Effect of adding spherical silica filler on physico-mechanical properties of resin modified glass-ionomer cement.

abstract：:To determine the effect of titanium (Ti) surface modification by ultraviolet irradiation (UVI) on the bond strength between Ti and porcelain. Grade 2 Ti plates were allotted to five groups: sandblasted (SA), 15 min UVI (UV), SA+5 min UVI (SA+UV5), SA+10 min UVI (SA+UV10), and SA+15 min UVI (SA+UV15). After surface tre...

journal_title：Dental materials journal

authors： Kumasaka T,Ohno A,Hori N,Hoshi N,Maruo K,Kuwabara A,Seimiya K,Toyoda M,Kimoto K

更新日期：2018-06-08 00:00:00

abstract：:The objective of this study was to clarify the effect of surface topography on osteoblast-like cell behavior on yttria stabilized tetragonal zirconia polycrystals (TZP). Mirror-polished; blasted with 50- or 150-µm alumina (SB50 and SB150); and SB150 acid-etched with hydrofluoric acid (SB150E) were prepared on TZP. Ini...

journal_title：Dental materials journal

authors： Ito H,Sasaki H,Saito K,Honma S,Yajima Y,Yoshinari M

更新日期：2013-01-01 00:00:00

abstract：:The aim of this investigation was to evaluate the metal-ceramic bonding of Au-1.6 wt% Ti alloy. Therefore, the coefficient of thermal expansion, modulus of elasticity, ceramic bonding strength, and hardness of Au-1.6 wt% Ti alloy were measured. The metal-ceramic interface was observed by EPMA to investigate its bondin...

journal_title：Dental materials journal

authors： Ito M,Kikuchi M,Okuno O,Kimura K

更新日期：2005-06-01 00:00:00

abstract：:The aim was to evaluate the effect of different zirconia discontinuous fiber fractions on radiopacity and other selected properties of glass discontinuous fiber-reinforced flowable composite (Exp-SFRC). Exp-SFRC was prepared by mixing 30 wt% of resin-matrix and 45 wt% of particulate-fillers to 25 wt% of various weight...

journal_title：Dental materials journal

authors： Garoushi S,Vallittu P,Lassila L

更新日期：2019-03-31 00:00:00

abstract：:The purpose of this study was to investigate the effects of the location and orientation of dentinal tubules in the tooth on tensile strengths of the dentin. Dumbbell-shaped specimens of 12 groups from various locations and dentinal tubule orientations were prepared. The tensile test was performed in distilled water a...

journal_title：Dental materials journal

authors： Inoue T,Takahashi H,Nishimura F

更新日期：2002-03-01 00:00:00

abstract：:The purpose of this study was to examine the effect of an electro-ionizing toothbrush with stannous fluoride in the treatment of dentin hypersensitivity following periodontal surgery. Thirty-two volunteers with dentin hypersensitivity were divided in two equal groups each using different methods: (Group I) stannous fl...

journal_title：Dental materials journal

authors： Orbak R,Canakçi V,Tezel A

更新日期：2001-06-01 00:00:00

abstract：:This study aimed to introduce a procedure for determining the bilinear elastic moduli (E1 and E2) of the periodontal ligament for a mathematical tooth model to analyse stress in the mandible. The bone and tooth morphology were scanned from a dry skull and an extracted intact tooth, respectively, and reconstructed in a...

journal_title：Dental materials journal

authors： Borák L,Florian Z,Bartáková S,Prachár P,Murakami N,Ona M,Igarashi Y,Wakabayashi N

更新日期：2011-01-01 00:00:00

abstract：:The purposes of this study were to examine the shock absorption capability of addition-cured silicone denture relining materials and the bonding strength of addition-cured silicone denture relining materials and a commercial mouthguard material to determine its applicability to mouthguard adjustment. Two addition-cure...

journal_title：Dental materials journal

authors： Fukasawa S,Churei H,Chowdhury RU,Shirako T,Shahrin S,Shrestha A,Wada T,Uo M,Takahashi H,Ueno T

更新日期：2016-01-01 00:00:00

abstract：:This study was to evaluate the load bearing capacity of monolithic dental zirconia crowns, and the effect of surface finishing on fracture strength. (1) The zirconia plates were divided into 5 groups and polished by various types of polishing bur, every specimen was analyzed by surface roughness testing, and X-ray dif...

journal_title：Dental materials journal

authors： Yin R,Lee MH,Bae TS,Song KY

更新日期：2019-03-31 00:00:00

abstract：:The behavior of microencapsulated polymerization initiators in dental adhesives is unknown. This study investigated the effects of new microencapsulated initiators in novel, multi-purpose, PMMA-type adhesive resin on the bonding performance and polymerization reactivity. Microencapsulated BPO and 1,3,5-trimethylbarbit...

