 samples. Four of the systems used internal c...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2015-023

    authors: Katsuta Y,Watanabe F

    更新日期:2015-01-01 00:00:00

  • Antimicrobial effects of several calcium silicate-based root-end filling materials.

    abstract::The purpose of this study was to evaluate, in vitro, the antimicrobial effect of iRoot BP, iRoot BP Plus, and mineral trioxide aggregate (MTA) against Entercoccus faecalis and Candida albicans by using direct contact test. The materials were tested immediately after application to the microtiter wells and after settin...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2013-250

    authors: Damlar I,Ozcan E,Yula E,Yalcin M,Celik S

    更新日期:2014-01-01 00:00:00

  • Technique-sensitivity of contemporary adhesives.

    abstract::Besides micro-mechanical interlocking through hybrid-layer formation, self-etch adhesives may benefit from additional chemical interaction between the functional monomer and residual hydroxyapatite. One-step adhesives are commonly associated with lower bonding effectiveness, which must be attributed in part to the dis...

    journal_title:Dental materials journal

    pub_type: 杂志文章,评审

    doi:10.4012/dmj.24.1

    authors: Van Meerbeek B,Van Landuyt K,De Munck J,Hashimoto M,Peumans M,Lambrechts P,Yoshida Y,Inoue S,Suzuki K

    更新日期:2005-03-01 00:00:00

  • Nanostructure evaluation of healthy and fluorotic dentin by atomic force microscopy before and after phosphoric acid etching.

    abstract::The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...

    journal_title:Dental materials journal

    pub_type: 杂志文章

    doi:10.4012/dmj.2011-023

    authors: Zavala-Alonso V,Aguilera-Flores R,Patiño-Marin N,Martinez-Castañon GA,Anusavice KJ,Loyola-Rodriguez JP

    更新日期:2011-01-01 00:00:00