Abstract:
OBJECTIVE:To evaluate the effect of mechanical loading on the microtensile bond strength (MTBS) of five adhesive systems to dentin. METHODS:Flat dentin surfaces from human molars were divided into five groups and bonded with total-etch self-priming adhesives (Single Bond, Prime&Bond NT and Prime&Bond XP), two-step self-etching primer (Clearfil SE Bond) and an all-in-one adhesive (Etch&Prime 3.0), according to the manufacturers' instructions. Composite build-ups were constructed incrementally with Tetric Ceram. After 24 hours of water storage, half the specimens were load cycled (5000 cycles, 90 N). The teeth were then sectioned into beams of 1.0 mm2 cross-sectional area. Each beam was tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by two-way ANOVA and Student Newman Keuls multiple comparisons tests (p<0.05). RESULTS:Clearfil SE Bond and Single Bond attained higher MTBS than the other three adhesives. Prime&Bond NT and Prime&Bond XP performed equally, and Etch&Prime 3.0 resulted in the lowest MTBS. After mechanical loading, MTBS decreased in all groups except Prime&Bond XP. Clearfil SE Bond, Single Bond and Prime&Bond XP obtained higher MTBS than Prime&Bond NT. Specimens bonded with Etch&Prime 3.0 resulted in premature failures and MTBS could not be measured. CLINICAL RELEVANCE:When using Etch&Prime 3.0, bond structures did not withstand mechanical loading, which may have an influence on the long-term success of restorations. If dentin is acid-etched, alcohol-based adhesive systems showed higher bond strength after mechanical loading.
journal_name
Oper Dentjournal_title
Operative dentistryauthors
Toledano M,Osorio R,Albaladejo A,Aguilera FS,Tay FR,Ferrari Mdoi
10.2341/04-161keywords:
subject
Has Abstractpub_date
2006-01-01 00:00:00pages
25-32issue
1eissn
0361-7734issn
1559-2863journal_volume
31pub_type
杂志文章abstract:STATEMENT OF THE PROBLEM:Precise shade matching can be one of the most difficult tasks for the dentist and some variables may influence the process of shade comparison. PURPOSE OF THE STUDY:This study tested the differences in shade perception between genders, the influence of the observer's clinical experience, and t...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/10-057-C
更新日期:2012-05-01 00:00:00
abstract::The DIAGNOdent, a device used in caries detection, uses a laser to excite fluorescence from pigments in carious tooth structure. In clinical use assessing occlusal surfaces, distance and tooth structure may separate the instrument's tip from the fluorescent source.The aim of this in vitro study was to examine the effe...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/10-179-L
更新日期:2012-03-01 00:00:00
abstract:PURPOSE:This study evaluated the amount of residual yellow in cured resin composites when polymerizing with either a quartz-tungsten-halogen (QTH) or blue light-emitting diode (LED). MATERIAL AND METHODS:Twelve shades (bleaching to conventional shades) of microfill, hybrid and microhybrid resin composite specimens (n ...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/06-129
更新日期:2007-09-01 00:00:00
abstract:OBJECTIVES:This study was performed to 1) quantify dentists' treatment thresholds for occlusal primary caries; 2) determine if the patient's age affects dentists' decisions to surgically treat these carious lesions; and 3) test the hypothesis that patients', dentists', and practices' characteristics are significantly a...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/13-141-C
更新日期:2014-09-01 00:00:00
abstract:OBJECTIVES:The aim of this investigation was to test the tensile bond strength (TBS) between different computer-aided-design/manufacturing (CAD/CAM) ceramics after conditioning using different universal adhesive systems and resin composite cement. METHODS AND MATERIALS:Substrates of four CAD/CAM ceramics-1) VITABLOCS ...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/18-017-L
更新日期:2019-07-01 00:00:00
abstract::One hundred non-carious, non-undercut cervical lesions were restored with Silux Plus or Estio LC and bonded with Fuji Bond LC. The restorations were evaluated yearly for retention and marginal discoloration. After five years, the overall retention rate was 96%. Of the 41 restorations examined at five years, five had c...