journal_title：Dental materials journal

authors： Fuchigami K,Ikemura K,Ichizawa K

更新日期：2008-01-01 00:00:00

abstract：:This study was evaluating how three desensitizing toothpastes used at home influence the effect associated with desensitizing agents after application in the clinic. Fifty dentine disks measure it permeability and 32 dentine disks with similar permeability levels were selected. Following Dental desensitizer treatment,...

journal_title：Dental materials journal

authors： Hu ML,Zheng G,Jiang RD,Han JM,Zhang YD,Lin H

更新日期：2020-09-29 00:00:00

abstract：:The aim of the study was to evaluate bone regeneration using a canine model with surgically created periodontal defects filled for 12 weeks using a stratified biomaterial consisting in a biphasic calcium phosphate (BCP) covered with a crosslinking hydrogel acting as polymer membrane of silated hydroxypropyl methylcell...

journal_title：Dental materials journal

authors： Struillou X,Fruchet A,Rakic M,Badran Z,Rethore G,Sourice S,Fellah BH,LE Guehennec L,Gauthier O,Weiss P,Soueidan A

更新日期：2018-09-30 00:00:00

abstract：:The effectiveness of a barbituric acid/copper (II) chloride initiator system in dentin was examined in terms of the effects of barbituric acid structures and dentin conditioners on bond strength. Curing times and tensile bond strengths to bovine dentin were measured for PMMA/MMA resins in conjunction with initiators c...

journal_title：Dental materials journal

authors： Suzuki A,Imai Y

更新日期：1995-12-01 00:00:00

abstract：:The aim of this study was to determine the effect of autoclave polymerization on the transverse strength of denture base polymers. To this end, 30 rectangular test specimens were fabricated of two heat-polymerized denture base polymers. The test groups were: (I) control, i.e., conventional water bath to polymerize res...

journal_title：Dental materials journal

authors： Durkan R,Ozel MB,Bağiş B,Usanmaz A

更新日期：2008-07-01 00:00:00

abstract：:The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a newly developed resin cement, ECD-89 (ECD, Tokuyama Dental, Tokyo, Japan) to dentin and to observe the interfacial micromorphology by comparing with two commercial resin cements, Multilink Automix (MA, Ivoclar Vivadent AG, Schaan, Lie...

journal_title：Dental materials journal

authors： Kawano S,Fu J,Saikaew P,Chowdhury AA,Fukuzawa N,Kadowaki Y,Kakuda S,Hoshika S,Nakaoki Y,Ikeda T,Tanaka T,Sano H

更新日期：2015-01-01 00:00:00

abstract：:Comparative studies on two-body sliding wear resistance were performed between a hybrid composite resin and conventional light-curing composite veneering materials. This study investigated the wear resistance of hybrid composite resins compared with three composite resin veneering materials for 12%Au-Ag-Pd alloy, the ...

journal_title：Dental materials journal

authors： Suese K,Kawazoe T

更新日期：2002-09-01 00:00:00

abstract：:Sixteen alloys and five pure metals were used and the open circuit potentials (OCP) and the coupled potentials with titanium were measured in five kinds of solutions. All alloys and metals showed the maximum OCP in 1.3% lactic acid solution, and the minimum in 0.01% sodium sulfide solution. The coupled potential depen...

journal_title：Dental materials journal

authors： Nakayama M,Ando N

更新日期：2001-03-01 00:00:00

abstract：:The effect of warm air-blowing on the sealing ability of two one-bottle and one two-bottle silane-containing universal adhesives (UAs) applied to lithium disilicate ceramics (LDS) was evaluated. Tapered cavities prefabricated in LDS blocks (IPS e.max CAD) were treated by the adhesives, air-blown either with normal air...

journal_title：Dental materials journal

authors： Kaykhine P,Tichy A,Abdou A,Hosaka K,Foxton RM,Sumi Y,Nakajima M,Tagami J

更新日期：2020-10-24 00:00:00

abstract：:This study evaluated the irrigation extrusion and smear layer (SL) removal of continuous ultrasonic irrigation (CUI). Forty root canals were shaped, embedded in warm sterile saline agar colored with 1% acid red, and distributed into four groups; three groups had the final irrigation sequence of sodium hypochlorite and...

journal_title：Dental materials journal

authors： Jamleh A,Suda H,Adorno CG

更新日期：2018-01-30 00:00:00

abstract：:The aim of this study was to evaluate the trial Teaching Robot for the development of a contact-type measuring apparatus for using directly in the oral cavity. A standard model was used to mimic the dentition by placing an arrangement of three bearing balls. The diameters of the balls were measured. A practical dentit...

journal_title：Dental materials journal

authors： Maikuma Y,Usui K,Araki K,Mataki S,Kurosaki N,Furuya N

更新日期：2003-06-01 00:00:00

abstract：:The blending effect (BE) plays an important role in esthetics of the composite resin. The objective of this study was to determine the extents to which filler size and content affect the BE. Three types of fillers (0.7, 1.0, and 1.5 µm) were mixed at weight contents of 60, 70, 75, and 80%. This study simulated clinica...