journal_title:Operative dentistry
pub_type: 临床试验,杂志文章
doi:
更新日期:2002-09-01 00:00:00
abstract::The effect of microabrasion on human enamel has been well documented; however, no information is available on its effect on dentin or restorative materials. The purpose of this study was to evaluate the effect of the microabrasion technique on the surface roughness of restorative materials and enamel and dentin surfac...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:1996-03-01 00:00:00
abstract:OBJECTIVES:To evaluate and compare the fracture toughness of dental CAD/CAM materials of different material classes intended for in-office milling (glass ceramics, hybrid, resin composites) and the influence of aging on this property. METHODS AND MATERIALS:The fracture toughness (critical intensity factor, KIc) values...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/18-161-L
更新日期:2019-07-01 00:00:00
abstract::The aim of this study was to evaluate the effect of grinding with diamond burs and low-temperature aging on the material surface characteristics and bacteria adhesion on a yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) surface. Y-TZP specimens were made from presintered blocks, sintered as recommended ...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/16-108-L
更新日期:2017-11-01 00:00:00
abstract:OBJECTIVE:This in vitro study evaluated the effect of polishing with different polishing systems on the surface roughness and gloss of commercial composites. METHODS:One hundred disk-shaped specimens (10 mm in diameter × 2 mm thick) were made with Filtek P-90, Filtek Z350 XT, Opallis, and Grandio. The specimens were m...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/14-014L
更新日期:2015-07-01 00:00:00
abstract::The role of silanes in the bonding of resin luting agents to glass-fiber posts (GFPs) is a controversial topic, and the question still remains whether post silanization is able to improve the retention of GFPs luted into root canals. Thus, this study was designed to determine whether evidence exists to justify silaniz...
journal_title:Operative dentistry
pub_type: 杂志文章,meta分析
doi:10.2341/14-330-O
更新日期:2015-11-01 00:00:00
abstract::This study investigated the effect of a crown-lengthening ferrule on the fracture resistance of endodontically-treated teeth restored with two dowel-core systems. Thirty-two extracted mandibular first premolars were sectioned perpendicular to the long axis at a point 1.0 mm occlusal to the buccal cementoenamel junctio...
journal_title:Operative dentistry
pub_type: 杂志文章,随机对照试验
doi:10.2341/06-169
更新日期:2007-11-01 00:00:00
abstract::While a one-year report had been previously published, this study was undertaken to evaluate the clinical performance and appearance of a resin-modified glass ionomer and a resin composite over two years. Thirty-seven pairs of restorations of FujI II LC and Z 250/Single Bond were placed in caries-free cervical erosion...
journal_title:Operative dentistry
pub_type: 临床试验,杂志文章,随机对照试验
doi:
更新日期:2003-09-01 00:00:00
abstract::The replacement of a restoration is one of the most common procedures in dentistry. However, the criteria for such intervention, excluding catastrophic failure and persistent discomfort and pain, continue to be the subject of considerable debate. The decision-making process remains subjective on the part of the treati...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/15-058-O
更新日期:2016-09-01 00:00:00
abstract::A core foundation system is frequently used in endodontically treated teeth that suffer excessive loss of the coronal portion of their structure. The volumetric shrinkage of core foundation resins may create marginal gaps that influence the bonding ability and longevity of a restored tooth. Little is known about how a...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:2005-09-01 00:00:00
abstract::This study compared the amount of artificial plaque synthesized in vitro by Streptococcus sobrinus on various dental materials using radioisotopes. In particular, plaque-retaining capacities of new types of ceramics were the focus of this study. Specimens were fabricated from the following materials (one amalgam alloy...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:2001-07-01 00:00:00
abstract::No data are available on the direct acute vascular effect of dental bonding materials on the dental pulp. This study investigated the effects of the components of a composite resin-bonding system on pulpal vascular diameter. Three groups of 10 male Sprague-Dawley rats (weighing 330 +/- 51 g) were used for this investi...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:2000-09-01 00:00:00
abstract:UNLABELLED:Examining three bleaching systems, this in vivo clinical trial evaluated the relationship among tooth sensitivity, light activation, and agent concentration, and it correlated dental sensitivity with tooth thickness. MATERIALS AND METHODS:Eighty-seven volunteer patients were included. Inclusion criteria wer...