journal_title：Dental materials journal

authors： Suh YR,Ahn JS,Ju SW,Kim KM

更新日期：2017-01-31 00:00:00

abstract：:The aim was to characterize by atomic force microscopy (AFM) the nanostructure of human dentin surfaces affected by dental fluorosis (DF) before and after phosphoric acid etching. This study included 240 human dentin samples classified according to the severity of DF, which were divided into four groups using the Thyl...

journal_title：Dental materials journal

authors： Zavala-Alonso V,Aguilera-Flores R,Patiño-Marin N,Martinez-Castañon GA,Anusavice KJ,Loyola-Rodriguez JP

更新日期：2011-01-01 00:00:00

abstract：:The purpose of this study was to evaluate the effects of acid-etched titanium on the biological responses of osteoblast-like MC3T3-E1 cells. Four types of treatments (polishing, sandblasting, concentrated H2SO4 etching, and concentrated H2SO4 etching with vacuum firing) were carried out on the surfaces of commercially...

journal_title：Dental materials journal

authors： Iwaya Y,Machigashira M,Kanbara K,Miyamoto M,Noguchi K,Izumi Y,Ban S

更新日期：2008-05-01 00:00:00

abstract：:An experimental primer was developed as a single-step bonding system for resin-modified glass ionomer cements (GIC). Efficacy of this primer on adhesion of resin-modified GICs and resin composite to enamel and dentin was evaluated by shear bond test and SEM observation. Good bond strengths to enamel were obtained (> 1...

journal_title：Dental materials journal

authors： Nikaido T,Nakajima M,Higashi T,Kanemura N,Pereira PN,Tagami J

更新日期：1997-06-01 00:00:00

abstract：:Though zirconia has been used in dental implant fixtures, the biocompatibility of the zirconia surface is not optimal for the surrounding tissue, and many surface modifications have been attempted. We have developed a novel method for improving the biocompatibility of zirconia by incorporating Ca ions. Elemental analy...

journal_title：Dental materials journal

authors： Sasaki K,Hayashi T,Asakura M,Ando M,Kawai T,Ban S

更新日期：2015-01-01 00:00:00

abstract：:Thermal misfit is deemed as one reason for the chipping of veneered zirconia restorations. Aim of the present study was to assess the effect of thermal misfit on the fracture load of veneered zirconia frameworks and to evaluate the applicability of a universal veneering ceramic for both zirconia and titanium framework...

journal_title：Dental materials journal

authors： Fischer J,Stawarczyk B,Tomic M,Strub JR,Hämmerle CH

更新日期：2007-11-01 00:00:00

abstract：:This study assessed the effect of the resin-coating technique on the bond strength and internal adaptation of computer-aided design/computer-aided manufacturing (CAD/CAM)-fabricated inlays. Seventy-two mesio-occlusal-distal (MOD) cavities were prepared and distributed into 3 groups according to the resin-coating techn...

journal_title：Dental materials journal

authors： Rozan S,Takahashi R,Nikaido T,Tichy A,Tagami J

更新日期：2020-12-03 00:00:00

abstract：:The objective of this work was to analyze the antimicrobial and antibiofilm activities of bismuth lipophilic nanoparticles (BisBAL NPs) incorporated into chitosan-based membranes. Chitosan-based membranes were homogeneously embedded with BisBAL NPs, confirming the bismuth presence by scanning electron microscopy. The ...

journal_title：Dental materials journal

authors： Martínez-Martínez MA,Hernandez-Delgadillo R,Abada BS,Pineda-Aguilar N,Solís-Soto JM,Nakagoshi-Cepeda MAA,Nakagoshi-Cepeda SE,Chellam S,Sánchez-Nájera RI,Cabral-Romero C

更新日期：2019-07-31 00:00:00

abstract：:In this study, two types of porous zirconia and dense zirconia were used. The flexural strength of non-layered zirconia specimens and those of the layered zirconia specimens with veneering porcelain were examined. Furthermore, the shear bond strength of veneering porcelain to zirconia was examined. The flexural streng...

journal_title：Dental materials journal

authors： Nakamura T,Sugano T,Usami H,Wakabayashi K,Ohnishi H,Sekino T,Yatani H

更新日期：2014-01-01 00:00:00

abstract：:The aim of the present study was to examine whether interconnected porous hydroxyapatite ceramics (IP-CHA) could be used as bone substitute for implant treatment in reconstructive surgery. We firstly assessed if surround of the titanium surface placed into granular or block-type IP-CHA can observe new bone formation i...

journal_title：Dental materials journal

authors： Minami M,Takechi M,Ohta K,Ohta A,Ninomiya Y,Takamoto M,Fukui A,Tada M,Kamata N

更新日期：2013-01-01 00:00:00