journal_title:Operative dentistry
pub_type: 杂志文章,随机对照试验
doi:10.2341/12-335-C
更新日期:2013-09-01 00:00:00
abstract::The clinical performance of light curing resin composites is greatly influenced by the quality of the light-curing unit (LCU). Halogen LCUs are commonly used for curing composite materials. However, they have some drawbacks. The development of new, blue, super bright light emitting diodes (LED LCU) of 470-nm wavelengt...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:2005-01-01 00:00:00
abstract::Post-operative sensitivity (POS) may be observed in recently placed posterior composites. Evidence-based guidelines for the management of posterior composites with POS have yet to be determined. This study examined a retrospective analysis of the findings of a unique multi-center clinical trial to investigate the five...
journal_title:Operative dentistry
pub_type: 临床试验,杂志文章,多中心研究
doi:
更新日期:2003-11-01 00:00:00
abstract:OBJECTIVE:To evaluate, through the application of different dentin bonding systems, the influence of wetness on shear bond strength in enamel. METHODS:This study evaluated three etch-and-rinse adhesive systems (Scotchbond MP [used with and without primer]; Singlebond; and Prime&Bond 2.1) and two self-etching adhesive ...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/10-163-L
更新日期:2011-05-01 00:00:00
abstract::Standardized class 4 cavities were prepared in bovine incisors and restored with a microfilled composite resin. The composite restorations were retained either by acid etching technique (AET) alone or by acid etching technique in combination with a self-threading retentive pin. Pins covered with a bonding/opaquer coat...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:1994-05-01 00:00:00
abstract:OBJECTIVE:The purpose of this study was to evaluate the strengthening effect of resin composite, cured by a modified layering protocol, for teeth with simulated coronal fracture and weakened immature roots. METHODS:Fifty maxillary teeth were decoronated and their apices sectioned to standardize the length to 12 mm. Pr...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/12-525L
更新日期:2014-05-01 00:00:00
abstract:PURPOSE:To investigate clinical performance of a low-shrinkage silorane-based composite resin when used for repairing conventional dimethacrylate-based composite restorations. BACKGROUND:Despite the continued development of resin-based materials, polymerization shrinkage and shrinkage stress still require improvement....
journal_title:Operative dentistry
pub_type: 杂志文章,随机对照试验
doi:10.2341/11-121-C
更新日期:2012-09-01 00:00:00
abstract::The molar proximal half-crown cast gold restoration may be an ideal choice for the conservative treatment of teeth with only one compromised proximal aspect. ...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/10-T1
更新日期:2010-03-01 00:00:00
abstract::Retained primary teeth in the smile zone can cause patient dissatisfaction, especially if associated with malposition of teeth. Orthodontic and prosthetic treatment options to treat the situation may not be accepted by some patients. Therefore, these patients tend to maintain their primary teeth and seek different est...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/15-363-S
更新日期:2017-03-01 00:00:00
abstract::Amalgapins are susceptible to early fracture during matrix removal and carving. The purpose of this study was to examine the early fracture resistance of amalgapin-retained restorations using a spherical amalgam alloy, an admixed amalgam alloy, a combination of admixed alloy over the spherical alloy, and a recently in...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:1998-03-01 00:00:00
abstract:PURPOSE:The present study aimed to investigate a novel adhesive system containing 0.2% chlorhexidine digluconate (CHX) for its ability to improve the stability of the adhesive interface compared with the use of 2% CHX as a therapeutic primer. Furthermore, the study aimed to confirm the inhibitory properties of these CH...
journal_title:Operative dentistry
pub_type: 杂志文章,随机对照试验
doi:10.2341/12-239-L
更新日期:2013-11-01 00:00:00
abstract:OBJECTIVES:This study investigated the influence of resin composite preheating temperature, light curing regimen (mode and duration) on post-gel shrinkage strain (PGSS) and degree of conversion (DC) of a restorative resin composite. METHODS:A hybrid resin composite preheated to three different temperatures (37 degrees...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:10.2341/09-072-L
更新日期:2010-03-01 00:00:00
abstract::This article outlines an atraumatic isolation approach and a conservative instrumentation sequence, followed by use of a highly viscous, rapid-setting, capsulated glass ionomer cement to manage a difficult deep proximal-cervical Class V lesion. ...
journal_title:Operative dentistry
pub_type: 杂志文章
doi:
更新日期:2004-05-01 00:00:00